Scanning probe microscopy imaging of metallic nanocontacts

We show scanning probe microscopy measurements of metallic nanocontacts between controlled electromigration cycles. The nanowires used for the thinning process are fabricated by shadow evaporation. The highest resolution obtained using scanning force microscopy is about 3 nm. During the first few electromigration cycles the overall slit structure of the nanocontact is formed. The slit first passes along grain boundaries and then at a later stage vertically splits grains in the course of consuming them. We find that first the whole wire is heated and later during the thinning process as the slit forms the current runs over several smaller contacts which needs less power.Comment: 4 pages, 4 figure

Combinatorial doping of TiO_2 with platinum (Pt), chromium (Cr), vanadium (V), and nickel (Ni) to achieve enhanced photocatalytic activity with visible light irradiation

Titanium dioxide (TiO_2) was doped with the combination of several metal ions including platinum (Pt), chromium (Cr), vanadium (V), and nickel (Ni). The doped TiO_2 materials were synthesized by standard sol-gel methods with doping levels of 0.1 to 0.5 at.%. The resulting materials were characterized by x-ray diffraction (XRD), BET surface-area measurement, scanning electron microscopy (SEM), and UV-vis diffuse reflectance spectroscopy (DRS). The visible light photocatalytic activity of the codoped samples was quantified by measuring the rate of the oxidation of iodide, the rate of degradation of methylene blue (MB), and the rate of oxidation of phenol in aqueous solutions at λ > 400 nm. 0.3 at.% Pt-Cr-TiO_2 and 0.3 at.% Cr-V-TiO_2 showed the highest visible light photocatalytic activity with respect to MB degradation and iodide oxidation, respectively. However, none of the codoped TiO_2 samples were found to have enhanced photocatalytic activity for phenol degradation when compared to their single-doped TiO_2 counterparts

Effects of the preparation method of the ternary CdS/TiO_2/Pt hybrid photocatalysts on visible light-induced hydrogen production

A variety of combinations of CdS, TiO2, and Pt in preparing the hybrid catalysts were studied for hydrogen production under visible light ( > 420 nm) irradiation. The preparation method sensitively influenced the activity of the ternary hybrid catalysts. The formation of the potential gradient at the interface between CdS and TiO2 is necessary in achieving the efficient charge separation and transfer and how the platinum as a cocatalyst is loaded onto the CdS/TiO2 hybrid catalysts determines the overall hydrogen production efficiency. The common method of photoplatinization of CdS/TiO2 hybrid [Pt-(CdS/TiO2)] was much less efficient than the present method in which Pt was photodeposited on bare TiO2, which was followed by the deposition of CdS [CdS/(Pt-TiO2)]. The CdS/(Pt-TiO2) has the hydrogen production rate ranging (6–9) × 10-3 mol h-1 g-1, which is higher by a factor of 3–30 than that of Pt-(CdS/TiO2). The photocatalytic activity of the ternary hybrid catalysts was extremely sensitive to where the platinum is loaded. The photoactivity of the hybrid catalyst was also assessed in terms of the photocurrent collected by the methyl viologen electron shuttle in the catalyst suspension. CdS/(Pt-TiO2) generated higher photocurrents than Pt-(CdS/TiO2) by a factor of 2–7. The extreme sensitivity of the preparation method to the hydrogen production activity should be taken into account when hybrid photocatalysts are designed and prepared

Effects of Single Metal-Ion Doping on the Visible-Light Photoreactivity of TiO_2

Titanium dioxide (M-TiO_2), which was doped with 13 different metal ions (i.e., silver (Ag^+), rubidium (Rb^+), nickel (Ni^(2+)), cobalt (Co^(2+)), copper (Cu^(2+)), vanadium (V^(3+)), ruthenium (Ru^(3+)), iron (Fe^(3+)), osmium (Os^(3+)), yttrium (Y^(3+)), lanthanum (La^(3+)), platinum (Pt^(4+), Pt^(2+)), and chromium (Cr3+, Cr6+)) at doping levels ranging from 0.1 to 1.0 at. %, was synthesized by standard sol−gel methods and characterized by X-ray diffraction, BET surface area measurement, SEM, and UV−vis diffuse reflectance spectroscopy. Doping with Pt(IV/II), Cr(III), V(III), and Fe(III) resulted in a lower anatase to rutile phase transformation (A−R phase transformation) temperature for the resultant TiO_2 particles, while doping with Ru(III) inhibited the A−R phase transformation. Metal-ion doping also resulted in a red shift of the photophysical response of TiO_2 that was reflected in an extended absorption in the visible region between 400 and 700 nm. In contrast, doping with Ag(I), Rb(I), Y(III), and La(III) did not result in a red shift of the absorption spectrum of TiO_2. As confirmed by elemental composition analysis by energy dispersive X-ray spectroscopy, the latter group of ions was unable to be substituted for Ti(IV) in the crystalline matrix due to their incompatible ionic radii. The photocatalytic activities of doped TiO_2 samples were quantified in terms of the photobleaching of methylene blue, the oxidation of iodide (I^(−)), and the oxidative degradation of phenol in aqueous solution both under visible-light irradiation (λ > 400 nm) and under broader-band UV−vis irradiation (λ > 320 nm). Pt- and Cr-doped TiO_2, which had relatively high percentages of rutile in the particle phase, showed significantly enhanced visible-light photocatalytic activity for all three reaction classes