Utilising DualEELS to probe the nanoscale mechanisms of the corrosion of Zircaloy-4 in 350 °C pressurised water

Characterisation of materials utilised for fuel cladding in nuclear reactors prior to service is integral in order to understand corrosion mechanisms which would take place in reactor. Zircaloy-4 is one such material of choice for nuclear fuel containment in Pressurised Water Reactors (PWRs). In particular, the metal-oxide interface has been a predominant focus of previous research, however, due to the complex oxidation process of zirconium cladding, there is still no clear understanding of what is present at the interface. Using Scanning Transmission Electron Microscopy (STEM) and Dual Electron Energy Loss Spectroscopy (DualEELS), we have studied the corrosion of this material under conditions similar to those that could be encountered in service. It is shown that under all conditions, whether during faster oxidation in the early stages, slow growth just prior to the transition to a new growth regime, or in the faster growth that happens after this transition, the surface of the metal below the scale is loaded with oxygen up to around 33 at%. Approaching transition, in conditions of slow growth and slow oxygen supply, an additional metastable suboxide is apparent with a thickness of tens of nm. By studying changes in both chemical composition and dielectric function of the material at the oxide scale – metal interface with nanometre resolution, quantitative mapping could be achieved, clearly showing that this is a suboxide composition of ZrO and a Zr oxidation state close to +2

EELS at very high energy losses

Electron energy-loss spectroscopy (EELS) has been investigated in the range from 2 to >10 keV using an optimized optical coupling of the microscope to the spectrometer to improve the high loss performance in EELS. It is found that excellent quality data can now be acquired up until about 5 keV, suitable for both energy loss near edge structure (ELNES) studies of oxidation and local chemistry, and potentially useful for extended energy loss fine structure (EXELFS) studies of local atomic ordering. Examples studied included oxidation in Zr, Mo and Sn, and the ELNES and EXELFS of the Ti-K edge. It is also shown that good quality electron energy-loss spectroscopy can even be performed for losses above 9.2 keV, the energy loss at which the collection angle becomes ‘infinite’, and this is demonstrated using the tungsten L3 edge at about 10.2 keV