Abstract
Fatigue crack growth (FCG) tests on the main circulating pump casing material were conducted at room temperature to investigate the effect of long-term aging at 400°C. It was found that the FCG rate increased with aging time. However, there were similar ∆Kth values for both the virgin material and aged material at the same stress ratios R. At room temperature, ∆Kth was observed to decrease with an increase in R. An equation incorporating the Kmax and ∆K effects was proposed to describe FCG rates over the linear portion of the curve (Paris equation) for all stress ratios. Additionally, fatigue fracture patterns near crack initiation sites reveals quasi-cleavage fracture in thermally aged specimens.Испытания на сопротивление росту усталостных трещин в материале корпуса главного циркуляционного насоса при комнатной температуре были проведены с целью изучения влияния долговременного старения при 400°С. Установлено, что скорость роста трещин возрастает по мере увеличения времени старения. Однако при одинаковых коэффициентах асимметрии R получены близкие значения ∆Kth для исходного и состаренного материала. Установлено, что при комнатной температуре ∆Kth снижается с увеличением R. Для описания скорости роста усталостных трещин на линейном участке кривой (уравнение Париса) для всех значений коэффициента асимметрии предложено уравнение, учитывающее влияние величин Kmax и ∆K. Характер усталостного разрушения вблизи области зарождения трещин соответствует квазихрупкому излому образцов, подвергшихся термическому старению