Vacancy-Driven Gelation Using Defect-Rich Nanoassemblies of 2D Transition Metal Dichalcogenides and Polymeric Binder for Biomedical Applications

A new approach of vacancy-driven gelation to obtain chemically crosslinked hydrogels from defect-rich 2D molybdenum disulfide (MoS2) nanoassemblies and polymeric binder is reported. This approach utilizes the planar and edge atomic defects available on the surface of the 2D MoS2 nanoassemblies to form mechanically resilient and elastomeric nanocomposite hydrogels. The atomic defects present on the lattice plane of 2D MoS2 nanoassemblies are due to atomic vacancies and can act as an active center for vacancy-driven gelation with a thiol-activated terminal such as four-arm poly(ethylene glycol)-thiol (PEG-SH) via chemisorption. By modulating the number of vacancies on the 2D MoS2 nanoassemblies, the physical and chemical properties of the hydrogel network can be controlled. This vacancy-driven gelation process does not require external stimuli such as UV exposure, chemical initiator, or thermal agitation for crosslinking and thus provides a nontoxic and facile approach to encapsulate cells and proteins. 2D MoS2 nanoassemblies are cytocompatible, and encapsulated cells in the nanocomposite hydrogels show high viability. Overall, the nanoengineered hydrogel obtained from vacancy-driven gelation is mechanically resilient and can be used for a range of biomedical applications including tissue engineering, regenerative medicine, and cell and therapeutic delivery

Nanocomposite clay-based bioinks for skeletal tissue engineering

Biofabrication is revolutionizing substitute tissue manufacturing. Skeletal stem cells (SSCs) can be blended with hydrogel biomaterials and printed to form three-dimensional structures that can closely mimic tissues of interest. Our bioink formulation takes into account the potential for cell printing including a bioink nanocomposite that contains low fraction polymeric content to facilitate cell encapsulation and survival, while preserving hydrogel integrity and mechanical properties following extrusion. Clay inclusion to the nanocomposite strengthens the alginate-methylcellulose network providing a biopaste with unique shear-thinning properties that can be easily prepared under sterile conditions. SSCs can be mixed with the clay-based paste, and the resulting bioink can be printed in 3D structures ready for implantation. In this chapter, we provide the methodology for preparation, encapsulation, and printing of SSCs in a unique clay-based bioink