Advanced Integration of Microwave Kiln Technology in Enhancing the Lost-Wax Glass Casting Process: A Study on Methodological Innovations and Practical Implications

Lost-wax glass casting, an esteemed yet technically demanding art form, traditionally relies on specialized, costly kiln equipment, presenting significant barriers to artists regarding equipment affordability, energy efficiency, and the technical mastery required for temperature control. Therefore, this study introduces an innovative approach by integrating a microwave kiln with standard household microwave ovens, thus facilitating the lost-wax glass casting process. This methodological adaptation allows artists to employ readily available home appliances for glass creation, significantly reducing the process’s cost and complexity. Our experimental investigations reveal that, by using a 500W household microwave oven for heating, the silicon carbide (SiC) in microwave kilns can efficiently absorb microwave energy, allowing the kilns to reach temperatures exceeding 700 °C, a critical threshold for casting glass softening. We further demonstrate that by adjusting the number of heating cycles, producing high-quality, three-dimensional(3D) glass artworks is feasible, even for large-scale projects. In addition, the microwave kiln can be used as an effective cooling tool to uniformly cool the formed casting glass. This study presents a possible alternative to conventional kiln technology and marks a paradigm shift in glassmaking, offering a more accessible and sustainable avenue for artists and practitioners

A Characteristic Study of Polylactic Acid/Organic Modified Montmorillonite (PLA/OMMT) Nanocomposite Materials after Hydrolyzing

In this study, the montmorillonite (MMT) clay was modified with NH4Cl, and then the structures were exfoliated or intercalated in a polylactic acid (PLA) matrix by a torque rheometer in the ratio of 0.5, 3.0, 5.0 and 8.0 wt%. X-ray diffraction (XRD) revealed that the organic modified-MMT(OMMT) was distributed successfully in the PLA matrix. After thermal pressing, the thermal stability of the mixed composites was measured by a TGA. The mixed composites were also blended with OMMT by a co-rotating twin screw extruder palletizing system, and then injected for the ASTM-D638 standard specimen by an injection machine for measuring the material strength by MTS. The experimental results showed that the mixture of organophilic clay and PLA would enhance the thermal stability. In the PLA mixed with 3 wt% OMMT nanocomposite, the TGA maximum decomposition temperature (Tmax) rose from 336.84 °C to 339.08 °C. In the PLA mixed with 5 wt% OMMT nanocomposite, the loss of temperature rose from 325.14 °C to 326.48 °C. In addition, the elongation rate increased from 4.46% to 10.19% with the maximum loading of 58 MPa. After the vibrating hydrolysis process, the PLA/OMMT nanocomposite was degraded through the measurement of differential scanning calorimetry (DSC) and its Tg, Tc, and Tm1 declined

Comparative Studies on Carbon Paste Electrode Modified with Electroactive Polyamic Acid and Corresponding Polyimide without/with Attached Sulfonated Group for Electrochemical Sensing of Ascorbic Acid

In this study, electroactive poly (amic acid) (EPAA) and corresponding polyimide (EPI) without or with a sulfonated group (i.e., S-EPAA, and S-EPI) were prepared and applied in electrochemical sensing of ascorbic acid (AA). The electroactive polymers (EAPs) containing EPAA/EPI and S-EPAA/S-EPI were synthesized by using an amine-capped aniline trimer (ACAT) and sulfonated amine-capped aniline trimer (S-ACAT) as an electroactive segment that controlled the redox capability and influenced the degree of sensitivity of the EAPs towards AA. Characterization of the as-prepared EAPs was identified by FTIR spectra. The redox capability of the EAPs was investigated by electrochemical cyclic voltammetric studies. It should be noted that the redox capability of the EAPs was found to show the following trend: S-EPAA > S-EPI > EPAA > EPI. For the electrochemical sensing studies, a sensor constructed from an S-EPAA-modified carbon paste electrode (CPE) demonstrated 2-fold, 1.27-fold, and 1.35-fold higher electro-catalytic activity towards the oxidation of AA, compared to those constructed using a bare CPE, S-EPI-, and EPI/EPAA-modified CPE, respectively. The higher redox capability of S-EPAA-modified CPE exhibited a good electrochemical response towards AA at a low oxidative potential, with good stability and selectivity. Moreover, an electrochemical sensor constructed from S-EPAA-modified CPE was found to reveal better selectivity for a tertiary mixture of AA/DA/UA, as compared to that of EPI-modified, EPAA-modified and S-EPI-modified CPE, based on a series of differential pulse voltammograms

The Synthesis of Biodegradable Poly(L-Lactic Acid)-Polyethylene Glycols Copolymer/Montmorillonite Nanocomposites and Analysis of the Crystallization Properties

This study makes use of polycondensation to produce poly (L-lactic acid)-(polyethylene glycols), a biodegradable copolymer, then puts it with organically modified montmorillonite (o-MMT) going through an intercalation process to produce a series of nanocomposites of PLLA-PEG/o-MMT. The exfoliation and intercalation of the montmorillonite-layered structure could be found through X-ray diffraction and transmission electron microscopy. The lower the molecular weight of poly (ethylene glycol), the more obvious the exfoliation and dispersion. The nanocomposites were investigated under non-isothermal crystallization and isothermal crystallization separately via differential scanning calorimetry (DSC). After the adding of o-MMT to PLLA-PEG copolymers, it was found that the PLLA-PEG nanocomposites crystallized slowly and the crystallization peak tended to become broader during the non-isothermal crystallization process. Furthermore, the thermal curve of the non-isothermal melt crystallization process of PLLA-PEG copolymers with different proportions of o-MMT showed that the melting point decreased gradually with the increase of o-MMT content. In the measurement of isothermal crystallization, increasing the o-MMT of the PLLA-PEG copolymers would increase the t1/2 (crystallization half time) for crystallization and decrease the value of ΔHc. However, the present study results suggest that adding o-MMT could affect the crystallization rate of PLLA-PEG copolymers. The o-MMT silicate layer was uniformly dispersed in the PLLA-PEG copolymers, forming a nucleating agent. The crystallization rate and the regularity of the crystals changed with the increase of the o-MMT content, which further affected the crystallization enthalpies

The Synthesis of Biodegradable Poly(L-Lactic Acid)-Polyethylene Glycols Copolymer/Montmorillonite Nanocomposites and Analysis of the Crystallization Properties

This study makes use of polycondensation to produce poly (L-lactic acid)-(polyethylene glycols), a biodegradable copolymer, then puts it with organically modified montmorillonite (o-MMT) going through an intercalation process to produce a series of nanocomposites of PLLA-PEG/o-MMT. The exfoliation and intercalation of the montmorillonite-layered structure could be found through X-ray diffraction and transmission electron microscopy. The lower the molecular weight of poly (ethylene glycol), the more obvious the exfoliation and dispersion. The nanocomposites were investigated under non-isothermal crystallization and isothermal crystallization separately via differential scanning calorimetry (DSC). After the adding of o-MMT to PLLA-PEG copolymers, it was found that the PLLA-PEG nanocomposites crystallized slowly and the crystallization peak tended to become broader during the non-isothermal crystallization process. Furthermore, the thermal curve of the non-isothermal melt crystallization process of PLLA-PEG copolymers with different proportions of o-MMT showed that the melting point decreased gradually with the increase of o-MMT content. In the measurement of isothermal crystallization, increasing the o-MMT of the PLLA-PEG copolymers would increase the t1/2 (crystallization half time) for crystallization and decrease the value of ΔHc. However, the present study results suggest that adding o-MMT could affect the crystallization rate of PLLA-PEG copolymers. The o-MMT silicate layer was uniformly dispersed in the PLLA-PEG copolymers, forming a nucleating agent. The crystallization rate and the regularity of the crystals changed with the increase of the o-MMT content, which further affected the crystallization enthalpies

Leaf on a Film: Mesoporous Silica-Based Epoxy Composites with Superhydrophobic Biomimetic Surface Structure as Anti-Corrosion and Anti-Biofilm Coatings

In this study, a series of amine-modified mesoporous silica (AMS)-based epoxy composites with superhydrophobic biomimetic structure surface of Xanthosoma sagittifolium leaves (XSLs) were prepared and applied as anti-corrosion and anti-biofilm coatings. Initially, the AMS was synthesized by the base-catalyzed sol–gel reaction of tetraethoxysilane (TEOS) and triethoxysilane (APTES) through a non-surfactant templating route. Subsequently, a series of AMS-based epoxy composites were prepared by performing the ring-opening polymerization of DGEBA with T-403 in the presence of AMS spheres, followed by characterization through FTIR, TEM, and CA. Furthermore, a nano-casting technique with polydimethylsiloxane (PDMS) as the soft template was utilized to transfer the surface pattern of natural XSLs to AMS-based epoxy composites, leading to the formation of AMS-based epoxy composites with biomimetic structure. From a hydrophilic CA of 69°, the surface of non-biomimetic epoxy significantly increased to 152° upon introducing XSL surface structure to the AMS-based epoxy composites. Based on the standard electrochemical anti-corrosion and anti-biofilm measurements, the superhydrophobic BEAMS3 composite was found to exhibit a remarkable anti-corrosion efficiency of ~99% and antimicrobial efficacy of 82% as compared to that of hydrophilic epoxy coatings

The Sequential Change in Left Ventricular Function among Various Cardiovascular Diseases: A 12-Year Study

Background: This 12-year study aimed to compare the longitudinal change in left ventricular diastolic dysfunction (LVDD) between healthy elderly, coronary artery disease (CAD), and hypertension (HTN) patients. Methods: From 2008 to 2020, 1476 patients were included, and 3181 echocardiography examinations were conducted. Finally, 130 participants (36 healthy elderly (79.39 ± 9.51 years old), 51 with CAD (68.31 ± 12.09 years old), and 43 with HTN (68.31 ± 12.09 years old)) with more than a 10-year follow-up period were included in the final analysis. Results: The change in diastolic function was different among these subjects according to the integrated score index (elderly vs. HTN, p = 0.01; CAD vs. HTN, p = 0.01), septal E/e′ ratio (elderly vs. HTN, p p = 0.01), lateral E/e′ ratio (elderly vs. HTN, p p p = 0.03; CAD vs. HTN, p p < 0.05). Conclusion: Under aggressive treatment, diastolic function was relatively preserved in HTN subjects with aging in comparison with elderly and CAD subjects

Erratum to: Guidelines for the use and interpretation of assays for monitoring autophagy (3rd edition) (Autophagy, 12, 1, 1-222, 10.1080/15548627.2015.1100356

non present