The Influence of Aging in Solvents on Dental Cements Hardness and Diametral Tensile Strength

Prosthetic materials must exhibit adequate resistance to the oral environment. The aim of this paper was to study the resistance of selected cements used for cementing restorations (Breeze—composite, Adhesor Carbofine—zinc-polycarboxylate and IHDENT–Giz type II—glass-ionomer) against ethanol, soda and green tea solutions. The highest values of hardness and DTS (diametral tensile strength) were obtained by composite cement (HV = 15–31, DTS = 34–45 MPa). Ethanol solution had the greatest impact on the hardness value of composite cement, and soda solution on zinc-polycarboxylate cement. No significant differences were noted in the DTS values of composite cements after immersion in solvents; however, the DTS value of zinc-polycarboxylate cement increased after prolonged immersion time in ethanol and the DTS of glass-ionomer cement (IHDENT Giz type II) clearly decreased after submersion in soda solutions. Variation in pH across the range of 6 (tea) to 9 (soda solution) had a low impact on the properties of dental cements. Extended exposure to solvents appears to worsen the properties of cements

The Influence of Low-Molecular-Weight Monomers (TEGDMA, HDDMA, HEMA) on the Properties of Selected Matrices and Composites Based on Bis-GMA and UDMA

Bisphenol A-glycidyl methacrylate (bis-GMA) and urethane dimethacrylate (UDMA) are usually combined with low-viscosity monomers to obtain more desirable viscosity, handling characteristics and general properties. The present study determined the flexural strength (FS), flexural modulus (FM), diametral tensile strength (DTS), and hardness (HV) of five matrices and composites based on these resins. The polymerization shrinkage stress (PSS) was also studied for the composites. The polymer matrices were formed using bis-GMA and UDMA. TEGDMA, HEMA and HDDMA acted as co-monomers. The composites had 45 wt.% of filler content. The highest FS and FM were obtained from the UDMA/bis-GMA/TEGDMA/HEMA matrix and the composite (matrix + filler). The best DTS values were obtained from the UDMA/bis-GMA/HEMA matrix and the composite. One of the lowest values of FS, FM, and DTS was obtained from the UDMA/bis-GMA/HDDMA matrix and the composite. All the composites demonstrated similar hardness values. The lowest polymerization shrinkage stress was observed for the UDMA/bis-GMA/TEGDMA/HEMA composite, and the highest PSS was observed for the UDMA/bis-GMA/TEGDMA/HDDMA composite. The addition of HEMA had a positive effect on the properties of the tested materials, which may be related to the improved mobility of the bis-GMA and UDMA monomers

Challenges of Co–Cr Alloy Additive Manufacturing Methods in Dentistry—The Current State of Knowledge (Systematic Review)

Complex dental components which are individually tailored to the patient can be obtained due to new additive manufacturing technology. This paper reviews the metallic powders used in dental applications, the fabrication process (build orientation, process parameters) and post-processing processes (stress relieving, surface finishing). A review of the literature was performed using PubMed, ScienceDirect, Mendeley and Google Scholar. Over eighty articles were selected based on relevance to this review. This paper attempts to include the latest research from 2010 until 2020, however, older manuscripts (10 articles) were also selected. Over 1200 records were identified through the search; these were screened for title and/or summary. Over eighty articles were selected based on relevance to this review. In order to obtain a product which can be used in clinical applications, the appropriate manufacturing parameters should be selected. A discussion was made on optimal selective laser melting (SLM) parameters in dentistry. In addition, this paper includes a critical review of applied thermal treatment methods for Co–Cr alloys used in dentistry

The Influence of Cement Layer Thickness on the Stress State of Metal Inlay Restorations—Photoelastic Analysis

The successful restoration of teeth requires a good connection between the inlay and natural tissue. A strong bond may improve retention and reinforce tooth structure. The purpose of this study was to evaluate the influence of cement layer thickness on contraction stress generated during photopolymerization, and to determine the changes in stress state of the cement occurring during aging in water (over 84 days). Two cements were used: resin composite cement (NX3) and self-adhesive resin cement (Maxcem Elite Chroma). A cylindrical sample made of CuZn alloy was used to imitate the inlay. The stress state was measured by photoelastic analysis. The contraction stress of the inlay restoration was calculated for cement layer thicknesses of 25 µm, 100 µm, 200 µm, and 400 µm. For both tested materials, the lowest contraction stress was observed for the thinnest layer (25 µm), and this increased with thickness. Following water immersion, a significant reduction in contraction stress was observed due to hygroscopic expansion. Applying a thin layer (approximately 25 µm) of composite and self-adhesive resin cements resulted in high levels of expansion stresses (over −6 MPa) after water aging

An Evaluation of the Hydrolytic Stability of Selected Experimental Dental Matrices and Composites

Materials with potential use as dental restoration should be evaluated in an aggressive environment. Such accelerated aging is widely used in other industries and allows the assessment of service life. In the presented study, three neat resins (UDMA/Bis-GMA/TEGDMA 70/10/20 wt.%, UDMA/Bis-GMA/TEGDMA 40/40/20 wt.% and UDMA/Bis-EMA/TEGDMA 40/40/20 wt.%) and three composites based on these matrices were tested before and after aging protocols (I-7500 cycles, 5 °C and 55 °C, water and 7 days, 60 °C, 0.1 M NaOH; II-5 days, 55 °C, water and 7 days, 60 °C, 0.1 M NaOH). Flexural strength (FS), diametral tensile strength (DTS) and hardness (HV) were determined. Applied aging protocols resulted in a decrease in the value of the FS, DTS and HV. Larger changes were noticed for the neat resins. Materials in which the content of bis-GMA was lower or substituted by bis-EMA showed better resistance to degradation. The choice of mixtures with monomers characterized by lower sorption values may favorably affect hydrolytic stability. It was shown that for composites there was a drastic decrease in hardness, which suggests a more superficial effect of the used protocols. However, degradation of the surface layer can result in a growing problem over time given that the mastication processes are an inherent element in the oral environment

The Influence of Cement Layer Thickness on the Stress State of Metal Inlay Restorations—Photoelastic Analysis

The successful restoration of teeth requires a good connection between the inlay and natural tissue. A strong bond may improve retention and reinforce tooth structure. The purpose of this study was to evaluate the influence of cement layer thickness on contraction stress generated during photopolymerization, and to determine the changes in stress state of the cement occurring during aging in water (over 84 days). Two cements were used: resin composite cement (NX3) and self-adhesive resin cement (Maxcem Elite Chroma). A cylindrical sample made of CuZn alloy was used to imitate the inlay. The stress state was measured by photoelastic analysis. The contraction stress of the inlay restoration was calculated for cement layer thicknesses of 25 µm, 100 µm, 200 µm, and 400 µm. For both tested materials, the lowest contraction stress was observed for the thinnest layer (25 µm), and this increased with thickness. Following water immersion, a significant reduction in contraction stress was observed due to hygroscopic expansion. Applying a thin layer (approximately 25 µm) of composite and self-adhesive resin cements resulted in high levels of expansion stresses (over −6 MPa) after water aging

Multi-Layer Application of Self-Etch and Universal Adhesives and the Effect on Dentin Bond Strength

Contemporary self-etch and multi-mode adhesives were introduced to ensure a fast and reliable bonding procedure. Yet, in terms of bond strength and stability they failed to perform as well as two-bottle, etch-and-rinse adhesives, which remain the gold standard in terms of durability. The purpose of this study was to assess the shear bond strength (SBS) of dental adhesives to dentin with different application protocols. Two self-etch (Adper Easy One and Xeno V) and two multi-mode adhesives (Single Bond Universal and Prime&Bond One Select) were used in the study. The highest SBS was obtained for Single Bond Universal applied in three layers, while the lowest, for Xeno V applied in one layer. Other tested adhesives obtained the highest SBS when applied in three layers. For all tested adhesives, multi-layer application resulted in an increase in adhesive layer thickness, as observed in SEM. The increased thickness of the adhesive layer produced by triple application of unfilled adhesives corresponded with higher SBS values. The present study showed that using triple adhesive layers with simplified adhesive systems can be recommended to improve their performance. Due to differences in the composition of self-etch and universal adhesives, the exact application protocol is product dependent

The Influence of Application Protocol of Simplified and Universal Adhesives on the Dentin Bonding Performance

Contemporary adhesives use etch-and-rinse, self-etch, and multimode adhesive strategies. Simplified and universal adhesives present lower bond strength to dentin than conventional, two-bottle etch-and-rinse adhesives. The purpose of this study was to evaluate bonding performance of simplified and universal adhesives to dentin after modifying their application protocol (multiplying applications and extending application time). Adhesive layer thickness (ALT) and shear bond strength (SBS), as well as the correlation between these parameters was calculated. Two universal (Single Bond Universal and Prime & Bond One Select) and two self-etch adhesives (Adper Easy One and Xeno V) were tested. Significant differences in ALT were detected between the adhesives, as well as within the same adhesive between study groups. Tested adhesives presented the thinnest adhesive layer when applied 2 times in 20 s. Single Bond Universal obtained the highest SBS results of all adhesives. Most adhesives (except for Prime & Bond One Select) obtained the highest SBS, when applied two or three times in 40 or 60 s, respectively. No correlation between the ALT and SBS was found. The study showed that increasing the number of applications and extending the application time of self-etch and universal adhesives can be recommended to improve their performance

The First Step in Standardizing an Artificial Aging Protocol for Dental Composites—Evaluation of Basic Protocols

The clinical performance of a dental restoration is strongly influenced by the complex and dynamically-changing oral environment; however, no standard procedure exists to evaluate this lifetime. This research provides an in-depth analysis of the effect of different aging procedures on the flexural strength (FS), diametral tensile strength (DTS) and hardness (HV) of selected dental materials (Resin F, Flow-Art and Arkon). Material structure was evaluated by scanning electron microscopy. It was found that each aging protocol had some influence on the tested properties, with continual erosion and degradation being observed. Greater mechanical degradation was observed for Resin F (neat resin) after the applied aging protocols, suggesting that a resin matrix is more susceptible for degradation. The most aggressive aging protocol was Protocol 5: 0.1 M NaOH, seven days, 60 °C. Further studies on the effect of artificial aging on dental materials should include a study of the thermal and chemical factors. A standardized aging procedure is crucial for improving the resistance of dental resin composite to oral conditions and their clinical performance

Contraction and Hydroscopic Expansion Stress of Dental Ion-Releasing Polymeric Materials

Ion-releasing polymeric restorative materials seem to be promising solutions, due to their possible anticaries effect. However, acid functional groups (monomers) and glass filler increase hydrophilicity and, supposedly, water sorption. The purpose of the study was to evaluate the influence of water sorption of polymeric materials on the stress state at the restoration-tooth interface. Beautifil Bulk Fill Flow, Beautifil Flow Plus F00, Beautifil Flow F02, Dyract eXtra, Compoglass Flow, Ionosit, Glasiosite, TwinkiStar, Ionolux and Fuji II LC were used for the study. The stress state was measured using photoelastic analysis after: 0.5, 24, 72, 96, 168, 240, 336, 504, 672, 1344 and 2016 h. Moreover, water sorption, solubility and absorption dynamic were assessed. The water sorption, solubility and absorption dynamic of ion-releasing restorative materials are material dependent properties. The overall results indicated that the tested restorative materials showed significant stress decrease. The total reduction in contraction stress and water expansion stress was not observed for materials with low value of water sorption (Beautifil Bulk Fill, Dyract eXtra, Glasionosit and Twinky Star). The photoelastic method turned out to be inadequate to evaluate stress changes of resin modified glass-ionomer cement (RMGI, Fuji II LC and Ionolux)