17 research outputs found
A comparative study of the corrosion of high copper dental amalgams
Metallographic studies carried out for Tytin-Plus and Dispersalloy amalgams show a porous multiphase material, whose surface phases are: gamma-(Ag3Sn), gamma(1)-(Ag2Hg3), eta'-(Cu6Sn5) and epsilon-(Cu3Sn). Additionally, Dispersalloy is present in the Ag-Cu eutectic. The application of surface analysis by SEM reveal a heterogeneous distribution of the above mentioned phases. Microstructures consisting of colonies or clusters were not observed. The corrosion testing of these materials was done in 0.9% NaCl aerated solution at 25 degrees C using potentiodynamic polarization curves and ac impedance measurements. The corrosion process in these multiphase systems can be interpreted as the sum of more than one electrodissolution process and the posterior formation of corrosion films. on each electrode, the corrosion film is formed by different mechanisms. (C) 1998 Elsevier B.V. B.V. All rights reserved
Estudio de la pasivacion de la aleacion Co-Cr-Mo en suero fisiologico
Results are presented on the mechanism of passivation of Co-Cr-Mo biological implant alloys in physiological serum using open circuit potentiometry, potentiodynamic curves, and electrochemical impedance spectroscopy. The potential dependence of impedance data and the analysis of the parameters obtained indicate a progressive diminution of the initial layer thickness and the simultaneous formation of a second higher resistive layer. In more severe conditions than the existent in human body, the metallographic examination of the alloy surface shows localized corrosion in interdendritric regions. Elemental analysis of the surface reveals the presence of higher chromium content in these regions. The presence of chlorine was not detected, which suggested that during preferential attack, soluble species are also formed
Qualitative and quantitative characterization of aluminium alloys after corrosion testing
The 2024 and 7050 aluminium alloys used as aircraft components were subjected to laboratory corrosion tests in sodium chloride solution, Light-microscope examinations make it possible to characterise morphological aspects of the localised corrosion. Image analysis was used to determine both depth and width of pits over corroded surfaces. It has been concluded that the annealing could reduce the pit growth in both alloys, by means of grains recrystallization or recovery. The 2024 alloy also tends to present an exfoliation mechanism, mainly throughout non-recrystallized and recrystallized grain boundaries, increasing the width and sustaining the depth of pit cavities during exposition to saline atmosphere. SEM and EDS analysis reveal the morphology and elemental distribution of the corrosion products formed after immersion corrosion test. Some of these products were identified by X-ray diffraction analysis. For 2024, Al(OH)(3), MS(OH)(2) and Cu2O were found. AI(OH)(3) and Cu2O were also found in 7050 samples
A metallurgical study of aluminium alloys used as aircraft components
The effects of heat treatment on morphologies and microstructures of Al 2024 and Al 7050 alloys, used as aircraft components, were studied by metallographic techniques. Light microscopy (LM) and quantitative image analysis were used to characterize the precipitate dispersion and morphology for these alloys. The application of the scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) combined techniques for studying these multiphase systems makes it possible to distinguish and quantify the different phases in the surface structure. Xray diffraction also permitted a qualitative comparison of the structures before and after heat treatments
Morphological analysis of pits formed on Al 2024-T3 in chloride aqueous solution
It has been used a new image analysis method, based on segmentation by shape parameters, for pits morphology examination from Al 2024 aluminum-copper alloy in chloride aqueous solution. Corrosion behavior of this alloys in naturally aerated 3.5% NaCl solution has been investigated through open circuit potential measurements. Afterwards, pits have been characterized by image analysis taking density and size measurements right from corroded surfaces. Morphological investigation has been conducted for profiles, cut orthogonally from mean surface planes, and observed through light microscopy. Image analysis data could demonstrate that pits are wider than deep, evoluting for conical, quasi-conical or irregular shapes. Most pits have presented a quasi-conical morphology, but the wider ones have evoluted to an irregular shape influenced by sub-surface microstructure. Image analysis based on shape segmentation could enhance the differences on morphological behavior. (C) 2004 Elsevier B.V. All rights reserved
Corrosion of Ni-Cr-Mo alloys for fixed dental prostheses in an aqueous solution of 0.05% NaF and in commercial mouthwashes by means of EIS
Abstract: -Ni-Cr-Mo alloys have been used as dental prostheses due their properties such as good mechanical strength, high corrosion resistance and also because they are economically viable. The corrosion protection of these alloys in salt solutions which are typical of physiological media is due to the phenomenon called passivation with an oxide superficial layer formation, particularly chromium oxides. This protective film, subjected to mechanical stress in a corrosive environment, can be broken partially releasing ions that have deleterious effects in a human body. Fluoride ions, existent in hygiene products, change the oral environment and their presence may enable the beginning of a localized corrosion process. The objective of this work is to evaluate the corrosion resistance of three Ni-Cr-Mo alloys, of different compositions: SC (73% Ni, 14% Cr, 8.5% Mo, 1.8% Be, 1.8% Al) SB (61% Ni, 25% Cr, 10.5% Mo, 1.5% Si) and W (65% Ni, 22.5% Cr, 9.5% Mo, 1.0% Nb, 1.0% Si, 0.5% Fe) in media containing fluoride which simulate oral rinse solutions. This study has been performed in solution of 0.05% NaF, NaCl 0.05% and commercial mouthwashes on pH 6.0 at 37°C using metallography analyses, immersion techniques, and electrochemical tests, impedance tests and analysis. SC, with the highest nickel and the lowest chromium content, does not passivate in the studied means showing a continuous increase in current density due to increasing potential, while the other alloys exhibit passivation range of 600 mV and passive current density 10 -6 A/cm 2 . In general, considering the immersion and electrochemical corrosion tests, it is concluded that the worst performance has been attributed to the alloy SC, while W and SB have shown the best performance and very similar behaviors
Corrosion behavior of Ti-6Al-4V alloy treated by plasma immersion ion implantation process
Ti-6Al-4V alloy is one of the most frequently used Ti alloys with diverse applications in aerospace and biomedical areas due to its favorable mechanical properties, corrosion resistance and biocompatibility. Meanwhile, its surface can stiffer intense corrosion caused by wear processes due to its poor tribological properties. Thus in the present study, PIII processing of Ti-6Al-4V alloy was carried out to evaluate its corrosion resistance in 3.5% NaCl solution. Two different sets of Ti-6Al-4V samples were PIII treated, varying the plasma gases and the treatment time. The corrosion behavior is correlated with the surface morphology, and the nitrogen content. SEM micrographs of the untreated sample reveal a typical two-phase structure. PIII processing promotes surface sputtering and the surface morphology is completely different for samples treated with N-2/H-2 mixture and N-2 only. The highest penetration of nitrogen (similar to 88 nm), corresponding to 33% of N-2 was obtained for the sample treated with N-2/H-2 mixture for 1:30 h. The corrosion behavior of the samples was investigated by a potentiodynamic polarization method. A large passive region of the polarization curves (similar to 1.5 V), associated with the formation of a protective film, was observed for all samples. The passive current density (similar to 3 x 10(-6) A cm(-2)) of the PIII-treated Ti-6Al-4V samples is about 10 times higher than for the untreated sample. This current value is still rather low and maintains good corrosion resistance. The anodic branches of the polarization curves for all treated Ti-6Al-4V samples demonstrate also that the oxide films break down at approximately 1.6 V, forming an active region. Although the sample treated by N-2/H-2 mixture for 1.30 It has thicker nitrogen enriched layer, better corrosion resistance is obtained for the PIII process performed with N, gas only. (c) 2007 Elsevier B.V. All rights reserved
Influence of chromate, molybdate and tungstate on pit formation in chloride medium
It has been characterized and evaluated the 2024-T351 and 7050-T7451 aluminum alloys pitting corrosion in naturally aerated chloride aqueous solutions containing chromate, molybdate and tungstate. It has been carried out electrochemical and non-electrochemical immersion corrosion tests accompanied by surface metallography analysis using an optical microscopy. Chromate for the two alloys and in molybdate for 7050 has corrosion inhibiting effects, whereas tungstate promotes the pitting corrosion for these alloys. Quantitative surface analysis upon the alloys after immersion has indicated that pits are predominantly conical or quasi-conical and irregular. In general, pits have been wider than deep and the widest have been also the deepest. Despite inhibitor presence, when pits have been nucleated, they grow with the same intensity. © 2005 Elsevier B.V. All rights reserved
Caracterizacion metalografica de aleaciones metalicas utilizadas como biomateriales en implantes quirurgicos
In this work, the chemical structure, the microstructure and the surface morphology of two non-ferrous materials used in dental implants (Ti-6Al-4V and Co-Cr-Mo) were studied. This was done by chemical analysis, scanning electron microscopy (SEM), energy disperse spectroscopy (EDS), and strength measurements (HV). Metallographic studies reveal that titanium alloy surface present a fine granular binary phase structure, while cobalt alloy present cast dendrite structures with an intense precipitation of carbides. To correlate the macro and microstructure with the mechanical behavior of the material, microhardness measurements were performed. Using the Vickers hardening method, the Ti-6Al-4V alloy yielded strength mean values smaller than the Co-Cr-Mo alloy. Their values are associated to the chemical composition and to the microstructural distribution of these materials. The Ti-6Al-4V alloy presents hardness similar to dental enamel, which suggests better performance as dental implant