42 research outputs found
Magnetic enhancement of CoZnFeO spinel oxide by mechanical milling
We report the magnetic properties of mechanically milled
CoZnFeO spinel oxide. After 24 hours milling of the
bulk sample, the XRD spectra show nanostructure with average particle size
20 nm. The as milled sample shows an enhancement in magnetization and
ordering temperature compared to the bulk sample. If the as milled sample is
annealed at different temperatures for the same duration, recrystallization
process occurs and approaches to the bulk structure on increasing the annealing
temperatures. The magnetization of the annealed samples first increases and
then decreases. At higher annealing temperature ( 1000C) the system
shows two coexisting magnetic phases {\it i.e.}, spin glass state and
ferrimagnetic state, similar to the as prepared bulk sample. The room
temperature M\"{o}ssbauer spectra of the as milled sample, annealed at
300C for different durations (upto 575 hours), suggest that the observed
change in magnetic behaviour is strongly related with cations redistribution
between tetrahedral (A) and octahedral (O) sites in the spinel structure. Apart
from the cation redistribution, we suggest that the enhancement of
magnetization and ordering temperature is related with the reduction of B site
spin canting and increase of strain induced anisotropic energy during
mechanical milling.Comment: 14 pages LaTeX, 10 ps figure
Análisis de perfiles de difracción de rayos X de una aleación Cu-8% en peso de Cr obtenida por medio de aleado mecánico
Grain Size, Misorientation, and Texture Evolution of Copper Processed by Equal Channel Angular Extrusion and the Validity of the Hall–Petch Relationship
Evaluation of dielectric and piezoelectric behavior of unpoled and poled barium titanate polycrystals with oxygen vacancies using phase field method
Experimental determination of the parameters for abnormal grain growth in the aluminum alloy AA5252
International audienc