CuCoMgAlO_x Mixed Oxides as Selective Catalysts for the Hydrogenation of Furan Compounds

Single phase CuCoMgAl-layered hydroxides were obtained by making fine adjustment to their composition through changing the (Co + Cu)/Mg = 0.5; 1; 2; 3 and Co/Cu = 0.5; 1; 2 ratios. The rise of Co/Cu in systems contributed to the increase in their thermal stability. CuCoMgAl-catalysts showed high selectivity of carbonyl group hydrogenation in furfural and 5-hydroxymethylfurfural. In furfural hydrogenation, the selectivity to furfuryl alcohol was more than 99%, and in 5-hydroxymethylfurfural hydrogenation, the selectivity to 2,5-hydroxymethyl furfural was 95%. The surface of the samples with different Co/Cu after calcination and reduction was the same and had a «core-shell» structure (TEM). «Core» consisted of Cu and Co metallic particles. «Shell» consisted of CuCoMgAlOx mixed no-stoichiometric spinel oxides. There was no sintering or change in size of the metallic particles after the reaction. For the sample with Co/Cu = 1, their phase composition after reaction remained unchangeable. The increase of Co/Cu led to the formation of an X-ray amorphous phase after the reaction. This suggests the decrease in structural stability of this sample. The obtained results prove the prospects of using bimetallic CoCu-systems for hydrogenation of furan aldehydes, and opens up new directions for further research and improvement

Synthesis of CuAl-, CoAl-, and CuCoAl-Catalysts from Layered Hydroxides for Furfural Hydrogenation

Catalysts based on CuAl-, CoAl-, and CuCoAl-layered hydroxides with M2+/Al = 2 and Cu/Co = 1 molar ratio were obtained. The effect of amount of cobalt on the structural properties, morphology, surface cations distribution, oxide phase formation, thermal stability of the samples and reduction of metals from them was studied. The effect of reaction conditions (temperature, time, pressure, solvent) and conditions of preliminary treatment of catalysts on their catalytic properties in furfural hydrogenation was established. High selectivity to furfuryl alcohol was observed for all the samples irrespective of pretreatment and reaction conditions. The synergetic effect in furfural hydrogenation between Co and Cu in the CuCoAlOx catalysts was revealed when ethanol is used as a solvent