Porous activated carbon materials from Triphala seed stones for high-performance supercapacitor applications

Porous activated carbon materials derived from biomass could be the suitable materials for high-rate performance electrochemical supercapacitors as it exhibits high surface area due to well-defined pore structure. Here, we report the novel porous activated carbon from Triphala seed stones by chemical activation with zinc chloride at different carbonization temperature (400-700 °C) under the nitrogen gas atmosphere. The activated carbon was characterized by Fourier transform-infrared (FTIR) spectroscopy, Raman scattering and scanning electron microscopy (SEM). Nitrogen adsorption-desorption measurements was used to study the surface properties (effective surface areas, pore volumes and pore size distributions). The electrochemical measurements were performed in an aqueous 1 M sulphuric acid (H2SO4) solution in a three-electrode cell set up. Triphala seed stones-derived porous carbon materials with well-defined micro- and mesopores exhibit high specific surface area ranges from 878.7 to 1233.3 m2 g-1 and total pore volume ranges from 0.439 to 0.626 cm3 g-1. The specific capacitance obtained by electrochemical measurement experiment was 208.7 F g-1 at 1 A g-1. These results indicate that the prepared nanoporous activated carbon material from Triphala seed stones would have significant possibility as supercapacitor electrode material for high-energy-storage supercapacitor applications

<i>Phyllanthus emblica</i> Seed-Derived Hierarchically Porous Carbon Materials for High-Performance Supercapacitor Applications

The electrical double-layer supercapacitance performance of the nanoporous carbons prepared from the Phyllanthus emblica (Amala) seed by chemical activation using the potassium hydroxide (KOH) activator is reported. KOH activation was carried out at different temperatures (700–1000 °C) under nitrogen gas atmosphere, and in a three-electrode cell set-up the electrochemical measurements were performed in an aqueous 1 M sulfuric acid (H2SO4) solution. Because of the hierarchical pore structures with well-defined micro- and mesopores, Phyllanthus emblica seed-derived carbon materials exhibit high specific surface areas in the range of 1360 to 1946 m2 g−1, and the total pore volumes range from 0.664 to 1.328 cm3 g−1. The sample with the best surface area performed admirably as the supercapacitor electrode-material, achieving a high specific capacitance of 272 F g−1 at 1 A g−1. Furthermore, it sustained 60% capacitance at a high current density of 50 A g−1, followed by a remarkably long cycle-life of 98% after 10,000 subsequent charging/discharging cycles, demonstrating the electrode’s excellent rate-capability. These results show that the Phyllanthus emblica seed would have significant possibilities as a sustainable carbon-source for the preparing high-surface-area activated-carbons desired in high-energy-storage supercapacitors