Bioremediation of mortar made from Ordinary Portland Cement degraded by Thiobacillus thioparus using Bacillus flexus

Cement is widely used as a construction material in the construction industry. However, there are challenges affecting its durability efficacy. Cement mortar/concrete is subject to degradation by aggressive ions such as sulphates and chlorides. Sulphates can be introduced into the concrete or mortar by Sulphur producing bacteria of the species Thiobacilli. Microbiologically induced CaCO3 precipitation (MICP) has found its application in bioremediating cement based materials. It has been found to be environmental friendly. However, no work has been reported on bioremediation of biodegraded cement based materials. This paper presents findings of possible bioremediation of mortars after undergoing biodegradation. Bacillus flexus, a beneficial bacterium was used. The control mortars were prepared using Ordinary Portland Cement (OPC). The test mortars were prepared and cured in a solution of Thiobacillus thioparus, a Sulphur oxidizing bacteria, deleterious bacterium for 14, 28, 56 and 90 days. Compressive strength analysis was conducted on the 14th, 28th, 56th and 90th day of curing. Results showed that the lowest compressive strength was recorded on the 90th day as 31.02 MPa. This was a 34.17 % loss in compressive strength. Another category of mortar cured in Thiobacillus thioparus for 28 days was bioremediated for 28 days using Bacillus flexus solution. Compressive strength and Scanning Electron Microscopy (SEM) analyses were then done. The results show a compressive strength of 45.83 MPa at the 56th day. This represents a 99.91 % strength recovery from biodeterioration. The SEM analysis results revealed a denser material. This was due to massive precipitation of calcium carbonate in the mortar matrix and pores/voids for bioremediated mortars as opposed to the biodegraded mortars. The results further revealed reduced ettringite crystals on the bioremediated mortars. Bacillus flexus could perhaps be used in restoring lost compressive strength as well as in sealing voids in degraded concrete in sewer lines and other cement based materials. This could improve on its efficacy with minimal repair

Biocementation Influence on Flexural Strength and Chloride Ingress by Lysinibacillus sphaericus and Bacillus megaterium in Mortar Structures

The concrete/mortar durability performance depends mainly on the environmental conditions, the microstructures, and its chemistry. Cement structures are subject to deterioration by the ingress of aggressive media. This study focused on the effects of Bacillus megaterium and Lysinibacillus sphaericus on flexural strength and chloride ingress in mortar prisms. Microbial solutions with a concentration of 1.0 × 107 cells/ml were mixed with ordinary Portland cement (OPC 42.5 N) to make mortar prisms at a water/cement ratio of 0.5. Four mortar categories were obtained from each bacterium based on mix and curing solution. Mortar prisms of 160 mm × 40 mm × 40 mm were used in this study. Flexural strength across all mortar categories was determined at the 14th, 28th, and 56th day of curing. Mortars prepared and cured using bacterial solution across all curing ages exhibited the highest flexural strength as well as the highest percent flexural strength gain. Lysinibacillus sphaericus mortars across all mortar categories showed higher flexural strength and percent flexural strength gain than Bacillus megaterium mortars. The highest percent flexural strength gain of 33.3% and 37.0% was exhibited by the 28th and 56th day of curing, respectively. The mortars were subjected to laboratory prepared 3.5% by mass of sodium chloride solution under the accelerated ion migration test method for thirty-six hours using a 12 V Direct Current power source after their 28th day of curing. After subjecting the mortar cubes to Cl media, their core powder was analyzed for Cl content. From these results, the apparent diffusion coefficient, Dapp, was approximated from solutions to Fick’s 2nd Law using the error function. Bacillus megaterium mortars across all mortar categories showed lower apparent diffusion coefficient values with the lowest being 2.6456 × 10–10 while the highest value for Lysinibacillus sphaericus mortars was 2.8005 × 10–10. Both of the test bacteria lowered the ordinary Portland cement Cl-ingress but Bacillus megaterium was significantly more effective than Lysinibacillus sphaericus in inhibition

Chloride Ingress in Cement Mortars Exposed to Acidithiobacillus thiooxidans Bacteria

Concrete structures placed in aggressive aqueous environments are vulnerable to degradation. Majority of studies have linked structural failures to the ingress of deleterious ions into the cement matrix. Some microbial activities may accelerate the penetration of harmful materials into the cement matrix and hence cause pronounced deterioration. This work reports a laboratory-simulated study carried out to determine the extent of chloride ingress in cement mortars exposed to Acidithiobacillus thiooxidans. Test prisms were cast from Portland pozzolana cement (PPC) and ordinary Portland cement (OPC) with water-to-cement ratio maintained at 0.5. Acidithiobacillus thiooxidans bacterial solution of concentration 1.0×107 cell/mL was used to prepare microbial mortar prisms, whereas distilled water was used to prepare the control mortar prisms. The test prisms were subjected to porosity and accelerated chloride ingress after 28th day of curing. Compressive strength was determined after the 2nd, 7th, 28th, and 56th days of curing. Apparent diffusion coefficients (Dapp) were estimated from the solutions to Fick’s second law of diffusion. After the 56th day of curing, the microbial-treated mortars exhibited a significant reduction in compressive strength. The resultant percentage decrease in compressive strength was 30.74% and 19.88% for OPC and PPC, respectively. Further, microbial-treated mortars demonstrated both high porosity and chloride ingress as compared to the control test mortars. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) analyses showed the formation of new deleterious products in the microbial-exposed mortars

Review of the Effect of Grinding Aids and Admixtures on the Performance of Cements

Grinding aids (GAs) are polar chemicals introduced in cement mills in either liquid or powder form to improve on mill grindability efficiency. Studies have shown that some GAs not only help in grinding efficiency but also play vital roles in improving the product particle size distribution, product ability to flow in the mill, grinding energy reduction, and improvement on the separator efficiency. This review investigated the impacts of the GAs on the performance of some properties of cement when used as either mortar and/or concrete. The influence of the GAs incorporation in cement grinding on properties such as workability and setting times of the placed concrete and/or mortar has been covered in this review. The performance of GAs on ordinary portland cement (OPC) and blended cements with other supplementary cementitious materials such as pozzolana, fly ash, and slag has also been discussed. This is in view to tapping the maximum benefits of using GAs in cement production and use. This review work established that GAs have a positive influence on mill performance when properly applied. It further established that blended cements work better when dosed with additives such as GAs and/or quality improvers when compared to OPC. The review work demonstrated that some superplasticizers help in lowering the water demand in highly blended pozzolanic-based cements. The review finally recommended that the future course of action in the production of blended cements should apply GAs. This is in order to help produce highly replaced blended cements that are sustainable