Utjecaj tretmana limunskom kiselinom na svojstva iverice proizvedene od grana vrtnog drveća pomiješanih s ostatkom od prerade šećerne trske i palminim lišćem

Abstract

The aim of this research was to determine the effect of citric acid treatment on the particleboard properties obtained by mixing three types of lignocellulosic sources. The board was produced by mixing garden tree branches, bagasse and palm leaves in different mass portions (90:5:5, 70:15:15, 50:25:25). Urea-formaldehyde (UF) resin was used at two levels as 10 % surface layer and 8 % middle layer, and 8 % surface layer and 6 % middle layer based on the raw materials. Citric acid was used at three levels of 0, 10, and 20 % by weight. The physical and mechanical properties of particleboards are measured according to the European Standard EN. Fourier transform infrared spectroscopy was used to distinguish the effect of citric acid treatment on the particles. The results showed that, when the amount of citric acid increased, the water absorption of panels decreased, and the mechanical properties improved. As garden tree branch content in the particleboard increased, so did the total resistance. According to the results of this study, the particleboards containing 70 % garden tree branches, 0 % citric acid, and 8 % UF resin, as well as those of 50 % garden tree branches, 0 % citric acid, and 10 % UF resin can be used for type P1 boards (bending strength of 10 MPa and 0.24 MPa internal bonding). In comparison, the boards containing 90 % garden tree branches, 10 % citric acid and 10 % UF resin were proposed for type P2 boards (bending strength of 11 MPa, modulus of elasticity of 1600 MPa and internal bonding of 0.35 MPa).Cilj ovog istraživanja bio je utvrditi utjecaj tretmana limunskom kiselinom na svojstva iverice proizvedene miješanjem triju vrsta lignoceluloznog materijala. Ploča je proizvedena miješanjem grana vrtnog drveća, ostataka od prerade šećerne trske i palmina lišća u različitim masenim udjelima (90 : 5 : 5; 70 : 15 : 15; 50 : 25 : 25). Urea-formaldehidna (UF) smola dodavana je u različitim udjelima s obzirom na lignoceluloznu sirovinu: 10 % u površinski sloj i 8 % u srednji sloj te 8 % u površinski sloj i 6 % u srednji sloj. Primijenjena su tri težinska udjela limunske kiseline: 0, 10 i 20 %. Fizička i mehanička svojstva ploča iverica mjerena su na temelju europskog standarda. Za određivanje utjecaja tretmana limunskom kiselinom na čestice lignoceluloznog materijala primijenjena je Fourierova infracrvena spektroskopija. Rezultati su pokazali da se s povećanjem količine limunske kiseline smanjilo upijanje vode ploča i da su se poboljšala njezina mehanička svojstva. Kako se udio grana vrtnog drveća u iverici povećavao, tako se povećavala i ukupna otpornost ploče. Kao ploče tipa P1 (čvrstoća na savijanje od 10 MPa i čvrstoća na raslojavanje od 0,24 MPa) mogu se upotrebljavati iverice koje sadržavaju 70 % grana vrtnog drveća, 0 % limunske kiseline i 8 % UF smole te iverice koje imaju 50 % grana vrtnog drveća, 0 % limunske kiseline i 10 % UF smole. Za usporedbu, ploče koje sadržavaju 90 % grana vrtnog drveća, 10 % limunske kiseline i 10 % UF smole predlažu se kao ploče tipa P2 (čvrstoća na savijanje 11 MPa, modul elastičnosti 1600 MPa i čvrstoća na raslojavanje 0,35 MPa)