Introduction of enzymatically degradable poly(trimethylene carbonate) microspheres into an injectable calcium phosphate cement

Poly(trimethylene carbonate) (PTMC) is an enzymatically degradable polyester with rubber-like properties. Introduction of this polymer into an injectable calcium phosphate bone cement can therefore be used to introduce macroporosity into the cement for tissue engineering purposes as well as to improve mechanical properties. Aim of this study was to investigate calcium phosphate cements with incorporated PTMC microspheres (PTMC CPCs) on their physical/mechanical properties and in vitro degradation characteristics. Therefore, composites were tested on setting time and mechanical strength as well as subjected to phosphate buffered saline (PBS) and enzyme containing medium. PTMC CPCs (12.5 and 25 wt%) with molecular weights of 52.7 kg mol−1 and 176.2 kg mol−1 were prepared, which showed initial setting times similar to that of original CPC. Though compression strength decreased upon incorporation of PTMC microspheres, elastic properties were improved as strain-at-yield increased with increasing content of microspheres. Sustained degradation of the microspheres inside PTMC CPC occurred when incubated in the enzymatic environment, but not in PBS, which resulted in an interconnected macroporosity for the 25 wt% composites

Physicochemical properties and applications of poly(lactic-co-glycolic acid) for use in bone regeneration

Item does not contain fulltextPoly(lactic-co-glycolic acid) (PLGA) is the most often used synthetic polymer within the field of bone regeneration owing to its biocompatibility and biodegradability. As a consequence, a large number of medical devices comprising PLGA have been approved for clinical use in humans by the American Food and Drug Administration. As compared with the homopolymers of lactic acid poly(lactic acid) and poly(glycolic acid), the co-polymer PLGA is much more versatile with regard to the control over degradation rate. As a material for bone regeneration, the use of PLGA has been extensively studied for application and is included as either scaffolds, coatings, fibers, or micro- and nanospheres to meet various clinical requirements

In vivo bone response and mechanical evaluation of electrosprayed CaP nanoparticle coatings using the iliac crest of goats as an implantation model.

Contains fulltext : 88092.pdf (publisher's version ) (Closed access)Recent trends in clinical implantology include the use of endosseous dental implant surfaces embellished with nano-sized modifications. The current study was initiated to evaluate the mechanical properties, as well as the potential beneficial effects, of electrosprayed CaP nanoparticle-coated (nano-CaP) implants on the in vivo osteogenic response, compared with grit-blasted, acid-etched (GAE) implant surfaces as controls. For this purpose nano-CaP coatings were deposited on cylindrical screw-type (St) implants and implanted bilaterally into the iliac crest of goats for 6weeks. In addition to histological and histomorphometrical analyses, insertion torque and removal torque values were measured on implant placement and retrieval, respectively. The present study showed similar insertion and removal torque values for nano-CaP-coated and GAE control implants, with no statistically significant increase in torque value during the implant period for either group. With regard to bone-implant contact and peri-implant bone volume, no significant differences were found between nano-CaP-coated and GAE implants after 6weeks implantation. In conclusion, this study has demonstrated that in situations in which implants are placed in a non-compromised situation using a standard press fit implantation strategy the performance of electrosprayed nano-CaP coatings is comparable with GAE implants, both with respect to implant fixation and bone healing response.1 juni 201