Прочностные и гидравлические свойства открытоячеистого пеностеклоуглерода, полученного разными методами

The paper reports on comparative studies of mechanical strength and hydraulic permeability of open-cell vitreous carbon foams manufactured by different methods. Vitreous carbon foam were manufactured either by infiltration of the epoxy precursor resin into a layer of pore-forming removable granules or by replication of a structure of polyurethane foam template with the phenolic precursor resin followed by pyrolysis of the precursor resins in neutral gaseous environment. It was stated that the vitreous carbon foams manufactured by the replication method had higher hydraulic permeability compared to the vitreous carbon foams manufactured by infiltration, but had poorer mechanical strength at similar cell diameter and within similar relative densities range. Recommendations for the use of the studied foams in various areas have been proposed.Проведены сравнительные исследования механической прочности и гидравлической проницаемости открытоячеистого пеностеклоуглерода, полученного разными методами. Пеностеклоуглерод получали инфильтрацией полимер-прекурсора в слой порообразующих удаляемых гранул и дублированием структуры высокопористого полимерного каркаса полимер-прекурсором с последующим пиролизом прекурсора в нейтральной газовой среде. Установлено, что при близком диаметре ячеек и в близком диапазоне относительных плотностей пеностеклоуглерод, полученный дублированием полимерного каркаса, превосходит по гидравлической проницаемости пеностеклоуглерод, полученный инфильтрацией, но уступает ему по механической прочности. Предложены рекомендации по применению исследованных пеноматериалов в различных областях

Модель формирования остаточных напряжений при газотермическом осаждении покрытий

The paper shows that gas-thermal coatings on the product surface may be considered on a first approximation as bimetallic material. Such approach permits to make calculations and determine residual stresses on the basis of multi-layer plate theory, mechanics of continuous medium and thermoelasticity.Показано, что газотермические покрытия на поверхности изделия можно рассматривать в первом приближении как биметаллический материал, что позволяет проводить расчеты и определять остаточные напряжения, основываясь на теории многослойных пластин, механики сплошных сред и термоупругости

Композиционные материалы на основе диборида титана для газотермических покрытий с высокой износостойкостью

The principles of producing composite materials based on titanium diboride with a metal binder and coatings from them with improved wear resistance have been studied. Composite powder TiB2/(Fe-Mo) having a grain size of titanium diboride of 80-500 nm fairly uniformly distributed in the material volume, was obtained by a combination of mechanical activation and SHS. Testing of detonation coatings from the composite powder TiB2/(Fe-Mo) has been carried out. The designed composition shows promise for strengthening machine parts and mechanisms operating in conditions of abrasion and friction without lubrication.Изучены принципы получения композиционных материалов на основе диборида титана с металлической связкой и покрытий из них с повышенной износостойкостью. Комбинацией методов механоактивации и СВС получен композиционный порошок TiB2/(Fe-Mo) с размером зерен диборида титана от 80 до 500 нм, достаточно равномерно распределенных в объеме материала. Проведены испытания детонационных покрытий из композиционного порошка TiB2/(Fe-Mo). Разработанная композиция является перспективной для упрочнения деталей машин и механизмов, работающих в условиях абразивного изнашивания и трения без смазки

Pattern of Residual Stress Formation at Gas-Thermal Coating Deposition

The paper shows that gas-thermal coatings on the product surface may be considered on a first approximation as bimetallic material. Such approach permits to make calculations and determine residual stresses on the basis of multi-layer plate theory, mechanics of continuous medium and thermoelasticity

FOUNDRY – PULSE METHOD OF ARTICLES PRODUCTION FROM ALLOY ON THE BASIS OF THE TITANIUM- ALUMINIUM

Consider the process of obtaining an addition alloy products from alloys of titanium-aluninum systems, which includes metallutgical and pulse processing of powder materials