18 research outputs found
Recommended from our members
Improved InGaN epitaxy yield by precise temperature measurement :yearly report 1.
This Report summarizes the first year progress (October 1, 2004 to September 30, 2005) made under a NETL funded project entitled ''Improved InGaN Epitaxy Yield by Precise Temperature Measurement''. This Project addresses the production of efficient green LEDs, which are currently the least efficient of the primary colors. The Project Goals are to advance IR and UV-violet pyrometry to include real time corrections for surface emissivity on multiwafer MOCVD reactors. Increasing wafer yield would dramatically reduce high brightness LED costs and accelerate the commercial manufacture of inexpensive white light LEDs with very high color quality. This work draws upon and extends our previous research (funded by DOE) that developed emissivity correcting pyrometers (ECP) based on the high-temperature GaN opacity near 400 nm (the ultraviolet-violet range, or UVV), and the sapphire opacity in the mid-IR (MIR) near 7.5 microns
Recommended from our members
Catalytic diodes for micropower applications : verification of high energy conversion efficiency.
Recommended from our members
Nanoporous films for epitaxial growth of single crystal semiconductor materials : final LDRD report.
This senior council Tier 1 LDRD was focused on exploring the use of porous growth masks as a method for defect reduction during heteroepitaxial crystal growth. Initially our goal was to investigate porous silica as a growth mask, however, we expanded the scope of the research to include several other porous growth masks on various size scales, including mesoporous carbon, photolithographically patterned SU-8 and carbonized SU-8 structures. Use of photolithographically defined growth templates represents a new direction, unique in the extensive literature of patterned epitaxial growth, and presents the possibility of providing a single step growth mask. Additional research included investigation of pore viability via electrochemical deposition into high aspect ratio photoresist. This project was a small footprint research effort which, nonetheless, produced significant progress towards both the stated goal as well as unanticipated research directions
Recommended from our members
Final LDRD report : design and fabrication of advanced device structures for ultra high efficiency solid state lighting.
The goal of this one year LDRD was to improve the overall efficiency of InGaN LEDs by improving the extraction of light from the semiconductor chip. InGaN LEDs are currently the most promising technology for producing high efficiency blue and green semiconductor light emitters. Improving the efficiency of InGaN LEDs will enable a more rapid adoption of semiconductor based lighting. In this LDRD, we proposed to develop photonic structures to improve light extraction from nitride-based light emitting diodes (LEDs). While many advanced device geometries were considered for this work, we focused on the use of a photonic crystal for improved light extraction. Although resonant cavity LEDs and other advanced structures certainly have the potential to improve light extraction, the photonic crystal approach showed the most promise in the early stages of this short program. The photonic crystal (PX)-LED developed here incorporates a two dimensional photonic crystal, or photonic lattice, into a nitride-based LED. The dimensions of the photonic crystal are selected such that there are very few or no optical modes in the plane of the LED ('lateral' modes). This will reduce or eliminate any radiation in the lateral direction so that the majority of the LED radiation will be in vertical modes that escape the semiconductor, which will improve the light-extraction efficiency. PX-LEDs were fabricated using a range of hole diameters and lattice constants and compared to control LEDs without a photonic crystal. The far field patterns from the PX-LEDs were dramatically modified by the presence of the photonic crystal. An increase in LED brightness of 1.75X was observed for light measured into a 40 degree emission cone with a total increase in power of 1.5X for an unencapsulated LED
Recommended from our members
Final report on LDRD project : outstanding challenges for AlGaInN MOCVD.
The AlGaInN material system is used for virtually all advanced solid state lighting and short wavelength optoelectronic devices. Although metal-organic chemical vapor deposition (MOCVD) has proven to be the workhorse deposition technique, several outstanding scientific and technical challenges remain, which hinder progress and keep RD&A costs high. The three most significant MOCVD challenges are: (1) Accurate temperature measurement; (2) Reliable and reproducible p-doping (Mg); and (3) Low dislocation density GaN material. To address challenge (1) we designed and tested (on reactor mockup) a multiwafer, dual wavelength, emissivity-correcting pyrometer (ECP) for AlGaInN MOCVD. This system simultaneously measures the reflectance (at 405 and 550 nm) and emissivity-corrected temperature for each individual wafer, with the platen signal entirely rejected. To address challenge (2) we measured the MgCp{sub 2} + NH{sub 3} adduct condensation phase diagram from 65-115 C, at typical MOCVD concentrations. Results indicate that it requires temperatures of 80-100 C in order to prevent MgCp{sub 2} + NH{sub 3} adduct condensation. Modification and testing of our research reactor will not be complete until FY2005. A new commercial Veeco reactor was installed in early FY2004, and after qualification growth experiments were conducted to improve the GaN quality using a delayed recovery technique, which addresses challenge (3). Using a delayed recovery technique, the dislocation densities determined from x-ray diffraction were reduced from 2 x 10{sup 9} cm{sup -2} to 4 x 10{sup 8} cm{sup -2}. We have also developed a model to simulate reflectance waveforms for GaN growth on sapphire
Nanofabrication of tunable nanowire lasers via electron and ion-beam based techniques.
Abstract Not Provide
Recommended from our members
Energy Frontier Research Center for Solid-State Lighting Science: Exploring New Materials Architectures and Light Emission Phenomena
The Energy Frontier Research Center (EFRC) for
Solid-State Lighting Science (SSLS) is one of 46 EFRCs initiated in
2009 to conduct basic and use-inspired research relevant to energy
technologies. The overarching theme of the SSLS EFRC is the
exploration of energy conversion in tailored photonic structures. In
this article we review highlights from the research of the SSLS EFRC.
Major research themes include: studies of the materials properties and
emission characteristics of III-nitride semiconductor nanowires;
development of new phosphors and II−VI quantum dots for use as
wavelength downconverters; fundamental understanding of competing
radiative and nonradiative processes in current-generation, planar
light-emitting diode architectures; understanding of the electrical,
optical, and structural properties of defects in InGaN materials and
heterostructures; exploring ways to enhance spontaneous emission through modification of the environment in which the
emission takes place; and investigating routes such as stimulated emission that might outcompete nonradiative processes
Semi-polar GaN materials technology for high IQE green LEDs.
The goal of this NETL funded program was to improve the IQE in green (and longer wavelength) nitride- based LEDs structures by using semi-polar GaN planar orientations for InGaN multiple quantum well (MQW) growth. These semi-polar orientations have the advantage of significantly reducing the piezoelectric fields that distort the QW band structure and decrease electron-hole overlap. In addition, semipolar surfaces potentially provide a more open surface bonding environment for indium incorporation, thus enabling higher indium concentrations in the InGaN MQW. The goal of the proposed work was to select the optimal semi-polar orientation and explore wafer miscuts around this orientation that produced the highest quantum efficiency LEDs. At the end of this program we had hoped to have MQWs active regions at 540 nm with an IQE of 50% and an EQE of 40%, which would be approximately twice the estimated current state-of-the-art
Recommended from our members
Semi-polar GaN materials technology for high IQE green LEDs.
The goal of this NETL funded program was to improve the IQE in green (and longer wavelength) nitride- based LEDs structures by using semi-polar GaN planar orientations for InGaN multiple quantum well (MQW) growth. These semi-polar orientations have the advantage of significantly reducing the piezoelectric fields that distort the QW band structure and decrease electron-hole overlap. In addition, semipolar surfaces potentially provide a more open surface bonding environment for indium incorporation, thus enabling higher indium concentrations in the InGaN MQW. The goal of the proposed work was to select the optimal semi-polar orientation and explore wafer miscuts around this orientation that produced the highest quantum efficiency LEDs. At the end of this program we had hoped to have MQWs active regions at 540 nm with an IQE of 50% and an EQE of 40%, which would be approximately twice the estimated current state-of-the-art