Cholinesterase inhibitors in Alzheimer disease therapy

In recent years, a progressive increase in age-related disorders could be observed in most western countries, among which Alzheimer’s disease (AD) is one of the most challenging. The progress of AD is characterized by a severe loss in memory and cognition, leading to behavioral changing, depression and death. Currently approved treatments, including the acetylcholinesterase inhibitors (AChEIs) donepezil, galantamine and rivastigmine and N-methyl-d-aspartate (NMDA) antagonist memantine, do not halt the progression of the disease. The discovering of multifunctional compounds considering that several dual binding site AChEIs were able to reach different targets, guided the development of new drug design strategy, the multi-target-directed ligand (MTDL) approach. This review shows briefly summaries past and present research on the cholinesterase inhibitors (ChIs) able to interact with other targets contributing in aetiology of Alzheimer’s disease

Modified method for determination of ParisErdogen relatIonship for mode I cyclic Delamination of carbon-epoxy laminate

W związku z brakiem ogólnie przyjętej standardowej procedury wyznaczania odporności na rozwarstwienia laminatów ze spoiwem polimerowym, w pracy do tego celu adaptowano normę ASTM E647. Dla uniknięcia konieczności bezpośredniego monitorowania rozwoju rozwarstwienia zaproponowano modyfikację wymagań tej normy, polegające na wyznaczaniu długości rozwarstwienia na podstawie zmian podatności próbki. Wyniki wskazują, iż jest to możliwe, jednak w celu podwyższenia ich wiarygodności konieczne jest wykonanie interlaboratoryjnych badań na obszerniejszej partii próbek, wykonanych ze zróżnicowanych materiałów.Designed for metals ASTM E647 standard test procedure was adapted for determination of Paris-Erdogen relationship for carbon-epoxy laminate. To eliminate the need for continuous monitoring of delamination growth during the test the new procedure was applied that takes advantage of compliance changes resulting from delamination growth. The test results indicate that such a procedure is promising one however additional interlaboratory test should be carried out with the use of larger number of specimens made of various laminates to enhance reliability of the procedure

Resistance of carbon-epoxy laminatete against mode I cyclic delamination

Przeprowadzone badania dotyczą odporności laminatu węglowo-epoksydowego o wzmocnieniu z jednokierunkowej z taśmy KDU1007 wykonywanego techniką "na mokro" na propagacje rozwarstwień w warunkach obciążeń cyklicznych, w warunkach I sposobu pękania, dla R = 0.5 i G max= 0.9 Gc . Z badań otrzymano następujące wyniki: wartości progowa i krytyczna współczynnika uwalniania energii wynoszą odpowiednio 0.145 i 0.275 N/mmm natomiast równanie Parisa przyjmuje postać da/dn = 10 6.404 G 15.977. Wyniki te są rezultatem przyjęcia do obliczeń obserwowanej długości rozwarstwienia a vis. Uzupełniono je o analogiczne wyniki uzyskane przez przyjęcie do obliczeń długości rozwarstwienia wynikającej ze zmian podatności próbki. Są to Gth = 0.15 N/mm, Gc = 0.275 n/mm i zależność da/ dn = 10 7.475 G 17.553.Carbon-epoxy laminate reinforced with KO111007 UD carbon fabric was tested to determine the laminate resistance against Mode I delamination due to cyclic loading. The laminate was made with the use of hand wet lay-up method. The tests ware carried out under displacement controlled conditions for R = 0.5 and G max = 0.9 G1c. The following results were obtained: Gth = 145 N/mm, GIc = 0.275 N/mm, and Paris low of the form da/dn = 10 6.404G 15.977 for visual assessment of the delamination extension, and G th = 0.15 N/mm , Gc =0.275 N/mm and Paris low of the form da/dn = 10 7.475 G 17.553 for compliance changes based assessment of delamination extension