Variation de l'aimantation à saturation et de la résistance électrique d'alliages fer-nickel, sous l'effet d'une compression isotrope aux basses températures

The saturation magnetization and electrical resistance of binary Fe-Ni alloys, with 38 and 45 % Ni, were studied as a function of pressure. The pressure was created by freezing water in a beryllium bronze bomb. Measurements were made from 1,7 to 77 °K, in fields up to 7 000 oersteds. The limiting values of the saturation magnetization and the electrical resistance as T → 0 were shown to depend on the isotropic compression, the variations having opposite signs. In large applied fields the limiting values also vary with the field, and the differential susceptibility at saturation does not become zero as T → 0. The ratio between the relative variation of the saturation magnetization and the relative variation of the resistivity is nearly the same for both external parameters, pressure and field.Étude des variations de l'aimantation à saturation et de la résistance électrique des alliages binaires fer-nickel avec 38 et 45 % de nickel sous l'action d'une pression créée par congélation d'eau dans une bombe en bronze de béryllium. Les mesures sont effectuées dans un intervalle de températures allant de 1,7° à 77 °K et dans des champs jusqu'à 7 000 œrsteds. Les valeurs limites de l'aimantation à saturation et de la résistance électrique quand T tend vers 0 varient sous l'effet d'une compression isotrope, et les signes de ces variations sont opposées. Les valeurs limites indiquées varient également avec l'augmentation ou la diminution du champ dans les champs magnétiques élevés, et la susceptibilité magnétique différentielle dans le domaine d'aimantation à saturation ne s'annule pas quand T tend vers 0. Les rapports entre les variations des valeurs limites de l'aimantation à saturation et de la résistance électrique sous l'effet d'une pression et sous l'effet d'un champ sont voisins

Résultats de recherches sur certaines propriétés magnétiques et magnéto-optiques de matières ferromagnétiques

1. Low temperature measurements of the saturation magnetization of NiCu alloys are given and agree with the T3/2 law. The exchange integral is calculated. 2. The magnetic properties of the system Mn-B are investigated. The compound MnB is the ferromagnetic component in these alloys. 3. The results of measurements of the paramagnetic susceptibility of ferromagnetic materials at high temperature, up to 1 600 °C, are given. 4. Resonance effects in ferromagnetic substances in the infrared region have been observed. Some mechanisms are proposed.1. Les auteurs rendent compte des résultats de mesures aux basses températures de l'aimantation à saturation des alliages NiCu. La loi en T 3/2 est bien vérifiée et on en déduit la valeur de l'intégrale d'échange. 2. Les auteurs ont étudié les propriétés magnétiques des alliages du système Mn-B. Le porteur du ferromagnétisme est précisément la combinaison MnB. 3. Résultats de recherches sur la variation avec la température (jusqu'à 1 600 °K) de la susceptibilité paramagnétique des substances ferromagnétiques. 4. Dans les métaux ferromagnétiques, l'auteur a mis en évidence par voie optique et essaie d'interpréter des résonances qui se situent dans l'infra-rouge