Furnace for in situ and simultaneous studies of nano-precipitates and phase transformations in steels by SANS and neutron diffraction

Interphase precipitation occurring during solid-state phase transformations in micro-alloyed steels is generally studied through transmission electron microscopy, atom probe tomography, and ex situ measurements of Small-Angle Neutron Scattering (SANS). The advantage of SANS over the other two characterization techniques is that SANS allows for the quantitative determination of size distribution, volume fraction, and number density of a statistically significant number of precipitates within the resulting matrix at room temperature. However, the performance of ex situ SANS measurements alone does not provide information regarding the probable correlation between interphase precipitation and phase transformations. This limitation makes it necessary to perform in situ and simultaneous studies on precipitation and phase transformations in order to gain an in-depth understanding of the nucleation and growth of precipitates in relation to the evolution of austenite decomposition at high temperatures. A furnace is, thus, designed and developed for such in situ studies in which SANS measurements can be simultaneously performed with neutron diffraction measurements during the application of high-temperature thermal treatments. The furnace is capable of carrying out thermal treatments involving fast heating and cooling as well as high operation temperatures (up to 1200 °C) for a long period of time with accurate temperature control in a protective atmosphere and in a magnetic field of up to 1.5 T. The characteristics of this furnace give the possibility of developing new research studies for better insight of the relationship between phase transformations and precipitation kinetics in steels and also in other types of materials containing nano-scale microstructural features.This work was financially supported equally by the Technology Foundation TTW, as part of the Netherlands Organization for Scientific Research (NWO), and Tata Steel Europe through the Grant No. 14307 under the Project No. S41.5.14548 in the framework of the Materials Innovation Institute (M2i) Partnership Program. The experiments performed at ISIS Neutron and Muon Source were supported by beam-time allocation from the Netherlands Organization for Scientific Research (NWO) through Project No. 721.012.102 (LARMOR) with Experiment No. RB1869024

On the Paris coefficient and crack closure effects of Alporas aluminum foam

Technische MateriaalwetenschappenMechanical, Maritime and Materials Engineerin

Bainite transformation of low carbon Mn-Si TRIP-assisted multiphase steels: influence of silicon content on cementite precipitation and austenite retention

Studies dealing with TRIP-assisted multiphase steels have emphasized the crucial role of the bainite transformation of silicon-rich intercritical austenite in the achievement of a good combination of strength and ductility. The present work deals with the bainite transformation in two steels differing in their silicon content. It is shown that both carbon enrichment of residual austenite and cementite precipitation influences the kinetics of the bainite transformation. A minimum silicon content is found to be necessary in order to prevent cementite precipitation from austenite during the formation of bainitic ferrite in such a way as to allow stabilisation of austenite by carbon enrichment. (C) 1999 Elsevier Science S.A. All rights reserved

Phase-transformation and precipitation kinetics in vanadium micro-alloyed steels by in-situ, simultaneous neutron diffraction and SANS

In-situ Neutron Diffraction and Small-Angle Neutron Scattering (SANS) are employed for the first time simultaneously in order to reveal the interaction between the austenite to ferrite phase transformation and the precipitation kinetics during isothermal annealing at 650 and at 700 °C in three steels with different vanadium (V) and carbon (C) concentrations. Austenite-to-ferrite phase transformation is observed in all three steels at both temperatures. The phase transformation is completed during a 10 h annealing treatment in all cases. The phase transformation is faster at 650 than at 700 °C for all alloys. Additions of vanadium and carbon to the steel composition cause a retardation of the phase transformation. The effect of each element is explained through its contribution to the Gibbs free energy dissipation. The austenite-to-ferrite phase transformation is found to initiate the vanadium carbide precipitation. Larger and fewer precipitates are detected at 700 than at 650 °C in all three steels, and a larger number density of precipitates is detected in the steel with higher concentrations of vanadium and carbon. After 10 h of annealing, the precipitated phase does not reach the equilibrium fraction as calculated by ThermoCalc. The external magnetic field applied during the experiments, necessary for the SANS measurements, causes a delay in the onset and time evolution of the austenite-to-ferrite phase transformation and consequently on the precipitation kinetics.Team Erik OffermanTeam Jilt SietsmaRST/Neutron and Positron Methods in MaterialsInstrumenten groe