High temperature fatigue behavior of a SiC/Ti-24Al-11Nb composite


A series of tension-tension strain- and load-controlled tests were conducted on unidirectional SiC/Ti-24Al-11Nb (at percent) composites at 425 and 815 C. Several regimes of damage were identified using Talrega's concept of fatigue life diagrams. Issues of test technique, test control mode, and definition of failure were also addressed