The mechanism of enhanced magnetic properties of sintered permanent magnets by substitution of Pr for Nd

Authors
Publication date
13 March 2012
Publisher
Doi

    Abstract

    In this study, the influence of substitution of Nd with Pr on the magnetic of sintered permanent magnets was investigated. The samples were prepared by traditional powder metallurgical technique. The nominal composition of the alloys is (Nd1？xPrx)29Dy1.3R3.1Febal (R = Al0.3Cu0.2 Co1.5 B1Zr0.1, wt%) with x varying from 0 to 1 in steps of 0.2. Experimental results show that the overall magnetic properties, especially the intrinsic coercivity and thermal stability of the magnets, could be improved by substituting Nd with Pr in the magnets. When the Pr replaces all Nd in the magnets, excellent performance magnets with Br = 13.65 KGs, Hcj = 22.13 KOe, (BH)max = 46.1 MGsOe are obtained with a low Dy content (1.3 wt%)

    Similar works

    Full text

    thumbnail-image

    Institutional Repository of Ningbo Institute of Material Technology & Engineering, CAS

    redirect
    oaioai:ir.nimte.ac.cn/:174433/957...
    Last time updated on 22/01/2018

    This paper was published in Institutional Repository of Ningbo Institute of Material Technology & Engineering, CAS.

    Having an issue?

    Is data on this page outdated, violates copyrights or anything else? Report the problem now and we will take corresponding actions after reviewing your request.