Pulpal response of dogs primary teeth to an adhesive system or to a calcium hydroxide cement Resposta pulpar de dentes decíduos de cães a um sistema adesivo ou ao cimento de hidróxido de cálcio

The aim of this study was to evaluate the pulpal response of dogs primary teeth to an adhesive system or to a calcium hidroxide cement after mechanic exposure of the pulp. Three mongrel dogs were used and ten class V cavities were prepared on their teeth. A mechanic pulp exposure was produced with a sterile exploratory probe in the central portion of each cavity and bleeding was controlled with dry sterile cotton pellets. Enamel, dentin and the site of the pulp exposure of five teeth were etched with 35% phosphoric acid followed by the application of an adhesive system (Scotchbond Multi-Purpose - 3M). In the other five teeth, calcium hydroxide cement (Hydro C - Dentsply) was applied on the site of the pulp exposition before application of the adhesive system (Scotchbond Multi-Purpose - 3M). All teeth were restored with a resin composite (Z-100 - 3M). After 7, 30 or 45 days the dogs were anesthetized and perfused with saline followed by a solution of neutral buffered formalin. Maxilla and mandible were sectioned into three parts and placed in a solution for demineralization. Following bone demineralization, all teeth were cut, trimmed, embedded in paraffin and longitudinally cut. Then, the teeth were stained with hematoxilin and eosin and observed under a light microscope. The results obtained with the treatments proposed in this study showed the presence and persistence of an inflammatory response of different intensities at the three experimental periods. There was no variation in the inflammatory response regarding the different treatments performed.<br>O objetivo deste estudo foi de avaliar a resposta pulpar de dentes decíduos de cães à um sistema adesivo ou a um cimento de hidróxido de cálcio após exposição mecânica da polpa. Foram utilizados três cães sem raça definida, e nestes foram realizados dez preparos cavitários classe V. Uma exposição pulpar mecânica foi produzida com uma sonda exploradora esterilizada, na porção central de cada cavidade. A hemorragia foi controlada com "bolinhas" de algodão esterilizadas. O esmalte, dentina e local da exposição pulpar de cinco dentes foram condicionados com ácido fosfórico a 35%, seguido da aplicação de um sistema adesivo (Scotchbond Multi-Uso - 3M). Nos outros cinco dentes, um cimento de hidróxido de cálcio (Hydro C - Dentsply) foi aplicada no local da exposição pulpar antes da aplicação do mesmo sistema adesivo. Todos os dentes foram restaurados com uma resina composta (Z-100 - 3M). Após 7, 30 ou 45 dias os cães foram anestesiados e perfundidos com solução salina seguida de uma solução de formalina neutra tamponada. A maxila e a mandíbula foram seccionadas em três partes e estocadas em uma solução para desmineralização. Após a desmineralização óssea, todos os dentes foram cortados, incluídos em parafina e seccionados longitudinalmente. A seguir todos os dentes foram corados com hematoxilina e eosina e observados em microscópio de luz. Os resultados demonstraram a presença e persistência de uma resposta inflamatória de diferentes intensidades nos três períodos experimentais. Não houve variação na resposta inflamatória pelos diferentes tratamentos propostos

Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta

The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.<br>O objetivo deste estudo foi determinar o efeito da polimerização gradual, mediante a utilização de aparelhos de Quartzo-Tungustênio-Halógena (QTH) e Arco de Plasma de Xenônio (PAC), no selamento marginal de restaurações classe V em resina composta com margens localizadas em dentina. Setenta e cinco incisivos bovinos receberam preparos de cavidades classe V, na raiz, com o intuito de situar as margens cavitárias em dentina. Os dentes foram divididos em cinco grupos de acordo com o método de fotoativação. As cavidades, depois de condicionadas, foram tratadas com o sistema adesivo Single Bond (3M Dental) e restauradas com a resina composta Z100 (3M Dental) pela técnica incremental. A fotoativação foi realizada para cada grupo como descrito a seguir: Grupo I: PAC pelo método de fotoativação constante: 1600mW/cm² - 3s; Grupo II: PAC pelo método de fotoativação por passos (800mW/cm² - 2s, subindo automaticamente para 1600mW/cm² - 4s); Grupo III: QTH pelo método de fotoativação constante: 400 mW/cm² - 40s; Grupo IV: QTH pelo método de fotoativação em rampa: 100 a 600 mW/cm² - 15s, permanecendo a 600mW/cm2 por mais 25s; Grupo V: QTH pelo método de fotoativação por pulso: 200 mW/cm² - 3s, tempo de espera de 3min.e a seguir 600mW/cm² - 30s. Os dentes foram armazenados em água destilada a 37ºC por 30 dias e então submetidos à ciclagem térmica, por 500 ciclos à 5 ºC e 55 ºC. Os ápices dos dentes foram selados com resina composta e os dentes foram cobertos com duas camadas de esmalte para unha, antes da sua imersão em fucsina básica a 0,5%. Os dentes foram seccionados e os cortes foram escaneados para avaliação da área infiltrada por corante por um programa de computador (Image Tools). Os cortes foram também visualizados com lupa para a determinação do grau de penetração do corante na interface dente-restauração por escores. Diferenças estatisticamente significantes foram observadas entre os grupos quanto ao grau e à área de penetração de corante (p < 0,05). Os grupos I e II apresentaram valores significantemente mais altos de infiltração e penetração do corante que os grupos III, IV e V. Em conclusão, o uso da fonte de PAC, no modo constante e por passos, resultou em valores significantemente maiores de infiltração marginal quando comparados com a intensidade de luz média emitida pelos aparelhos de QTH. Os métodos de fotoativação por pulso, rampa e continuo com a fonte de QTH resultaram num grau similar de microinfiltração