Fatigue-Induced Damage in High-Strength Concrete Microstructure

A high-strength concrete subjected to compressive fatigue loading with two maximum stress levels was investigated and the behaviour was evaluated using the macroscopic damage indicators, strain and acoustic emission hits (AE-hits), combined with microstructural analyses utilising light microscopy and scanning electron microscopy (SEM). A clustering technique using Gaussian mixture modelling combined with a posterior probability of 0.80 was firstly applied to the AE-hits caused by compressive fatigue loading, leading to two clusters depending on the maximum stress level. Only a few cracks were visible in the microstructure using light microscopy and SEM, even in phase III of the strain development, which is shortly before failure. However, bluish impregnated areas in the mortar matrix of higher porosity or defects, changing due to the fatigue loading, were analysed. Indications were found that the fatigue damage process is continuously ongoing on a micro- or sub-microscale throughout the mortar matrix, which is difficult to observe on a mesoscale by imaging. Furthermore, the results indicate that two different damage mechanisms take place, which are pronounced depending on the maximum stress level. This might be due to diffuse and widespread compressive damage and localised tensile damage, as the findings documented in the literature suggest

Wave-Induced Distribution of Microplastic in the Surf Zone

In this study, the wave-induced distribution of 13 microplastic (MP) samples of different size, shape, and density was investigated in a wave flume with a sandy mobile beach bed profile. The particle parameter were chosen based on an occurrence probability investigated from the field. MP abundances were analyzed in cross-shore and vertical direction of the test area after over 40,000 regular waves. It was found, that MP particles accumulated in more shallow waters with increasing size and density. Particles with high density (ρs>1.25 g/cm3) have been partly confined into deeper layers of the sloping beach during the formation of the bed profile. Particles with a density lower than that of water used in the experiments floated constantly in the surf zone or deposited on the beach caused by wave run-up. A correlation was found between the settling velocity of the MP particles and the flow velocity at the accumulation point and a power function equation developed. The obtained results were critically discussed with findings from the field and further laboratory studies