NGHIÊN CỨU BIỂU HIỆN TỚI HẠN TRONG CÁC BĂNG HỢP KIM Fe88Co2Zr7B2Cu1

In this work, we investigated the critical behavior of Fe88Co2Zr7B2Cu1 alloy ribbons prepared using a single-roller melt-spinning method. X-ray diffraction analysis shows that the alloy is almost amorphous. This alloy undergoes a second-order ferromagnetic-paramagnetic (FM-PM) phase transition at room temperature (Curie temperature TC = 296 K). To investigate the nature of the FM-PM phase transition near the TC for the alloy, we performed a critical-exponent study. Based on modified Arrott plots, the Kouvel-Fisher method, and Widom’s scaling relation, a set of critical parameters were determined. The critical parameters are β = 0.545 ± 0.041 and γ = 1.109 ± 0.018 obtained from the modified Arrott plots; β = 0.547 ± 0.005 and γ = 1.105 ± 0.016 from the Kouvel-Fisher method, and d = 3.035 ± 0.059 from Widom’s scaling relation. These values are close to those expected for the mean-field model, revealing long-range FM interactions.Trong bài báo này, chúng tôi đã khảo sát biểu hiện tới hạn của băng hợp kim Fe88Co2Zr7B2Cu1 đã được chế tạo bằng phương pháp nguội nhanh. Phép phân tích cấu trúc bằng nhiễu xạ tia X đã cho thấy hợp kim là gần như vô định hình. Hợp kim trải qua chuyển pha loại hai sắt từ-thuận từ (FM-PM) tại nhiệt độ phòng, nhiệt độ chuyển pha Curie TC = 296 K. Để khảo sát bản chất của chuyển pha FM-PM xung quanh TC của hợp kim, chúng tôi đã nghiên cứu các tham số tới hạn. Dựa trên các đồ thị Arrott, phương pháp Kouvel-Fisher và hệ thức Widom, một bộ các tham số tới hạn đã được xác định. Các tham số tới hạn thu được là β = 0.545 ± 0.041, γ = 1.109 ± 0.018 bằng cách sử dụng các đồ thị Arrott, và β = 0.547 ± 0.005, γ = 1.105 ± 0.016 bằng cách sử dụng phương pháp Kouvel-Fisher. Các giá trị thu được là gần với giá trị của mô hình trường trung bình, đặc trưng cho các tương tác sắt từ trật tự xa

Tuning the magnetic phase transition and the magnetocaloric properties of La0.7Ca0.3MnO3 compounds through Sm-doping

In this work, we point out that the width and the nature of the magnetic phase transition, TC value, and as well as magnetocaloric effect in La0.7-xSmxCa0.3MnO3 compounds can be easily modified through Sm-doped into La-site. With an increasing Sm concentration, a systematic decrease in the magnetization, TC, and magnetic entropy change (ΔSm) are observed. The Arrott-plot proveds that the samples with x = 0 and 0.1 undergoing a first-order phase transition. Meanwhile, sample x = 0.2 undergoes a second-order phase transition, which exhibits a high value of the relative cooling power (81.5 J/kg at ΔH = 10 kOe). An analysis of the critical behavior based on the modified Arrott plots method has been done for sample x = 0.2. The results proved a coexistence of the long- and short-range interactions in La0.5Sm0.2Ca0.3MnO3 compound

Magnetocaloric effect and critical behavior in Fe-La-Zr rapidly quenched ribbons

Fe90-xLaxZr10 (x = 1 and 2) rapidly quenched ribbons with thickness of about 15 μm were prepared by the melt-spinning method. X-ray diffraction analysis shows that the structure of the ribbons is mostly amorphous. The Curie temperature, TC, of the alloy considerably increased, from ∼262 K for x = 1 to ∼302 K for x = 2, with increasing La-concentration. The maximum magnetic entropy change, |ΔSm|max, of the alloy is about 1.1 J∙kg−1K−1 for a magnetic field change ΔH = 12 kOe. A quite large refrigerant capacity (RC ∼ 74 J∙kg−1 for ΔH = 12 kOe) near the room temperature region is obtained for the alloy. A thorough analysis on critical exponents around the ferromagnetic-paramagnetic phase transition, using the Arrott–Noakes plots and Kouvel–Fisher method, sheds light on the critical magnetic behavior and its association with the magnetocaloric effect in the Fe-La based alloys. Keywords: Magnetocaloric effect, Magnetic refrigerant, Critical parameter, Magnetic entropy change, Melt-spinning metho