Achievement of Room Temperature Superelasticity in Ti-Mo-Al Alloy System via Manipulation of ω Phase Stability

The achievement of room-temperature (RT) superelasticity in a Ti-Mo-Al ternary alloy system through the addition of a relatively high concentration of Al to manipulate the phase stability of the ω phase is realized in this study. The composition of the Ti-6 mol% Mo (Ti-11.34 mass% Mo) alloy was designated as the starting alloy, while 5 mol% Al (=2.71 mass% Al) and 10 mol% Al (=5.54 mass% Al) were introduced to promote their superelastic behavior. Among the alloys, Ti-6 mol% Mo-10 mol% Al alloy, which was investigated for the very first time in this work, performed the best in terms of superelasticity. On the other hand, Ti-6 mol% Mo and Ti-6 mol% Mo-5 mol% Al alloys exhibited a shape memory effect upon heating. It is worth mentioning that in the transmission electron microscopy observation, ω phase, which appeared along with β-parent phase, was significantly suppressed as Al concentration was elevated up to 10 mol%. Therefore, the conventional difficulties of the inhibited RT superelasticity were successfully revealed by regulating the number density of the ω phase below a threshold

Investigations of Effects of Intermetallic Compound on the Mechanical Properties and Shape Memory Effect of Ti–Au–Ta Biomaterials

Owing to the world population aging, biomedical materials, such as shape memory alloys (SMAs) have attracted much attention. The biocompatible Ti–Au–Ta SMAs, which also possess high X–ray contrast for the applications like guidewire utilized in surgery, were studied in this work. The alloys were successfully prepared by physical metallurgy techniques and the phase constituents, microstructures, chemical compositions, shape memory effect (SME), and superelasticity (SE) of the Ti–Au–Ta SMAs were also examined. The functionalities, such as SME, were revealed by the introduction of the third element Ta; in addition, obvious improvements of the alloy performances of the ternary Ti–Au–Ta alloys were confirmed while compared with that of the binary Ti–Au alloy. The Ti3Au intermetallic compound was both found crystallographically and metallographically in the Ti–4 at.% Au–30 at.% Ta alloy. The strength of the alloy was promoted by the precipitates of the Ti3Au intermetallic compound. The effects of the Ti3Au precipitates on the mechanical properties, SME, and SE were also investigated in this work. Slight shape recovery was found in the Ti–4 at.% Au–20 at.% Ta alloy during unloading of an externally applied stress