Разработка новых видов сорбционных материалов на минеральной основе для извлечения тяжелых металлов из водных сред

В процессе исследования проводилось изучение литературных источников.В результате был разработан новый сорбционный материал на минеральной основе для извлечения тионов кадмия и свинца из водных растворов.In the process of investigation the study of literary sources.In the result there was developed a new sorption material on a mineral basis for izvlecheniya thions of cadmium and lead from aqueous plaster

Türkiye’deki üniversite kütüphanelerinde RDA algısı, süreçler, sorunlar ve Özyeğin Üniversitesi Kütüphanesi örneği

Kütüphane hizmetlerinin her alanında olduğu gibi, yaşanan gelişme ve değişim kütüphane kataloglarındaki değişimi de gerekli kılmış ;kullanıcıya verimli, hızlı bibliyografik bilgi sunma, bilginin kayıtlı olduğu her türlü ortamdaki bilgi kaynağını daha detaylı, anlaşılır ve etkin biçimde tanımlama, ilişkisel veriler sunarak erişilebilirliğini arttırma gibi amaçlar ile daha güçlü ve işlevsel kütüphane kataloglarına ihtiyaç duyulmaya başlanmıştır. Bu doğrultuda Anglo Amerikan Kataloglama Kuralları 2 (AAKK2)’nin yerini alan yeni kataloglama standardı Resource Description and Access (RDA) dünyada ve ülkemizde kimi kütüphanelerde uygulanmaya başlanmıştır. Bu konudaki yeni yaklaşımlar, kurallar, uygulamalar gerek ülkemizde gerekse dünyada halen tartışılmakta; kataloglama ve meta data kütüphanecileri deneyimlerini paylaşmaktadır. Bu çalışmada RDA’nın kısaca yapısı, felsefesi ve terminolojisi literatüre dayalı olarak açıklanacak, Türkiye’deki üniversite kütüphanelerinde çalışan kataloglama kütüphanecilerinin RDA uygulamalarına ilişkin yapılmış bir anketin sonuçlarına dayanarak süreçler, yaşanan sorunlar ve RDA algısı ortaya konulacaktır. Çalışmada, Özyeğin Üniversitesi Kütüphanesi’ndeki RDA uygulamasından bahsedilerek beraberinde kütüphane kataloğunda AAKK’2 ye göre görülen değişim de örneklerle anlatılacaktır

Nucleosomes in gene regulation: theoretical approaches

This work reviews current theoretical approaches of biophysics and bioinformatics for the description of nucleosome arrangements in chromatin and transcription factor binding to nucleosomal organized DNA. The role of nucleosomes in gene regulation is discussed from molecular-mechanistic and biological point of view. In addition to classical problems of this field, actual questions of epigenetic regulation are discussed. The authors selected for discussion what seem to be the most interesting concepts and hypotheses. Mathematical approaches are described in a simplified language to attract attention to the most important directions of this field

Фазовые превращения при кристаллизации Sr2CrMoO6–δ

The sequence of phase transformations in the process of crystallization of the Sr2CrMoO6 by the solid-phase technique from a stoichiometric mixture of simple oxides SrCO3 + 0.5Cr2O3 + MoO, has been investigated. It was determined that the synthesis of the strontium chrome-molybdate proceeds through a series of sequential-parallel stages. By means of the differential thermal analysis and thermogravimetric analysis data, it has been established that five clearly expressed endothermal effects were observed in the temperature range 300—1300 K. It was found that during the studies of the phase transformations sequence in the process of the double perovskite synthesis, SrCrO3, SrMoO4 and Sr2CrO4 are the main concomitant compounds. Herewith, it has been observed that with the annealing temperature increase from 300 to 1270 K, the complex compounds SrCrO4, SrCrO3 (350—550 K) and SrMoO4, Sr2CrO4 (600—750 K) are emerging initially and practically simultaneously. It has been revealed with a subsequent temperature increase that in the temperature range 940—1100 K, the SrMoO4, Sr2CrO4 and SrCrO3 phase concentration dramatically drops with the emerging and growth of the Sr2CrMoO6-δ double perovskite. With that in the range up to 1120—1190 K, the main XRD reflexes intensity for the SrCrO3 and SrMoO4 lowers substantially, and their content in the samples at 1170 К is no more than 7,9 %. During a consideration of the derivative of the SrCrO3, SrMoO4 and Sr2CrO4 phase transformation degree (|(dα/dt)|mах), at which their crystallization rates are maximal, it has been determined that |(dα/dt)|mах for the Sr2CrO4 corresponds to the maximal temperature 1045 K, which indicates the presence of considerable kinetic difficulties at the formation of the Sr2CrO4 phase. Thereafter this phase does not disappear and at its appearance the slowing down of the double perovskite growth takes place. On the base of investigations of the phase transformations dynamics for the obtaining of the single-phase Sr2CrMoO6-δ compound with the superstructural ordering of the Cr/Mo cations and improved magnetic characteristics, the SrCrO3 and SrMoO4 precursors were used with combined heating modes.Исследована последовательность фазовых превращений в процессе кристаллизации Sr2CrMoO6-δ из стехиометрической смеси простых оксидов SrCO3 + 0,5Cr2O3 + MoO. Установлено, что фазообразование хромомолибдата стронция протекает через ряд последовательно-параллельных стадий. Согласно данным дифференциально-термического и термогравиметрического анализов, обнаружено, что в температурном диапазоне 300—1300 К наблюдается пять ярко выраженных эндотермических эффектов. При изучении последовательности фазовых превращений в процессе синтеза двойного перовскита обнаружено, что основными сопутствующими соединениями являются SrCrO3, SrMoO4 и Sr2CrO4. При этом замечено, что с ростом температуры отжига от 300 до 1270 К в исходной смеси первоначально и практически одновременно появляются сложные соединения SrCrO4, SrCrO3 (350—550 К), а затем и SrMoO4, Sr2CrO4 (600—750 К). Показано, что с последующим увеличением температуры в интервале температур 940—1100 К концентрация фаз SrMoO4, Sr2CrO4 и SrCrO3 резко падает с появлением и ростом двойного перовскита Sr2CrMoO6-δ. При этом в интервале температур до 1120—1190 К основные рентгеновские рефлексы фазы Sr2CrO4 уменьшаются незначительно, тогда как интенсивность рентгеновских рефлексов фаз SrCrO3 и SrMoO4 снижается существенно больше и их содержание в образце при температуре 1170 К составляет не более 7,9 %. Анализ амплитудных значений производной степени превращения фаз SrCrO3, SrMoO4 и Sr2CrO4, при которых скорости их кристаллизации максимальны, показал, что для Sr2CrO4 величина |(dα/dt)|mах соответствует наибольшей температуре T = 1045 К. Это указывает на наличие кинетических трудностей при образовании фазы Sr2CrO4, которая в дальнейшем не исчезает, а при ее появлении наблюдается замедление роста двойного перовскита. На основании результатов, полученных при изучении динамики фазовых превращений для формирования однофазного Sr2CrMoO6-δ со сверхструктурным упорядочением Cr/Mo и улучшенными магнитными характеристиками, были применены прекурсоры SrCrO3 и SrMoO4 с использованием комбинированных режимов нагрева