Comparative indoor and outdoor stability measurements of polymer based solar cells

We report comparative indoor and outdoor stability testing of organic solar cells based on a blend between a donor-acceptor polyfluorene copolymer and a fullerene derivative. The outdoor testing was conducted for a period over 12,000 hours in Sheffield, England, with a Ts80 lifetime determined in excess of 10,000 hours (420 days). Indoor lifetime testing was performed on solar cells using a solar simulator under a constant irradiance of 1000 W/m(2) for more than 650 hours. We show that under the conditions explored here, device degradation under the two sets of conditions is approximately dependent on the absorbed optical energy dose

Not Available

Not AvailableNot AvailableNot Availabl

PCDTBT based solar cells: one year of operation under real-world conditions.

We present measurements of the outdoor stability of PCDTBT:PC71BM based bulk heterojunction organic solar cells for over the course of a year. We find that the devices undergo a burn-in process lasting 450 hours followed by a TS80 lifetime of up to 6200 hours. We conclude that in the most stable devices, the observed TS80 lifetime is limited by thermally-induced stress between the device layers, as well as materials degradation as a result of edge-ingress of water or moisture through the encapsulation

The first demonstration of entirely roll-to-roll fabricated perovskite solar cell modules under ambient room conditions

The rapid development of organic-inorganic hybrid perovskite solar cells has resulted in laboratory-scale devices having power conversion efficiencies that are competitive with commercialised technologies. However, hybrid perovskite solar cells are yet to make an impact beyond the research community, with translation to large-area devices fabricated by industry-relevant manufacturing methods remaining a critical challenge. Here we report the first demonstration of hybrid perovskite solar cell modules, comprising serially-interconnected cells, produced entirely using industrial roll-to-roll printing tools under ambient room conditions. As part of this development, costly vacuum-deposited metal electrodes are replaced with printed carbon electrodes. A high-throughput experiment involving the analysis of batches of 1,600 cells produced using 20 parameter combinations enabled rapid optimisation over a large parameter space. The optimised roll-to-roll fabricated hybrid perovskite solar cells show power conversion efficiencies of up to 15.5% for individual small-area cells and 11.0% for serially-interconnected cells in large-area modules. Based on the devices produced in this work, a cost of ~0.7 USD W-1 is predicted for a production rate of 1,000,000 m² per year in Australia, with potential for further significant cost reductions.ARENA grant: 2017/RND01