Resist??ncia ?? flex??o e m??dulo de elasticidade de diferentes tipos de resina composta

By Sinval Adalberto Rodrigues J??nior, Cesar Henrique Zanchi, Rodrigo Varella de Carvalho and Fl??vio Fernando Demarco

Abstract

The aim of the study was to test whether the filler composition of resin composites influences their flexural strength and modulus of elasticity. Flexural strength and modulus of elasticity were obtained through a three-point bending test. Twelve bar shaped specimens of 5 commercially available composites ??? Supreme (3M/ESPE), a universal nanofilled composite; Esthet-X (Dentsply), Z-250 (3M/ESPE), Charisma (Heraeus Kulzer), universal hybrid composites; and Helio Fill (Vigodent), a microfine composite ??? were confectioned according to the ISO 4049/2000 specifications. The test was performed after a 7- days storage time using a universal test machine with a crosshead speed of 1 mm/min. The filler weight content was determined by the ashing technique. The data obtained on the mechanical properties were submitted to ANOVA and Tukey test (p < 0.05). Pearson???s correlation test was used to determine the correlation between the filler content and the mechanical properties. A weak but significant correlation between the mechanical properties evaluated and the filler weight content was observed (p < 0.000). The microfine composite presented the lowest filler weight and the lowest mechanical properties. Statistically different flexural strength and modulus of elasticity results were observed among the universal hybrid composites. The nanofilled composite presented intermediary results. Within the limitations of this in vitro study, it could be concluded that the filler content significantly interfered in the flexural strength and modulus of elasticity of the composites tested

Topics: Composite resins, Physical and chemical properties, Inorganic particles
Publisher: Sociedade Brasileira de Pesquisa Odontol??gica
Year: 2007
OAI identifier: oai:agregador.ibict.br.RI_UFPEL:oai:repositorio.ufpel.edu.br:123456789/837
Download PDF:
Sorry, we are unable to provide the full text but you may find it at the following location(s):
  • http://www.rcaap.pt/detail.jsp... (external link)
  • Suggested articles


    To submit an update or takedown request for this paper, please submit an Update/Correction/Removal Request.