Stress-dependent electromechanical properties of doped (Ba1-xCax)(ZryTi1-y)O3

Abstract

The effect of 1 at% Fe- and FeNb-doping on the temperature and stress stability of the electromechanical properties of (Ba1-xCax)(ZryTi1-y)O3 (BCZT) was investigated. For the composition (Ba0.89Ca0.11)(Zr0.135Ti0.865)O3 with rhombohedral symmetry, doping reduces the Curie point and the temperature stability of the large-signal electromechanical properties significantly. The large-signal piezoelectric coefficient d33* at room temperature was reduced to 500pm/V compared to 700pm/V in the undoped composition at 1kV/mm. The electrostrain, however, was found to be less sensitive to mechanical prestresses, showing a plateau up to stresses of 80MPa in both doped compositions. These effects were attributed to a reduction of the domain wall mobility due to a smaller grain size, charged defect dipoles and the proximity of the room-temperature measurements to the reduced ferroelectric-paraelectric phase transition temperature. The study reveals that the exceptionally large strains observed in BCZT rely on the instabilities around the polymorphic phase transition in the system. Aliovalent doping changes this sensitive system and reduces the electrostrain considerably.close3

Similar works

Full text

thumbnail-image

ScholarWorks@UNIST

redirect
Last time updated on 12/04/2017

This paper was published in ScholarWorks@UNIST.

Having an issue?

Is data on this page outdated, violates copyrights or anything else? Report the problem now and we will take corresponding actions after reviewing your request.