Tribological performance of PVD film systems against plastic counterparts for adhesion-reducing application in injection molds

The deposition of physical vapor deposition (PVD) hard films is a promising approach to enhance the tribological properties of injection molds in plastic processing. However, the adhesion is influenced by the pairing of PVD film and processed plastic. For this reason, the friction behavior of di erent PVD films against polyamide, polypropylene, and polystyrene was investigated in tribometer tests by correlating the relation between the roughness and the adhesion. It was shown that the dispersive and polar surface energy have an impact on the work of adhesion. In particular, Cr-based nitrides with a low polar component exhibit the lowest values ranging from 65.5 to 69.4 mN/m when paired with the polar polyamide. An increased roughness leads to a lower friction due to a reduction of the adhesive friction component, whereas a higher work of adhesion results in higher friction for polyamide and polypropylene. Within this context, most Cr-based nitrides exhibited coe cients of friction below 0.4. In contrast, polystyrene leads to a friction-reducing material transfer. Therefore, a customized deposition of the injection molds with an appropriated PVD film system should be carried out according to the processed plastic

Reduction of ejection forces in injection molding by applying mechanically post-treated CrN and CrAlN PVD films

In injection molding, the reduction of ejection forces is a process relevant aspect to improve the production rates. For this purpose, CrN and CrAlN films were sputtered on cylindrical and quadratic AISI H11 cores of an injection mold in order to investigate their influence on the resulting ejection forces to demold polypropylene test components. Within this context, the ejection forces of the PVD coated cores were compared to those of uncoated cores made of AISI H11. For both the cylindrical and quadratic cores, the as-deposited CrN and CrAlN films exhibit higher ejection forces than the uncoated cores due to the increase of the roughness profile after sputtering. It is known that the ejection forces are directly related to the surface roughness. In order to ensure comparable surface conditions to the uncoated surfaces, and to demonstrate the potential of PVD coated mold surfaces when reducing the ejection forces, the coated surfaces were mechanically post-treated to obtain a similar roughness profile as the uncoated cores. The combination of a PVD deposition and post-treatment ensures a significant reduction of the ejection forces by 22.6% and 23.7% for both core geometries