The exceptional mechanical properties of polycrystalline nickel-based superalloys arise through various concurrent strengthening mechanisms. Whilst these mechanisms are generally understood, consensus has yet to be established on the precise contribution of each to the overall alloy strength. Furthermore, changes in alloy chemistry influence several different mechanisms, making the assessment of individual alloying elements complex. In this study, a series of model quinary Ni-based superalloys has been investigated to systematically study the effect of varying Mo content on the contributing strengthening mechanisms. Using microstructural data, the yield strength was modelled by summing the individual effects of solid solution in both the γ and γ ' phases, coherency, grain boundary and precipitation strengthening. The total predicted yield stress increased with Mo content despite the diminishing contribution of precipitation strengthening. It is shown that solid solution strengthening of the ordered γ' precipitate phase is a key contributor to the overall strength, and that variations in composition between the tertiary and secondary γ ' lead to significant changes in mechanical properties that should be accounted for in models of alloy strength.Funding was provided by the EPSRC/Rolls-Royce Strategic Partnership under EP/M005607/1 and EP/H022309/1. The Oxford Atom Probe facility was funded by the EPSRC under EP/M022803/1. E. I. Galindo-Nava would like to acknowledge the Royal Academy of Engineering for his fellowship funding. Neutron diffraction beam time was supported through the Canadian Neutron Beam Centre under Experiment number 1258
Is data on this page outdated, violates copyrights or anything else? Report the problem now and we will take corresponding actions after reviewing your request.