Reactive SPS of Al2O3–RE:YAG (RE = Ce; Ce+Gd) composite ceramic phosphors

Ultrafine-grained Al2O3–rare earth:yttrium aluminium garnet (Al2O3–RE:YAG) (RE = Ce; Ce+Gd) composite ceramics were obtained for the first time by reactive spark plasma sintering (SPS) using commercially available initial oxide powders. The effect of key sintering parameters (temperature, dwell time, and external pressure (Pload)) on densification peculiarities, structural-phase states, and luminescent properties of composites was studied comprehensively. Differences in phase formation and densification between Ce-doped and Ce,Gd-codoped systems were shown. Parameters of reactive SPS, at which there is partial melting with the formation of near-eutectic zones of the Al2O3–YAG system/coexistence of several variations of the YAG-type phase, were established. Pure corundum–garnet biphasic ceramics with an optimal balance between microstructural and luminescence performance were synthesized at 1425 ℃/30 min/30–60 MPa. The external quantum efficiency (EQE) of the phosphor converters reached 80.7% and 72% with close lifetime of ~63.8 ns, similar to those of commercial Ce:YAG materials, which is promising for further applications in the field of high-power white light-emitting diodes (WLEDs) and laser diodes (LDs)

Spark Plasma Sintering of WC-Based 10wt%Co Hard Alloy: A Study of Sintering Kinetics and Solid-Phase Processes

The paper describes the method for producing WC-10wt%Co hard alloy with 99.6% of the theoretical density and a Vickers hardness of ~1400 HV 0.5. Experimental data on densification dynamics, phase composition, morphology, mechanical properties, and grain size distribution of WC-10%wtCo using spark plasma sintering (SPS) within the range of 1000–1200 °C are presented. The high quality of the product is provided by the advanced method of high-speed powder mixture SPS-consolidation at achieving a high degree of densification with minimal calculated grain growth at 1200 °C