Importance of the surface exchange kinetics as rate limiting step in oxygen permeation through mixed-conducting oxides

Attention is drawn to the possible involvement of the surface exchange kinetics in limiting the rate of oxygen permeation through mixed-conducting oxide ceramics. A theoretical approach is provided with which it is possible to distinguish between surface exchange- and bulk diffusion controlled kinetics of oxygen permeation. New results on the oxygen permeability of perovskites La0.8Sr0.2CoO3−σ and SrCo0.8Fe0.2O3−σ are presented. The importance of the exchange reaction re to diffusion in limiting overall oxygen transport through (La,Sr)(Co,Fe)O3−σ perovskite-type oxides is emphasized.\u

Oxidative coupling of methane in a mixed-conducting perovskite membrane reactor

Ionic-electronic mixed-conducting perovskite-type oxide La0.6Sr0.4Co0.8Fe0.2O3 was applied as a dense membrane for oxygen supply in a reactor for methane coupling. The oxygen permeation properties were studied in the pO2-range of 10¿3¿1 bar at 1073¿1273 K, using helium as a sweeping gas at the permeate side of the membrane. The oxygen semi-permeability has a value close to 1 mmol m¿2 s¿1 at 1173 K with a corresponding activation energy of 130¿140 kJ/mol. The oxygen flux is limited by a surface process at the permeate side of the membrane. It was found that the oxygen flux is only slightly enhanced if methane is admixed with helium. Methane is converted to ethane and ethene with selectivities up to 70%, albeit that conversions are low, typically 1¿3% at 1073¿1173 K. When oxygen was admixed with methane rather than supplied through the membrane, selectivities obtained were found to be in the range 30¿35%. Segregation of strontium was found at both sides of the membrane, being seriously affected by the presence of an oxygen pressure gradient across it. The importance of a surface limited oxygen flux for application of perovskite membranes for methane coupling is emphasized

Oxygen permeation through oxygen ion oxide-noble metal dual phase composites

Oxygen permeation behaviour of three composites, yttria-stabilized zirconia-palladium, erbia-stabilized bismuth oxidenoble metal (silver, gold) was studied. Oxygen permeation measurements were performed under controlled oxygen pressure gradients at elevated temperatures. Air was supplied at one side of a dense sintered disk specimen, while helium was fed at the opposite side to sweep away the permeated oxygen. This research has demonstrated that in addition to the presence of percolative metal phase in the oxide matrix, a large ionic conductivity of the oxide phase and a high catalytic activity of the metal phase towards surface oxygen exchange are required for the dual phase composite to possess high oxygen permeability. The bismuth oxide-silver composite fulfils these requirements, hence showing the best oxygen permeability

Preparation of gas-tight strontium-doped lanthanum cobaltate by an aqueous sol-gel process

Gas-tight dense membranes of highly Sr-doped LaCoO3 (such as the composition La0.3Sr0.7CoO3 chosen in this study) are difficult to prepare using usual synthesis processes. This report presents an aqueous sol-gel route using metal acetates as precursors to achieve this goal. Hydrogen peroxide and ammonia are added to the acetates precursor solution to obtain stable sol and xerogel, as well as a homogeneous powder after heat treatment. Thermal analysis and XRD show the presence of SrCO3 and La2O3 when the heat treatment temperature of the xerogel is lower than 950 °C. Single phase of cubic perovskite La0.3Sr0.7CoO3 can be obtained after treatment at above 1000 °C. Sintering the cold pressed green compact at above 1100 °C may result in gas-tight samples. It is found that the sintering temperature has a minor influence on the oxygen permeability of a gas-tight membrane

Oxygen semi-permeability of erbia-stabilized bismuth oxide

The isothermal permeability of oxygen through sintered dense disks of bismuth oxide stabilized with 25 mol% erbia (BE25) has been studied at 610–810°C and oxygen pressures of 0.0001–1 atm. It is concluded that the permeating flux is rate limited both by solid state diffusion of electron holes and by the surface exchange reaction. From the results the p-type electronic conductivity of BE25 and the surface oxygen exchange rate have been evaluated. The value obtained for the latter shows excellent agreement with that obtained from 18O-16O isotope exchange reported previously. Using gold point electrodes it is demonstrated that the oxygen semipermeability flux in case of partial rate control by surface oxygen exchange leads to deviations from Nernst behaviour, though oxygen permeation measurements reveal that under the applied conditions BE25 remains a solid electrolyte with an ionic transference number close to unity.\u

Influence of order-disorder transitions on oxygen permeability through selected nonstoichiometric perovskite-type oxides

New results on the oxygen permeability of perovskite-type oxides SrCo0.8B'0.2O3¿¿ (with B'=Cr, Fe, Co and Cu) and La0.6Sr0.4CoO3¿¿ are presented. The occurrence of order-disorder transitions at elevated temperatures (790¿940°C) in these phases has been confirmed by DSC measurements and, in some cases, by X-ray powder diffraction of samples either slowly cooled or quenched from high temperature after annealing in different atmospheres. The oxygen permeability found upon exposing opposite sides of sealed disc specimens to a stream of air and of helium, respectively, increases sharply (between 5¿6 orders of magnitude up to 0.3¿3×10¿7 mol cm¿2s¿1) at the onset of the transition from a low-temperature vacancy-ordered state to defec t perovskite, except for SrCo0.8Fe0.2O3¿¿. In the latter case only a slight anomaly is found in the Arrhenius plot of th e oxygen permeability at 790°C. The comparatively high oxygen flux through SrCo0.8Fe0.2O3¿¿ observed at intermediate tempe ratures is interpreted in terms of a two-phase mixture of a vacancy-ordered state and disordered perovskite, while above 790°C the sample is single-phase of defect perovskite structure

Quantum dynamics of a qubit coupled with structured bath

The dynamics of an unbiased spin-boson model with Lorentzian spectral density is investigated theoretically in terms of the perturbation theory based on a unitary transformation. The non-equilibrium correlation function $P(t)$ and susceptibility $\chi^{\prime\prime}(\omega)$ are calculated for both the off-resonance case $\Delta\lesssim 0.5\Omega$ and the on-resonance case $\Delta\sim \Omega$. The approach is checked by the Shiba's relation and the sum rule. Besides, the coherent-incoherent transition point $\alpha_c$ can be determined, which has not been demonstrated for the structured bath by previous authors up to our knowledge.Comment: 25 pages, 11 figure

Entanglement Purification through Zeno-like Measurements

We present a novel method to purify quantum states, i.e. purification through Zeno-like measurements, and show an application to entanglement purification.Comment: 5 pages, 1 figure; Contribution to the Proceedings of "Mysteries, Puzzles and Paradoxes in Quantum Mechanics", Gargnano, Italy, 2003 (to be published in J. Mod. Opt.