Polymer toughening using residue of recycled windshields: PVB film as impact modifier

In this work, poly(vinyl butyral) (PVB) film originated from the mechanical separation of windshields was tested as all impact modifier of Polyamide-6 (PA-6). The changes undergone by PVB film during the recycling process and the blend manufacturing were evaluated by thermal analyses, infrared spectroscopy and loss oil ignition. Blends of PA-6/original PVB film and PA-6/recovered PVB film were obtained in concentrations ranging from 90/10 to 60/40. The mechanical properties of the blends were investigated and explained in light of the blends morphologies, which in turns were correlated to the changes undergone by the PVB film during the recycling process. The original film presented a plasticizer content of 33 wt.%, which decreased to as low as 20 wt.%, after the recycling and blend preparation processes. The PA-6/PVB film blends presented lower values of tensile strength and Young`s modulus than Polyamide-6, but all blends presented a dramatic increase in their toughness, with a special feature for the 40 wt.%(, blend, which resulted in a super toughened material (impact strength exceeding 500 J/m). Similar results were obtained with recovered PVB film and super tough blends were also obtained. The use of recovered PVB resulted in a smaller improvement of the impact strength due to the loss of plasticizer undergone during the recycling process. The morphological observations showed that if the interparticle distance is smaller than around 0.2 mu m (critical value), the notched Izod impact strength values increase considerably and the fracture surface of blends exhibit characteristics of tough failure. (C) 2007 Elsevier Ltd. All rights reserved

Estudo das propriedades térmicas e reológicas de PLA reforçado com nanowhiskers de celulose.

No presente trabalho foram obtidos nanowhiskers de celulose (NCs) por meio da hidrólise ácida com ácido sulfúrico, os quais foram caracterizados por DRX e TGA. A incorporação dos NCs em matriz de PLA em estado fundido foi feita através de câmara de mistura e prensagem. As amostras foram caracterizadas por DSC, microscopia óptica e por análises reologias. Os resultados de DSC e microscopia mostraram que os NCs alteraram o processo de cristalização do PLA. Os ensaios reológicos de cisalhamento oscilatório de pequenas amplitudes (COPA) mostraram que a adição de 3% em massa de NCs no PLA foi suficiente para alterar o comportamento reológico do polímero.CAPESFAPES

Influência da adição de argilas organofilicas e sódica nas propriedades de nanocompósitos de matriz biodegradável

O presente trabalho apresenta um estudo sobre nanocompósitos formados pelo polímero biodegradável PLA e diferentes argilas : a Closite Sódica, uma argila esmectiitica sódica natural e as Cloisite 2A, Cloisite 30B e Cloisite 15A, que são argilas Cloisite Sodica tratadas com sal quaternário de amônio

Photodegradation of composite obtained by the addition of colloidal silicon dioxide in the blend PBA/PLA

Este trabalho tem por objetivo avaliar o efeito da silica coloidal no processo de fodegradação da blenda de poli (adipta de butileno-co-tereflato de butileno)/poli (ácido láctico) - PBAT/PLA . Os compósitos de PBA/PLA com adição de sílica coloidal com composições de 5% e 10% em massa de silica foram obtidos pelo método de intercalação no polímero fundido em uma extrusora de dupla rosca. as amostras foram expostas à radiação UV por tempos de até 40 dias e caracterização por análises de espectroscopia vibracional de absorção no infravermelho (FTIR)

Properties of PLA reinforced with nanocellulose

Este trabalho teve como objetivo a obtenção de nanocelulose, a incorporação destas partículas no poliácido láctico (PLA) e o estudo das propriedades dos comósitos obtidos. A nanocelulose (NC) foi obtida por hidrólise ácida utilizando ácido sulfúrico. As nanopartículas foram caracterizadas por DRX e TGA. A incorporação da NC no PLA foi realizada em câmara de mistura no estado fundido

Propriedades mecânicas e térmicas de nanocompósitos PLA/Argila (Laponita RD e Cloisite Na+) obtidos por extrusão

Neste trabalho foram obtidos nanocompósitos poli(acido lático) PLA com duas diferentes argilas Laponita RD e CloisiteNa+ na proporção de 5% em relação a massa total de mistura. Os nanocompósitos foram obtidos via extrusão em extrusora dupla rosca. O PLA puro e os compósitos foram caracterizados por ensaios de Resistência à Tração e Resistência ao Impacto Izod, Análise Termogravimétrica (TG), Análise de Calorimetria Exploratória Diferencial (DSC). Os resultados mecânicos mostram que a argila Cloisite Na+ atua como agente tenacificante para o PLA sendo que observou-se aumento de 14% na resistência ao impacto. As argilas atuam como agente nucleante na matriz de PLA aumentado a intensidade dos picos de cristalizaçãoCNPqCAPE

Avaliação da influência de cargas nas propriedades mecânicas de compósitos com ECOVIO

Este trabalho tem como objetivo estudar as propriedades mecânicas do ECOVIO®, antes e após a adição de 5 e 10% em massa de carga. As cargas utilizadas foram Sílica coloidal Aerosil 200® e dois tipos de argilas comerciais do grupo esmectita: Cloisite 30B® e Cloisite Sódica®. Os compósitos obtidos foram caracterizados por ensaios mecânicos de resistência à tração e resistência ao impacto Izod e por microscopia óptica. Os resultados mecânicos indicam que o ECOVIO® apresentou melhorias nos valores de módulo de elasticidade em função da adição de carga. Em particular, a composição com sílica coloidal apresentou aumentos de até 110% nos valores de módulo de elasticidade, e valores de resistência ao impacto Izod similares ou superiores aos obtidos para a fase matriz, sem perdas significativas em resistência à tração e alongamentoCAPESBAS