Temperature Dependent Characteristics of Activated Carbons from Walnut Shells for Improved Supercapacitor Performance

Activated carbons (ACs) have been prepared from chemical treatment of walnut shells (WS) precursor at various temperatures (400‒800 °C) by using phosphoric acid (H3PO4) as activating agent. Influence of activation temperature on the porosity development and capacitive properties of resulting carbons was investigated. Thermal post-treatment of carbons previously activated at moderate temperature, e.g. 400 °C allowed further structural and porosity modification. Then, these carbons were investigated by scanning electron microscopy, Raman spectroscopy, energydispersive X-ray spectroscopy, electrochemical techniques and low temperature nitrogen adsorption exhibiting high BET specific surface area of approximately 2100 m2 g-1 and a total pore volume up to 1.3 cm3 g-1. Carbon material obtained through activation by H3PO4 at 400 °C and post-treated at 800 °C was used to make electrodes which were implemented to realize AC/AC capacitor using 1 mol L-1 Li2SO4. The electrochemical capacitor demonstrated high capacitance of 123 F g-1 per mass of one electrode, reduced cell resistance and stable capacitance for 5000 galvanostatic charge/discharge cycles at 1.0 A g-1