Charakterytyka stopu Al-Zn-In otrzymanego metodą przeciskania w kanale kątowym

Equal channel angular pressing (ECAP) is a technique that creates a high accumulated strain in metals and results in ultrafine-grained structure. In this study, Al-5Zn-0.02In was processed by ECAP at a room temperature using route Bc through an ECAP die (press angle of Φ = 100° and Ψ = 20°). The samples were subjected to ECAP with 1, 2, 3 and 4 passes. The processed specimens were characterized using electron backscatter diffraction (EBSD). The results confirmed the grain refinement of the alloy after ECAP to an average grain size less than 5 μm after 4-pass ECAP. The microhardness test shows that the hardness increased with the number of passes. The hardness of the cross-sectional area of the sample was similar to that tested along the pressing direction.Metoda przeciskania w kanale kątowym (ang. Equal channel angular pressing; ECAP) prowadzi do powstania bardzo wysokich naprężeń, w wyniku czego otrzymuje się ziarna o bardzo drobnej strukturze. W niniejszej pracy, stop Al-5Zn-0,02In wytwarzano metodą ECAP w temperaturze pokojowej, wykorzystując ścieżkę Bc przez matrycę ECAP (kąty krzywizny: Φ = 100° i Ψ = 20°). Próbki poddano ECAP z 1, 2, 3 i 4 przejściami. Otrzymane próbki badano metodą dyfrakcji elektronów wstecznie rozproszonych (ang. electron back scatter diffraction; EBSD). W stopie otrzymanym metodą ECAP z 4 przejściami, średnia wielkość ziaren wynosiła mniej niż 5 μm. Badania mikrotwardości wykazały, że twardość zwiększała się wraz z liczbą przejść. Twardość zmierzona w poprzek próbki byłą porównywalna do tej mierzonej wzdłuż osi nacisku