Effect of Iignocellulosic Nanoparticles Extracted from Yerba Mate (Ilex paraguariensis) on the Structural, Thermal, Optical and Barrier Properties of Mechanically Recycled Poly(lactic acid)

In this work, yerba mate nanoparticles (YMNs) were extracted from Ilex paraguairiencis yerba mate wastes and further used to improve the overall performance of mechanically recycled PLA (PLAR). Recycled PLA was obtained by melt reprocessing PLA subjected to an accelerated ageing process, which involved photochemical, thermal and hydrothermal ageing steps, as well as a final demanding washing step. YMNs (1 and 3 wt. %) were added to the PLAR during the melt reprocessing step and further processed into films. The main goal of the development of PLAR-YMNs bionanocomposites was to increase the barrier properties of recycled PLA, while showing good overall performance for food packaging applications. Thus, optical, structural, thermal, mechanical and barrier properties were evaluated. The incorporation of YMNs led to transparent greenish PLAR-based films with an effective blockage of harmful UV radiation. From the backbone FTIR stretching region (bands at 955 and 920 cm−1), it seems that YMNs favor the formation of crystalline domains acting as nucleating agents for PLAR. The morphological investigations revealed the good dispersion of YMNs in PLAR when they are used in the lowest amount of 1 wt. %, leading to bionanocomposites with improved mechanical performance. Although the addition of high hydrophilic YMNs increased the water vapor transmission, the addition of 1 wt. % of YMNs enhanced the oxygen barrier performance of the produced bionanocomposite films. These results show that the synergistic revalorization of post-consumer PLA and nanoparticles obtained from agri-food waste is a potential way for the production of promising packaging materials that meet with the principles of the circular econom

Technical Evaluation of Mechanical Recycling of PLA 3D Printing Wastes

The importance of 3D printing is growing rapidly. A recent example of this increasing importance involves the fight against the Covid-19 pandemic, in which 3D printing has helped to overcome the shortage of critical supplies. However, 3D printing generates large amounts of plastic waste that could pose an environmental problem, thus making it necessary to find methods for the correct management of such wastes. The combination of additive manufacturing and distributed mechanical recycling can contribute to the development of a more circular economy. The main goals of this work were to characterize the poly(lactic acid) (PLA) wastes generated in 3D printing processes and evaluate the effect of their heterogeneity on the technical feasibility of mechanical recycling. Two PLA 3D printing wastes were used: waste coming from a well-known PLA grade, and a mixture of PLA 3D printing residues coming from an association of coronamakers in Madrid. Recycled material obtained from the waste of a well-known PLA grade shows good properties, similar to those for non-used material. However, the recycled material obtained from mixed PLA waste shows lower viscosity values, higher crystallization ability and less transparency. These results highlight that special attention should be paid to the sorting and characterization of the 3D wastes, to obtain recycled materials with good properties

Effect of Yerba Mate and Silk Fibroin Nanoparticles on the Migration Properties in Ethanolic Food Simulants and Composting Disintegrability of Recycled PLA Nanocomposites

The main objective of the present research is to study the effect of the incorporation of low amounts of silk fibroin nanoparticles (SFNs) and yerba mate nanoparticles (YMNs) on the migration phenomenon into ethanolic food simulants as well as on the disintegrability under composting conditions of mechanically recycled polylactic acid (PLA). Recycled PLA was obtained under simulated recycling conditions by melt processing virgin PLA into films and further subjecting them to an accelerated aging process, which involved photochemical, thermal, and hydrothermal aging steps followed by an intense washing step. SFNs were extracted from Bombyx mori cocoons and YMNs from yerba mate waste. Then, recycled PLA was melted, reprocessed, and reinforced with either 1%wt. of SFNs or YMNs, by melt extrusion, and further processed into films by compression molding. The obtained nanocomposites were exposed to ethanolic food simulants (ethanol 10% v/v, simulant A and ethanol 50% v/v, simulant D1) and the structural, thermal, and mechanical properties were studied before and after the exposure to the food simulants. The migration levels in both food simulants were below the overall migration limits required for food contact materials. The materials were disintegrated under simulated composting conditions at the laboratory scale level and it was observed that the nanoparticles delayed the disintegration rate of the recycled PLA matrix, but nanocomposites were fully disintegrated in less than one month