Dynamic Mechanical Analysis for Waste Tires Reinforced Polystyrene: Shear Compliance
Abstract: Polystyrene/waste tires composites were prepared in this study by incorporating small particles of waste tires into polydisperse commercial polystyrene (PS) in a melt-mixing method. The dynamic mechanical properties of PS and PS/composite were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements were carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The shear compliance of PS composite were studied and compared with those of unfilled PS. The shear compliance were studied and evaluated. Where the values of J' at = 0.06 radians/s are 110-4 and 5.310-5 Pa-1 for PS and PS composite, respectively At = 0.1 radians/s the addition of the rubber alters the value of J'' from 1.610-4 to 8.410-5 Pa-1. That means the stability of PS is enhanced by the incorporation of the rubbe
Rheological Properties of Polyvinylacetate: Part II
The dynamic viscoelastic properties of Polyvinylacetate with molecular weight 83000g/mol (PVA 83K) were determined by using a Rheometer operated in the dynamic mode and 8 mm parallel plate over a wide range of temperature as a function of frequency. The measurements were performed successively in the parallel plate geometry using 8 mm plate instead of 25 mm. The glass plateau regime is clearly observed because we could measure PVA 83K sample successively under its glass temperature. The rheological properties of polydisperse PVA 83K were completely studied and the experimental data were analyzed using the Winter model
Rheological Properties of Polyvinylacetate: Compliance and Relaxation Spectrum
Abstract: The dynamic viscoelastic properties of Polyvinylacetate with molecular weight 83000g/mol (PVA 83K ) were determined by using a Rheometer operated in the dynamic mode and 8 mm parallel plate over a wide range of temperature as a function of frequency. The measurements were performed successively in the parallel plate geometry using 8 mm plate instead of 25 mm. The glass plateau regime is clearly observed because we could measure PVA 83K sample successively under its glass temperature. The rheological properties of polydisperse PVA 83K were completely studied. The storage and loss compliance and the relaxation spectrum are evaluated
Rheological Characterization of Bitumen/Waste Polyethylene Composites: Part III
Waste polyethylene (PE) bags were reused in the modification of commercially available bitumen. The bitumen/PE blend was prepared by mixing homogenously commercial bitumen with waste PE in the molten state. The samples of bitumen blend and bitumen base were rheologically analyzied. The rheological properties such as complex modulus, shear compliance, torque and complex viscosity of bitumen and bitumen blend were studied using an ARES- Rheometer (Rheometric Scientific, Co.) in the dynamic mode, plate-plate geometry with diameter 8 mm. The measurements were performed over a wide range of temperatures ranged from-10°C to 60°C and frequencies from 100 to 0.1 radians per second. The results evidence that the complex modulus, shear compliance, torque and viscosity are improved by the incorporation of the waste PE into bitumen. The flow activation energy for neat bitumen and bitumen-9%PE are calculated from 0 by using the rheometric software
Dynamic and Complex Viscosity of Polystyrene/ Waste Tires Composites
Abstract: In this work, polystyrene/waste tires composites were prepared using the melt-mixing method. The viscoelastic properties of PS and PS/composite have been evaluated and compared. These properties were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements are carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The dynamic and complex viscosity of the PS composites were studied and compared with those of unfilled PS.
The results showed that the frequency, is shifted from 0.46 to 0.072 radians/s and the value of dynamic viscosity increases from 5.0104 to 1.3105 Pa.s by the addition of the rubber for PS. Zero-shear viscosity, 0 was found to be increased from is 9.5104 for PS/waste tire composite to 4.5104 for PS.
The flow activation energy is calculated from 0 by using the rheometric software to be 1.063 105 and 1.46 105 J/mol.K for Ps and PS composite, respectively
Complex Modulus of Waste Tires Reinforced Polystyrene
Abstract: In this work, polystyrene/waste tires composites were prepared by incorporating of waste tires into polydisperse commercial polystyrene in a melt-mixing method. The rheological characterization of PS and PS/composite have been studied and compared. These properties were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements are carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The complex modulus (G*) were evaluated and compared with those of unfilled PS. The dynamic mechanical properties and stability at elevated temperatures were found to increase with the addition of waste tires to PS as confirmed by the results.
The results showed that the value of G* at = 1.0 radian/s is 1.8104 and 4.4104 Pa for PS and PS/waste tires, respectively. This difference rises at low frequencies-branch to be the value of G* at = 0.06 radian/s is 8.8102 and 7.8103 Pa for PS and PS/waste tires, respectively. Generally G* increases by the addition of rubber as filler for P
The Shear Creep Stress and Loss Factor of Polystyrene/ Waste Tires Composites
Abstract— Polystyrene/waste tires composites were prepared in this study by incorporating shredded waste tires into polydisperse polystyrene in a melt-mixing method. The dynamic mechanical properties of PS and PS/composite have been evaluated and compared. These properties were studied using ARES-Rheometer under nitrogen atmosphere in parallel plate geometry with diameter 8 mm. The measurements are carried out over a wide range of temperatures ranged from 120°C to 220°C and frequencies from 100 to 0.1 radians per second. The shear creep stress J(t) and loss factor were studied and compared with those of unfilled PS. The dynamic mechanical properties and stability at elevated temperatures were found to increase with the addition of waste tires to PS as confirmed by the results.
From the results, the value of J(t) modulus for PS/waste tire is higher than this for the original material of PS. The incorporation of the rubber to the PS changes the value of J(t) at 0.001 second from 5.610-6 to 3.710-6 Pa-1 for PS and PS/waste tire, respectively and this difference increases with time. This confirmed that PS/waste tire composite exhibits higher stability at 180°C for a long time than the original unfilled PS. At frequency = 6.7102 radians/s , the value of tan increases about 20% by the incorporation of the rubber filler, due to the increase in the G'' modulus particularly at low frequencies in the flow regime
- …