E-Glass Fiber Reinforced Composites in Dental Applications

Fiber reinforced composites (FRCs) are more and more widely applied in dentistry to substitute for metallic restorations: periodontal splints, fixed partial dentures, endodontic posts, orthodontic appliances, and some other indirect restorations. In general in FRCs, the fiber reinforcement provides the composite structure with better biomechanical performance due to their superior properties in tension and flexure. Nowadays, the E-glass fiber is most frequently used because of its chemical resistance and relatively low cost. Growing interest is being paid to enhance its clinical performance. Moreover, various techniques are utilized to reinforce the adhesion between the fiber and the matrix. Oral conditions set special requirements and challenges for the clinical applications of FRCs. The biomechanical properties of dental materials are of high importance in dentistry, and given this, there is on-going scientific interest to develop E-glass fiber reinforced composite systems. FRCs are generally biocompatible and their toxicity is not a concern. © 2011 The Author(s).published_or_final_versionSpringer Open Choice, 21 Feb 201

Identification and quantification of monomers released from dental composites using HPLC

The aim of this study was to detect and quantify the main residual monomers released from composites, using high performance liquid chromatography (HPLC). Discs were made with dental composites (Herculite XRV, Tetric Ceram and Filtek Z250) and immersed in deionized water at 37ºC for 28 days, with water changes in 1, 7, 14 and 21 days. The mean concentration of residual monomers were subject to the Kruskal-Wallis test (p<0.05). Tetric Ceram exhibited significantly higher concentrations of leached monomers. Bis-GMA was the monomer released in lower concentrations for all the materials. There was no statistical difference between the amounts of TEGDMA and UDMA. Most of the monomers demonstrated maximal concentration at the 7-day period. The HPLC analysis identified Bis-GMA, TEGDMA and UDMA in detectable quantities for all the tested composites.<br>A liberação de monômeros residuais pode afetar o comportamento clínico e a biocompatibilidade dos materiais resinosos. O objetivo deste estudo foi detectar e quantificar os principais monômeros residuais liberados de resinas compostas, usando cromatografia líquida de alta performance (HPLC). Discos foram construídos de resinas compostas de uso odontológico (Herculite XRV, Tetric Ceram and Filtek Z250) e imersos em água deionizada a 37ºC durante 28 dias, com mudanças de água em 24 horas, 7, 14 e 21 dias. As concentrações médias dos monômeros residuais foram submetidas ao teste de Kruskal-Wallis (p<0,05). Tetric Ceram apresentou as maiores concentrações de monômeros lixiviados. Bis-GMA foi o monômero liberado em menores concentrações para todos os materiais. Não houve diferença estatística significante entre TEGDMA e UDMA. A maioria dos monômeros demonstrou máxima concentração no período de 7 dias. A análise por meio de HPLC identificou Bis-GMA, TEGDMA e UDMA em quantidades detectáveis para todas as resinas compostas testadas