Optimization of Suture-Free Laser-Assisted Vessel Repair by Solder-Doped Electrospun Poly(ε-caprolactone) Scaffold

Poor welding strength constitutes an obstacle in the clinical employment of laser-assisted vascular repair (LAVR) and anastomosis. We therefore investigated the feasibility of using electrospun poly(ε-caprolactone) (PCL) scaffold as reinforcement material in LAVR of medium-sized vessels. In vitro solder-doped scaffold LAVR (ssLAVR) was performed on porcine carotid arteries or abdominal aortas using a 670-nm diode laser, a solder composed of 50% bovine serum albumin and 0.5% methylene blue, and electrospun PCL scaffolds. The correlation between leaking point pressures (LPPs) and arterial diameter, the extent of thermal damage, structural and mechanical alterations of the scaffold following ssLAVR, and the weak point were investigated. A strong negative correlation existed between LPP and vessel diameter, albeit LPP (484 ± 111 mmHg) remained well above pathophysiological pressures. Histological analysis revealed that thermal damage extended into the medial layer with a well-preserved internal elastic lamina and endothelial cells. Laser irradiation of PCL fibers and coagulation of solder material resulted in a strong and stiff scaffold. The weak point of the ssLAVR modality was predominantly characterized by cohesive failure. In conclusion, ssLAVR produced supraphysiological LPPs and limited tissue damage. Despite heat-induced structural/mechanical alterations of the scaffold, PCL is a suitable polymer for weld reinforcement in medium-sized vessel ssLAVR

Endoluminal laser-assisted vascular anastomosis—an in vivo study in a pig model

Microvascular surgery is time consuming and requires high expertise. Laser-assisted vascular anastomosis (LAVA) is a promising sutureless technique that has the potential to facilitate this procedure. In this study, we evaluate the handling of our soldering material and the 1-week patency rate in a porcine model. Six pigs were subjected to LAVA. For each pig, the saphenous artery on one side was transected while the contralateral side was used as control. A porous polycaprolactone scaffold soaked in 40% (w/w) bovine serum albumin solution in combination with 0.1% (w/w) indocyanine green was wrapped at the anastomosis site and at the control site. Both sides were then soldered with a diode laser coupled into a light diffuser fiber emitting radiation with a wavelength of 808 nm and a power of 2-2.2 W. Vessels were successfully soldered with a 100% immediate patency rate. The 1-week patency rate was 83% for the anastomoses versus 67% for the control side. Vessels irradiated for 80 to 90 s tended to maintain the highest patency rate. Macroscopically, there was no difference between the two sides. The patch was easy to handle provided that the environment could be kept dry. This study shows the potential and the limitations of endoluminal LAVA as a one-step procedure without the use of stay sutures. Further studies are needed to improve the soldering material, the long-term patency rate, and standardized irradiation parameters. The long-term effects of laser soldering on the vessel wall remain to be determined