Li diffusion and electrochromism in amorphous and crystalline vanadium oxide thin film electrodes

Amorphous vanadium oxide films were synthesized onto ITO-coated glass substrates by the hot filament metal oxide deposition technique. The as-deposited samples were heat-treated in an argon atmosphere. X-ray diffraction analysis revealed that the films treated at 200 and 300 ºC were still amorphous, while those treated at 400 and 500 ºC were crystalline, with a V2O5 structure. All electrodes were electrochemically reversible for Li+ intercalation, exhibiting the electrochromic effect, observed from optical transmittance measurements at 632.8 nm. The Li-diffusion coefficient, DC, was measured by the galvanostatic intermittent titration technique (GITT) as function of the inserted charge. For the crystalline films it was observed that the optical absorbance and the DC increase with increasing Li insertion in the single-phase regions of crystalline Li xV2O5 and decrease in the two-phase regions. For the latter, an effective DC was considered. The presence of other vanadium oxides mixed to the V2O5 matrix was inferred for the crystalline films from the chronopotentiometric and DC measurements

Desenvolvimento e avaliação de uma fonte DC de alta tensão para utilização em sistema de deposição de filmes finos por pulverização catódica

RESUMO O trabalho em questão está relacionado ao projeto e construção de uma fonte de alta tensão em corrente contínua utilizando materiais e dispositivos adquiridos no comércio local visando sua aplicação no processo de pulverização catódica. Essa técnica permite a deposição de filmes finos de metais, óxidos e nitretos sobre substratos sólidos. Como teste de funcionamento e aplicação da fonte DC, com a mesma instalada em canhão de pulverização em alto vácuo, filmes finos de diferentes espessuras de cobre, aço inoxidável 304 e tungstênio foram depositados e estudados. Análise de espessura, morfologia, e resistência elétrica e resistividade foram conduzidas. Filmes com resistividade elétrica dependente das espessuras foram obtidos. A fonte DC se mostrou confiável em operação e permite a deposição de uma infinidade de materiais nas mais diferentes espessuras sobre vários tipos de substratos

Plasma-treated Multilayer Graphene: Synthesis And Applications

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)This work presents the study of multilayer graphene (MLG) obtainment and functionalization using plasmas of different gas species. MLGs were obtained using mechanical exfoliation methods of pre-exfoliated graphite in acids. The functionalization of MLGs was made through cold plasma using mixtures of CO2 and Ar gases. Investigation of electrical, optical and morphological properties are presented and discussed. Structure and chemical composition were investigated with Raman, XPS and other techniques. MLGs showed a certain incorporation of oxygen as can be seen in XPS results. We investigated the treatment conditions and the changes in the materials obtained particularly the properties of MLGs films and pellets. Applications of these treated MLGs in super capacitor devices are herein presented and discussed, enabling applications in electronic devices and energy storage areas.CNPqFAPESPFAPEMIGDST/IndiaConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)31st Symposium on Microelectronics Technology and Devices (SBMicro)AUG 29-SEP 03, 2016Belo Horizonte, BRAZI

Li diffusion and electrochromism in amorphous and crystalline vanadium oxide thin film electrodes

Amorphous vanadium oxide films were synthesized onto ITO-coated glass substrates by the hot filament metal oxide deposition technique. The as-deposited samples were heat-treated in an argon atmosphere. X-ray diffraction analysis revealed that the films treated at 200 and 300 ºC were still amorphous, while those treated at 400 and 500 ºC were crystalline, with a V2O5 structure. All electrodes were electrochemically reversible for Li+ intercalation, exhibiting the electrochromic effect, observed from optical transmittance measurements at 632.8 nm. The Li-diffusion coefficient, DC, was measured by the galvanostatic intermittent titration technique (GITT) as function of the inserted charge. For the crystalline films it was observed that the optical absorbance and the DC increase with increasing Li insertion in the single-phase regions of crystalline Li xV2O5 and decrease in the two-phase regions. For the latter, an effective DC was considered. The presence of other vanadium oxides mixed to the V2O5 matrix was inferred for the crystalline films from the chronopotentiometric and DC measurements.Filmes amorfos de óxido de vanádio foram depositados sobre substratos de vidro recobertos com ITO, pela técnica de deposição de filmes de óxidos metálicos por filamento aquecido. Os espectros de difração de raios-X mostraram que os filmes como-depositados tratados termicamente em atmosfera de argônio em 200 e 300 ºC continuaram amorfos e os tratados a 400 e 500 ºC tornaram-se policristalinos, com a estrutura do V2O5. Os eletrodos foram eletroquimicamente reversíveis sob intercalação de Li+, exibindo o efeito eletrocrômico, observado por medidas da transmitância ótica em 632,8 nm. O coeficiente de difusão do Li, DC, foi medido pela técnica de titulação galvanostática intermitente (GITT) em função da carga inserida. Para os filmes cristalinos, a absorbância ótica e o DC aumentam com a quantidade de Li inserido, nas regiões de fase única de Li xV2O5 cristalino e decrescem nas regiões de duas fases. Para essas, um DC efetivo foi considerado. Nos filmes cristalinos foi inferida a presença de outros óxidos de vanádio misturados à matriz de V2O5, através das medidas de cronopotenciometria e de DC.788794Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES

Infrared spectroscopy investigation of various plasma-deposited polymer films irradiated with 170 keV He+ ions

This work illustrates the advantages of using p-polarized radiation at an incidence angle of 70 degrees in contrast to the conventional unpolarized beam at normal (or near-normal) incidence for the infrared spectroscopic study of polycarbosilane, polysilazane and polysiloxane thin films synthesized by plasma enhanced chemical vapor deposition (PECVD) and subsequently irradiated with 170 keV He+ ions at fluences from 1 x 10(14) to 1 x 10(16) cm(-2). Several bands not seen using the conventional mode could be observed in the polarized mode. (c) 2006 Elsevier B.V. All rights reserved