Measurements of temperature dependence of the electrical conductivity and thermopower along the chain and perpendicular-to-chain directions of the inorganic conductor (TaSe4)2I, exhibiting the charge density wave transition, are reported. The electrical conductivity and thermopower along the chain and perpendicular-to-the chain direction were measured for the first time on the same sample. Measurements in both directions enable obtaining an information on the predominant carriers along different crystallographic directions which may be different due to different energy gaps.Načinili smo mjerenja temperaturne ovisnosti električne vodljivosti i termostruje uzduž i poprečno na smjer lanaca neorganskog vodiča (TaSe4)2I koji pokazuje prijelaz na valove nabojne gustoće. Ovo su prva mjerenja električne vodljivosti i termostruje uzduž i poprečno na smjer lanaca na istom uzorku. Mjerenja u oba smjera omogućuju dobivanje podataka o nositeljima naboja duž dviju kristalografskih osi koji mogu biti uzrokovani različitim energijskim procjepima

Anizotropna termoelektrična svojstva (TaSe4)2I

Measurements of temperature dependence of the electrical conductivity and thermopower along the chain and perpendicular-to-chain directions of the inorganic conductor (TaSe4)2I, exhibiting the charge density wave transition, are reported. The electrical conductivity and thermopower along the chain and perpendicular-to-the chain direction were measured for the first time on the same sample. Measurements in both directions enable obtaining an information on the predominant carriers along different crystallographic directions which may be different due to different energy gaps.Načinili smo mjerenja temperaturne ovisnosti električne vodljivosti i termostruje uzduž i poprečno na smjer lanaca neorganskog vodiča (TaSe4)2I koji pokazuje prijelaz na valove nabojne gustoće. Ovo su prva mjerenja električne vodljivosti i termostruje uzduž i poprečno na smjer lanaca na istom uzorku. Mjerenja u oba smjera omogućuju dobivanje podataka o nositeljima naboja duž dviju kristalografskih osi koji mogu biti uzrokovani različitim energijskim procjepima