Tailoring Photoprotection of Polylactide with New Isobornyl Derivatives of Phenol and Aniline

This article is devoted to the development of new photostabilizers for polylactide (PLA), a polymer that is an environmentally friendly alternative to polymers and is based on fossil raw materials. We have elucidated the role of the reaction center of two potential PLA photoprotectors: N-isobornylaniline and 2-isobornylphenol, in reactions occurring in a polymer matrix under the action of UV-C radiation. PLA samples with the photostabilizers were irradiated under a wavelength of 253.7 nm for 4, 8 and 12 h. The effectiveness of the photostabilizers was evaluated based on FTIR spectrometric data, 1H and 13C NMR, scanning electron microscopy and simultaneous thermal analysis (TG-DSC). Both stabilizers led to the protection of ester bonds between monomer units of PLA. However, 2-isobornylphenol proved to be more effective at a concentration of 0.05 wt.%, while the optimal concentration of N-isobornylaniline was 0.5 wt.% by weight. TG-DSC showed that the addition of N-isobornylaniline led to an increase in PLA resistance to thermal decomposition; the temperature of the onset of weight loss increased by 2.8 °C at 0.05 wt.% and by 8.1 °C at 0.5 wt.% of N-isobornylaniline. The photoprotector 2-isobornylphenol, on the contrary, reduced the thermal stability of PLA

Isobornyl and Isocamphyl Photostabilizers in Poly(lactic acid)-Based Electrospun Fibers

In this work, electrospun polylactide fibers with new photostabilizing additives, 4-methyl-2,6-diisobornylphenol (DIBP) and N-isocamphylaniline (NICA), have been tested under the influence of UV-C radiation (254 nm). The changes in the polymers’ chemical structure under UV-C radiation were revealed through the increase in absorption in the 3600–3100 cm−1 region in regard to the FTIR spectra. In the samples that were irradiated for 1 h, the stabilizing effect of the photoprotectors became most noticeable as the difference in the content of the hydroxyl groups in stabilized and the pure PLA reached a maximum. The TG–DSC method revealed that the most sensitive indicator of the irradiation effect was the glass transition temperature (Tg), which persisted after 2 h of irradiation when using photostabilizers and their combinations. The PLA/DIBP(1) and PLA/NICA(1) samples showed the best results in protecting PLA from UV-C radiation based on the Tg values; although, the mixture of DIBP and NICA was not as effective. The chemical structure of the photostabilized PLA samples was studied using NMR, GPC, and Py–GC/MS analysis. The electrospun polylactide fibers were mechanically tested and the effects of the electrospun samples on cell viability were studied