Влияние скорости нагрева цементируемых конструкционных сталей на рост аустенитного зерна в процессе высокотемпературной выдержки

The influence of the heating mode of samples of constructional cemented steels 20ХН3А, 20ХГНР and 15ХГН2ТА on the value of austenite grain after high-temperature isothermal aging at 1000 °С is studied. It is shown that the heating of steels at a rate of 1.2–3.0 °C / min in the phase-transformation interval stabilizes the grain structure of the steels and leads to a slowing down of the kinetics of the growth of austenite grains during prolonged high-temperature aging, which makes it possible to increase the temperature of the chemical-thermal treatment of steels. It is concluded that the stabilization of the grain structure of steels is associated with the formation of segregation of impurity atoms and particles at grain boundaries with high-angle disorientation during slow heating, which prevents migration of grain boundaries in the process of prolonged high-temperature aging. A high-temperature chemical-thermal treatment of a batch of billets from steel 20ХН3А under experimental conditions with stepwise heating in the phase-transformation interval provided a qualitative fine-grained structure of the cemented layer.Исследовано влияние режима нагрева образцов конструкционных цементируемых сталей 20ХН3А, 20ХГНР и 15ХГН2ТА на величину аустенитного зерна после высокотемпературной изотермической выдержки при 1000 °С. Показано, что нагрев сталей со скоростью 1,2–3,0 °С/мин в интервале фазового α→γ превращения стабилизирует зеренную структуру сталей и приводит к замедлению кинетики роста аустенитного зерна при длительной высокотемпературной выдержке, что позволяет повысить температуру химико-термической обработки сталей. Сделано заключение, что стабилизация зеренной структуры сталей связана с образованием при медленном нагреве сегрегаций примесных атомов и частиц на границах зерен с высокоугловой разориентацией, что препятствует миграции границ зерен в процессе длительной высокотемпературной выдержки. Проведена высокотемпературная химико-термическая обработка партии заготовок из стали 20ХН3А по экспериментальному режиму со ступенчатым нагревом в интервале фазового α→γ превращения, обеспечившему получение качественной мелкозернистой структуры цементированного слоя

THE FACTORS INFLUENCING QUALITY OF STRUCTURE OF WORKPIECES PROCESSED ON THE VACUUM LINE «MODULTHERM 7/1»

Results of metallographical observations of structural constituent of carburized cases and a core of gears after thermochemical treatment on a vacuum line «ModulTherm 7/1» made by corporation «ALD Vacuum Technologies GmbH» are given. It was established that the cause of formation of non martensitic transformations of austenite in carburized cases and in a core of workpieces is insufficient cooling capacity of the hardening module of a vacuum line «ModulTherm 7/1»

INFLUENCE OF THE THERMAL PROCESS STAGE ON THE SIZE OF VALID GRAIN OF CONSTRUCTIONAL CARBURIZED STEEL GRADE 20CHN3A

Results of studies of the kinetics of changes in actual grains during technological process at different stages of the manufacture of parts with the use of a universal metallographic etchant to identify borders of valid grains in rolling and stamping in carburizing layers and core parts made of alloy structure steel grades are presented

STRUCTURAL FEATURES OF ECONOMICALLY-ALLOYED STEEL 20HGNMB AFTER CHEMICAL AND THERMAL HARDENING

It is established that structural characteristics of the parts produced of industrial steel melting correspond to the requirements rendered to quality of the cemented layer and core of high-intense gear wheels according to the results of spectral, metallographic, X-ray structural and durometric analyses