Синтез перовскитоподобных оксидов в системе Sr-Ni-Ta-O

Abstract

The effect of strontium excess on formation of single-phase nickelates in Sr3+zNiyTa2-yOx (3 ≤ 3 + z ≤ 4; 1 ≤ y ≤ 1,75) system has been established by XRD and electron microprobe techniques. It has been found that single-phase products of Sr3Ti2O7 structural type were formed when strontium (3 + z ) and nickel ( y ) content is close to 4 and 2, respectively. Crystallization of two predominant phases, i. e. Sr2(Ni,Ta)O4±δ and Sr3+z(Ni,Ta)2Ox of K2NiF4 and Sr3Ti2O7 structural types, has been shown to occur with strontium content of 3 ≤ 3 + z < 4 and nickel of 1 ≤ y < 1,75, at 1300 °С. Intergrowth phases have been foundto appear for Sr2(Ni,Ta)O4±δ and Sr3+z(Ni,Ta)2Ox.C использованием методов рентгенофазового, микрозондового рентгеновского анализов, сканирующей электронной микроскопии установлено влияние избыточного количества стронция на формирование однофазных никелатов в системе Sr3+zNiyTa2-yOx (3 ≤ 3 + z ≤ 4; 1 ≤ y ≤ 1,75). Установлено, что при концентрациистронция (3+ z ), стремящейся к 4, и концентрации никеля ( y ), стремящейся к 2, образуются однофазные продукты со структурным типом Sr3Ti2O7. Показано, что в области содержания Sr 3 ≤ 3 + z < 4 и Ni 1 ≤ y < 1,75 при температуре около 1300 °С происходит кристаллизация в основном двух фаз: Sr2(Ni,Ta)O4±δ и Sr3+z(Ni,Ta)2Ox со структурными типами K2NiF4 и Sr3Ti2O7 соответственно. Обнаружено, что в соединениях Sr2(Ni,Ta)O4±δ и Sr3+z(Ni,Ta)2Ox появляются фазы прорастания