Thermal fatigue and oxidation data on TAZ-8A, MAR-M 200, and Udimet 700 superalloys

Abstract

The fluidized bed technique was used to determine the relative thermal fatigue and oxidation resistance of three superalloys: TAZ-8A, Mar-M 200, and Udimet 700. The alloys TAZ-8A and MAR-M 200 were also tested in the directionally-solidified form. For the 13 combinations of composition, solidification method, surface protection, and specimen geometry, the cycles to cracking varied from 1250 to 15,000. The alloy/coating having the best resistance to thermal fatigue cracking was coated directionally-solidified NASA TAZ-8A. This combination also had excellent oxidation resistance