    Valence instability of cerium under pressure in the Kondo-like perovskite La0.1_{0.1}Ce0.4_{0.4}Sr0.5_{0.5}MnO3_3

    Full text link
    Effect of hydrostatic pressure and magnetic field on electrical resistance of the Kondo-like perovskite manganese oxide, La0.1_{0.1}Ce0.4_{0.4}Sr0.5_{0.5}MnO3_3 with a ferrimagnetic ground state, have been investigated up to 2.1 GPa and 9 T. In this compound, the Mn-moments undergo double exchange mediated ferromagnetic ordering at TCT_{\rm C} \sim 280 K and there is a resistance maximum, TmaxT_{\rm max} at about 130 K which is correlated with an antiferromagnetic ordering of {\it cerium} with respect to the Mn-sublattice moments. Under pressure, the TmaxT_{\rm max} shifts to lower temperature at a rate of dTmaxT_{max}/dPP = -162 K/GPa and disappears at a critical pressure PcP_{\rm c} \sim 0.9 GPa. Further, the coefficient, mm of logT-logT term due to Kondo scattering decreases linearly with increase of pressure showing an inflection point in the vicinity of PcP_{\rm c}. These results suggest that {\it cerium} undergoes a transition from Ce3+^{3+} state to Ce4+^{4+}/Ce3+^{3+} mixed valence state under pressure. In contrast to pressure effect, the applied magnetic field shifts TmaxT_{\rm max} to higher temperature presumably due to enhanced ferromagnetic Mn moments.Comment: to be published in Phys. Rev. B (rapid commun

    High Pressure X-Ray Diffraction Study of UMn2Ge2

    Full text link
    Uranium manganese germanide, UMn2Ge2, crystallizes in body-centered tetragonal ThCr2Si2 structure with space group I4/mmm, a = 3.993A and c = 10.809A under ambient conditions. Energy dispersive X-ray diffraction was used to study the compression behaviour of UMn2Ge2 in a diamond anvil cell. The sample was studied up to static pressure of 26 GPa and a reversible structural phase transition was observed at a pressure of ~ 16.1 GPa. Unit cell parameters were determined up to 12.4 GPa and the calculated cell volumes were found to be well reproduced by a Murnaghan equation of state with K0 = 73.5 GPa and K' = 11.4. The structure of the high pressure phase above 16.0 GPa is quite complicated with very broad lines and could not be unambiguously determined with the available instrument resolution

    Effects of Disorder in FeSe : An Ab Initio Study

    Full text link
    Using the coherent-potential approximation, we have studied the effects of excess Fe, Se-deficiency, and substitutions of S, Te on Se sub-lattice and Co, Ni and Cu on Fe sub-lattice in FeSe. Our results show that (i) a small amount of excess Fe substantially disorders the Fe-derived bands while Se-deficiency affects mainly the Se-derived bands, (ii) the substitution of S or Te enhances the possibility of Fermi surface nesting, specially in FeSe0.5_{0.5}Te0.5_{0.5}, in spite of disordering the Se-derived bands, (iii) the electron doping through Co, Ni or Cu disorders the system and pushes down the Fe-derived bands, thereby destroying the possibility of Fermi surface nesting. A comparison of these results with the rigid-band, virtual-crystal and supercell approximations reveals the importance of describing disorder with the coherent-potential approximation.Comment: Redone VCA calculations, and some minor changes. (Accepted for publication in Journal of Physics:Condensed Matter

    Enhanced Impurity Scattering due to Quantum Critical Fluctuations

    Full text link
    It is shown on the basis of the lowest order perturbation expansion with respect to critical fluctuations that the critical fluctuations give rise to an enhancement of the potential scattering of non-magnetic impurities. This qualitatively accounts for the enhancement of the resistivity due to impurities which has been observed in variety of systems near the quantum critical point, while the higher order processes happen to give much larger enhancement as seen from the Ward identity arguments. The cases with dynamical critical exponent zz=2 and zz=3 are discussed explicitly.Comment: Submitted to J. Phys. Soc. Jpn. on 27 September, 200

    Thermodynamic and Transport Properties of CeMg2Cu9 under Pressure

    Full text link
    We report the transport and thermodynamic properties under hydrostatic pressure in the antiferromagnetic Kondo compound CeMg2Cu9 with a two-dimensional arrangement of Ce atoms. Magnetic specific heat Cmag(T) shows a Schottky-type anomaly around 30 K originating from the crystal electric field (CEF) splitting of the 4f state with the first excited level at \Delta_{1}/kB = 58 K and the second excited level at \Delta_{2}/kB = 136 K from the ground state. Electric resistivity shows a two-peaks structure due to the Kondo effect on each CEF level around T_{1}^{max} = 3 K and T_{2}^{max} = 40 K. These peaks merge around 1.9 GPa with compression. With increasing pressure, Neel temperature TN initially increases and then change to decrease. TN finally disappears at the quantum critical point Pc = 2.4 GPa.Comment: 10 pages, 6 figure

    Magnetic Field and Pressure Phase Diagrams of Uranium Heavy-Fermion Compound U2_2Zn17_{17}

    Full text link
    We have performed magnetization measurements at high magnetic fields of up to 53 T on single crystals of a uranium heavy-fermion compound U2_2Zn17_{17} grown by the Bridgman method. In the antiferromagnetic state below the N\'{e}el temperature TNT_{\rm N} = 9.7 K, a metamagnetic transition is found at HcH_c \simeq 32 T for the field along the [112ˉ\bar{2}0] direction (aa-axis). The magnetic phase diagram for the field along the [112ˉ\bar{2}0] direction is given. The magnetization curve shows a nonlinear increase at HmH_m \simeq 35 T in the paramagnetic state above TNT_{\rm N} up to a characteristic temperature TχmaxT_{{\chi}{\rm max}} where the magnetic susceptibility or electrical resistivity shows a maximum value. This metamagnetic behavior of the magnetization at HmH_m is discussed in comparison with the metamagnetic magnetism of the heavy-fermion superconductors UPt3_3, URu2_2Si2_2, and UPd2_2Al3_3. We have also carried out high-pressure resistivity measurement on U2_2Zn17_{17} using a diamond anvil cell up to 8.7 GPa. Noble gas argon was used as a pressure-transmitting medium to ensure a good hydrostatic environment. The N\'{e}el temperature TNT_{\rm N} is almost pressure-independent up to 4.7 GPa and starts to increase in the higher-pressure region. The pressure dependences of the coefficient of the T2T^2 term in the electrical resistivity AA, the antiferromagnetic gap Δ\Delta, and the characteristic temperature TρmaxT_{{\rho}{\rm max}} are discussed. It is found that the effect of pressure on the electronic states in U2_2Zn17_{17} is weak compared with those in the other heavy fermion compounds

    Interplay between magnetism and superconductivity and appearance of a second superconducting transition in alpha-FeSe at high pressure

    Full text link
    We synthesized tetragonal alpha-FeSe by melting a powder mixture of iron and selenium at high pressure. Subsequent annealing at normal pressure results in removing traces of hexagonal beta- FeSe, formation of a rather sharp transition to superconducting state at Tc ~ 7 K, and the appearance of a magnetic transition near Tm = 120 K. Resistivity and ac-susceptibility were measured on the annealed sample at hydrostatic pressure up to 4.5 GPa. A magnetic transition visible in ac-susceptibility shifts down under pressure and the resistive anomaly typical for a spin density wave (SDW) antiferromagnetic transition develops near the susceptibility anomaly. Tc determined by the appearance of a diamagnetic response in susceptibility, increases linearly under pressure at a rate dTc/dP = 3.5 K/GPa. Below 1.5 GPa, the resistive superconducting transition is sharp; the width of transition does not change with pressure; and, Tc determined by a peak in drho/dT increases at a rate ~ 3.5 K/GPa. At higher pressure, a giant broadening of the resistive transition develops. This effect cannot be explained by possible pressure gradients in the sample and is inherent to alpha-FeSe. The dependences drho(T)/dT show a signature for a second peak above 3 GPa which is indicative of the appearance of another superconducting state in alpha-FeSe at high pressure. We argue that this second superconducting phase coexists with SDW antiferromagnetism in a partial volume fraction and originates from pairing of charge carriers from other sheets of the Fermi surface

    Upper critical field, lower critical field and critical current density of FeTe0.60Se0.40 single crystal

    Full text link
    The transport and magnetic studies are performed on high quality FeTe0.60Se0.40 single crystals to determine the upper critical fields (Hc2), lower critical field (Hc1) and the Critical current density (Jc). The value of upper critical field Hc2 are very large, whereas the activation energy as determined from the slope of the Arrhenius plots are was found to be lower than that in the FeAs122 superconductor. The lower critical field was determined in ab direction and c direction of the crystal, and was found to have a anisotropy of 'gamma'{=(Hc1//c) / (Hc1//b)} ~ 4. The magnetic isotherms measured up to 12 Tesla shows the presence of fishtail behavior. The critical current densities at 1.8K of the single crystal was found to almost same in both ab and c direction as 1X105 Amp/cm2 in low field regime.Comment: 9 pages, 6 figure