3 research outputs found
Biopolymers and Their Application in Bioprinting Processes for Dental Tissue Engineering
Dental tissues are composed of multiple tissues with complex organization, such as dentin, gingiva, periodontal ligament, and alveolar bone. These tissues have different mechanical and biological properties that are essential for their functions. Therefore, dental diseases and injuries pose significant challenges for restorative dentistry, as they require innovative strategies to regenerate damaged or missing dental tissues. Biomimetic bioconstructs that can effectively integrate with native tissues and restore their functionalities are desirable for dental tissue regeneration. However, fabricating such bioconstructs is challenging due to the diversity and complexity of dental tissues. This review provides a comprehensive overview of the recent developments in polymer-based tissue engineering and three-dimensional (3D) printing technologies for dental tissue regeneration. It also discusses the current state-of-the-art, focusing on key techniques, such as polymeric biomaterials and 3D printing with or without cells, used in tissue engineering for dental tissues. Moreover, the final section of this paper identifies the challenges and future directions of this promising research field
Fabrication of Mechanically Reinforced Gelatin/Hydroxyapatite Bio-Composite Scaffolds by Core/Shell Nozzle Printing for Bone Tissue Engineering
In tissue engineering, biocompatible scaffolds are used as 3D cell niches to provide a similar environment to that of native tissue for seeded cells to regenerate the target tissue. When engineering bone tissue, high mechanical strength and calcium phosphate composition are essential factors to consider. In this study, we fabricated biocompatible composite scaffolds composed of synthetic polymers (polycaprolactone (PCL) and poly (vinyl alcohol) (PVA)), natural polymers (gelatin and collagen) and bioceramic (hydroxyapatite; HA) for bone tissue engineering. The synthetic polymers were used to enhance the mechanical properties of the composite scaffolds while the natural protein-based polymers were used to enhance various cellular activities, such as cell adhesion and proliferation. Meanwhile, the bioceramic was introduced to promote osteogenic differentiation. Composite scaffolds were evaluated for their physical characteristics, such as mechanical, swelling and protein absorbing properties as well as biological properties (cell proliferation, alkaline phosphatase (ALP) activities and calcium deposition) with human osteoblast-like cells (MG63). Consequently, incorporation of hydroxyapatite into the gelatin/PVA (C-GPH) scaffold showed 5-fold and 1.5-fold increase in calcium deposition and ALP activities, respectively compared to gelatin/PVA scaffold (C-GP). Moreover, compressive modulus also increased 1.8-fold. Integration of PCL core into gelatin/PVA/hydroxyapatite scaffold (C-PGPH) further amplified the compressive modulus 1.5-fold. In conclusion, the scaffold that is reinforced with HA particles and integrated with PCL core of the struts showed significant potential in field of bone tissue engineering
Bio-printing of aligned GelMa-based cell-laden structure for muscle tissue regeneration
Volumetric muscle loss (VML) is associated with a severe loss of muscle tissue that overwhelms the regenerative potential of skeletal muscles. Tissue engineering has shown promise for the treatment of VML injuries, as evidenced by various preclinical trials. The present study describes the fabrication of a cell-laden GelMa muscle construct using an in situ crosslinking (ISC) strategy to improve muscle functionality. To obtain optimal biophysical properties of the muscle construct, two UV exposure sources, UV exposure dose, and wall shear stress were evaluated using C2C12 myoblasts. Additionally, the ISC system showed a significantly higher degree of uniaxial alignment and myogenesis compared to the conventional crosslinking strategy (post-crosslinking). To evaluate the in vivo regenerative potential, muscle constructs laden with human adipose stem cells were used. The VML defect group implanted with the bio-printed muscle construct showed significant restoration of functionality and muscular volume. The data presented in this study suggest that stem cell-based therapies combined with the modified bioprinting process could potentially be effective against VML injuries