Influence of waxes remelting used in investment casting on their thermal properties and linear shrinkage

This paper presents the results of thermal properties and linear shrinkage of jewelry waxes utilized in investment casting. Three types of jewelry waxes were cyclically processed (by heating, holding in a molten state and cooling)in the temperature range between 25 and 90 °C for about 7 hours. The samples were tested after 5th, 10th and 15thcycle. The remelting was designed to simulate the process of waxes reusability for production of patterns. Changes in thermal properties of waxes were determined using differential scanning calorimetry (DSC) and linear shrinkage values were specified. The conducted examinations allowed to establish the way of multiple utilization of waxes in producing precise models

Manufacturing and characterization of sustainable and recyclable wood-polypropylene biocomposites:Multiprocessing-properties-structure relationships

In this study, sustainable polymeric materials with a polypropylene matrix reinforced with wood waste were developed for structural applications. The new polymer biocomposites (WPCs) were evaluated for their mechanical and structural properties regarding their susceptibility to multiple processing. As thermo-mechanical degradation processes are associated with the repeated processing of plastics, which causes changes in the properties and structure of these materials. Therefore, to determine the extent to which the composites can be used under operating conditions, the composites were examined by DMA. As a result of the study observed some effects caused by the repeated effects of shear stress and temperature on the rheological and mechanical properties of polymer composites. The first of these is related to a decrease in viscosity of WPC composites subjected to the six times processing and changes in flow conditions during extrusion and injection moulding due to the degradation of the polypropylene matrix. As the viscosity of the composites decreased, a reduction in tensile strength and other mechanical properties of the polypropylene matrix was noted. On the other hand, the second effect observed leads to the conclusion that, as the composites' processing cycles increase, the WPC composite's mechanical properties increase due to an increase in the degree of homogenization of the individual components of the WPC composition. This study aims to describe the relationship between these two primary processes and to determine the relationship between the properties and the structure of the new WPCs.</p

The influence of mechanical recycling on the deformation and structure of polyoxymethylene

W pracy przedstawiono wyniki badań wytrzymałościowych i strukturalnych polioksymetylenu (POM) poddanego wielokrotnemu przetwarzaniu. Zbadano wpływ recyklingu na właściwości mechaniczne i strukturę materiału. Określono następujące właściwości mechaniczne: moduł sprężystości wzdłużnej, naprężenie zrywające, wydłużenie przy zerwaniu. Zmiany strukturalne POM oceniono na podstawie badań mikroskopowych i różnicowej kalorymetrii skaningowej (DSC). Stwierdzono, że ze wzrostem cykli przetwarzania następuje obniżenie stopnia krystaliczności dla polimerów wtórnych (po 4-,6-krotnym przetwórstwie) na skutek procesów degradacji termo-mechanicznej.This work covers experimental research of polyoxymethylene (POM) after mechanical reprocessing. The influence of the recycling on mechanical properties and structure the of recycled materials was investigated. The following parameters were determined: Young's modulus at tensile, strength at break, elongation at break. Structural changes in these reprocessed materials were investigated by microscopy, differential scanning calorimetry (DSC).The results show the decrease of the degree of crystallinity with the increasing number (4-,6- of processing cycles) as the result of mechanical and thermal degradation of polyoxymethylene

Pulverization technology and properties of powder obtained from polyethylene waste

Oceniono proces pulweryzacji recyklatów polietylenowych przy użyciu pulweryzatora wyposażonego w młyn tarczowy i porównano z proszkiem pierwotnym stosowanym do odlewania rotacyjnego. Zbadano wpływ prędkości podawania materiału na wydajność procesu i jakość surowca. Największą efektywność procesu uzyskano dla najwyższej szybkości podawania surowca Stwierdzono, że pulweryzacja odpadów polietylenowych w temperaturze 50°C i przy szybkości podawania surowca odpowiadającej natężeniu prądu 97A zapewnia uzyskanie proszku o odpowiedniej jakości (gładkiej powierzchni ziarna proszku pozbawionej nitek) i średniej wielkości ziarna wynoszącej 0,4 mm. W wyniku pulweryzacji recyklatów otrzymano proszki polimerowe, które mogą być stosowane do formowania wyrobów za pomocą odlewania rotacyjnego.The evaluation of pulverization process of polyethylene recycles was performed using a pulverizer equipped with the disc mill. The re-powder was compared to the original powder used in rotational molding. The assessment of material dosing speed on the grinding efficiency and quality of powder as carried out. The highest efficiency of pulverization was obtained for the highest dosing speed of material. It was found that the pulverization of polyethylene waste at temperature of 50°C, material dosing rate referring to 97A of electric current, ensured the powder of required quality surface of powder particles without threads) and the average particle size of 0.4 mm. As a result, the pulverization of recycled enable one to obtain polymer powder that can be used in the rotation molding technology

Effect of process conditions on properties and structure of recycled polyethylene terephthalate (rPET)

W pracy oceniono wpływ parametrów technologicznych na właściwości przetwórcze i strukturę regranulatów z poli(tereftalanu etylenu) - PET. Zbadano wpływ temperatury i czasu suszenia na jakość regranulatów. Jako kryterium oceny jakości przyjęto wskaźnik szybkości płynięcia i lepkość istotną. Technikę DSC wykorzystano do oceny stopnia krystaliczności rPET. Stwierdzono, że najkorzystniejsze cechy (lepkość istotna równa 0,67 dl/g, stopień krystaliczności wynoszący ok. 27%) otrzymano podczas suszenia rPET w temperaturze 135°C w czasie 5 godzin.An influence of drying parameters on rheological properties and structure c polyethylene terephthalate regranulates produced by extrusion technology is presented in the paper. The assessment of drying temperature and time on regranulates quality was performed. As a criterion for assessing the rPE quality the melt flow index (MFI) and intrinsic viscosity of rPET were assumed. The DSC technique was used to evaluate the degree of rPET crystallinity. The drying temperature - 135°C and drying time - 5 hours turn out to be the optimal ones (intrinsic viscosity equal to 0.67 dl/g, crystallinity degree of ca. 27%)

Evaluation of possible usage of shredded waste of molding BMC

W pracy przedstawiono właściwości kompozytów PA6/BMC. Oznaczano: wskaźnik szybkości płynięcia (MFR), cechy wytrzymałościowe w próbie statycznego rozciągania, udamość oraz strukturę metodą dynamicznej analizy termomechanicznej (DMTA). Badania DMTA prowadzono w zakresie temperatur od -100°C do 200°C; wyznaczano temperaturę przejść relaksacyjnych oraz moduł zachowawczy poliamidu 6 i kompozytów. Stwierdzono, że wprowadzenie tłoczywa BMC do osnowy poliamidowej powoduje wzrost sztywności PA6. Ponadto stwierdzono, że wytrzymałość na rozciąganie, wydłużenie dla kompozytów PA6/BMC maleje wraz z zawartością napełniacza.The paper presents Reprocessing properties of polyamide 6/BMC are presented in the paper. The melt flow rate (MFR), strength properties in a static tensile test, tension, impact and dynamic mechanical thermal analysis (DMTA) were examined. The temperature of relaxation transitions and values of storage modulus (E’) of PA6 and its composites were determined using DMTA measurements in the temperature range between -100°C and 200°C. It can be stated that the introduction of molding BMC increased the stiffness of polyamide PA6 matrix. Moreover, the tensile strength and elongation of PA6/BMC composites decreased with the filler content

Processing effectiveness of cellular PVC shielding tubes

Proces wytłaczania porującego jest metodą przetwórstwa mającą na celu otrzymanie między innymi kształtowników, prętów, rur, powłok porowatych o zmniejszonej gęstości oraz pozbawionych zapadnięć na powierzchni wytłoczyny i wykazujących minimalny skurcz przy jednoczesnym zachowaniu zbliżonych właściwości wytworów wytłaczanych metodą konwencjonalną. W artykule przedstawiono specyfikę procesu wytłaczania porującego PVC. W badaniach procesu wytłaczania porującego zastosowano nowoczesne środki porujące chemicznie o endotermicznym oraz egzotermicznym procesie rozkładu, dozowane w ilości do 1,5% masowych w stosunku do masy tworzywa. Przeprowadzono obszerne badania efektywności procesu wytłaczania porującego obejmujące określenie wydajności procesu, zużycia energii podczas przetwórstwa, sprawności energetycznej wytłaczania porującego.Cellular extrusion is a method for manufacturing profiles, bars, low density cellular coatings and other cellular products that have no hollow cavities on the surface and show minimal processing shrinkage, while their properties are similar to those of products produced by conventional extrusion. The paper deals with cellular extrusion of PVC. The investigation of the process was conducted using state-of-the-art endothermic and exothermic blowing agents that were dosed in up to 1.5% by weight. The experiments involved measuring output, energy consumption and energy efficiency of the process

Composites of recycled polyolefin plastics filled with fly ash

W pracy zbadano wpływ zawartości napełniacza (popiołów lotnych) na właściwości mechaniczne kompozytów polimerowych sporządzonych na bazie odpadów polietylenu (rLDPE) i polipropylenu (PP). Kompozyty wykonano na wytłaczarce jednoślimakowej typu Brabender. Analiza zmian właściwości mechanicznych kompozytów dotyczyła takich cech jak: naprężenie zrywające, wydłużenie w chwili zerwania, moduł sprężystości przy rozciąganiu, udarność Charpy oraz twardość Shore 'a. Uzyskane wyniki badań wskazują, że wraz z zawartością napełniacza w kompozytach maleje wytrzymałość i odkształcenie, co należy tłumaczyć słabą adhezją międzyfazową pomiędzy cząstkami napełniacza, a matrycą polimerową oraz koncentracją naprężeń wokół cząstek napełniacza. Wyniki badań wskazują, istotne zwiększenie sztywności i twardości kompozytów poliolefiny/popioły lotne.An effect of filler (fly ash) on mechanical properties of composites made up of recycled low-density polyethylene (LDPE) and polypropylene were investigated in this study. The composites were prepared using a single extruder Brabender. Tensile strength, elongation at break, Youngs modulus, impact strength and Shore 's hardness were checked. It was found that fly ash decreased the tensile strength and elongation at break for these composites. The decrease can be explained by stress concentration initiating cracks around filler particles. This provides a direct evidence of poor interfacial adhesion between FA filler and polymer matrix. Young 's modulus and hardness of composites tended to increase with the incorporation of fly ash. Key words: fly ash, recycled polyethylene, plastics waste, composites, mechanical propertie

The processing and thermal properties of powder made from recycled polyethylene

W pracy przeprowadzono badania reologiczne i termiczne proszków z polietylenu (rPE) otrzymanych z odpadów technologią pulweryzacji. Na podstawie badań wyznaczono krzywe lepkości wtórnych proszków, które porównano z pierwotnym proszkiem, stosownym do odlewania rotacyjnego. Pomiary lepkości wykonano za pomocą reometru kapilarnego typu LCR 7000 Dynisco w zakresie szybkości ścinania 10-103 s-1, a pomiary MFR z zastosowaniem plastometru obciążnikowego, działającego na zasadzie stałego naprężenia stycznego. W wyniku przeprowadzonych badań zaobserwowano istotny wpływ parametrów procesu rozdrabniania na drodze pulweryzacji na cechy reologiczne przetwarzanych materiałów wtórnych. W zakresie niskich szybkości ścinania, stwierdzono obniżenie lepkości i wzrost wskaźnika szybkości płynięcia wtórnego proszku w stosunku do proszku pierwotnego. Analiza DSC wykazała, że proszki z wtórnego PE posiadają znacznie wyższą entalpię topnienia i stopień krystaliczności. Stwierdzono, że pulweryzacja wpływa korzystnie na właściwości otrzymanych proszków wtórnych.Rheological and calorimetric studies of recycled polyethylene powders obtained by pulverization were performed. On the basis of the studies, the viscosity and flow curves of the recycled powders were determined which were compared to the virgin powder suitable for rotary molding. Viscosity measurements were made using a LCR 7000 Dynisco capillary rheometer in terms of shear rate and MFR measurements, and with a load cell gravimeter operating on the principle of constant tangential stress. As a result of the research, the influence of the parameters of the pulverizing process on the rheological properties of recycled materials was observed. In the range of low shear rates, the decrease viscosity and an increase in the melt flow index were observed compared to the original powder. DSC analysis has shown that recycled powders have a significantly higher melting enthalpy and the degree of crystallinity

Influence of the multiplicity of processing on the flammability of polyamide 6

W pracy określono wpływ krotności przetwarzania na palność poliamidu 6 oraz wybrane właściwości mechaniczne. Badaniom poddano granulaty oraz kształtki wtryskowe z polimerów pierwotnych oraz po 1-krotnym, 2-krotnym, 3-krotnym oraz 4-krotnym recyklingu. Właściwości mechaniczne PA 6 określono w próbie statycznego rozciągania. Palność próbek oceniono na podstawie testu UL94 oraz indeksu tlenowego OI. Stwierdzono, że na właściwości termiczne i krotność ich przetwarzania wpływa rodzaj użytego antypirenu.In work defined impact times the processing on the flammability of polyamide 6 and mechanical properties. Research has been the primary polymer injection moulded parts and granules and 1 x, 2 x, 3 x and 4 x. The mechanical properties of PA 6 specified in the static stretching. Flammability samples was assessed on the basis of the test and the oxygen index UL94 OI. It was found that the thermal properties and times the processing affects the type of used antypiren