Synergistic effect between 8-hydroxyquinoline and benzotriazole for the corrosion protection of 2024 aluminium alloy: A local electrochemical impedance approach

This work is devoted to the corrosion inhibition of the 2024 aluminium alloy (AA2024) in neutral aqueous solution by 8-hydroxyquinoline (8-HQ) and benzotriazole (BTA). First, current-voltage curves and global electrochemical impedance measurements confirmed that 8-HQ and BTA are two effective corrosion inhibitors for AA2024. Mixing the two compounds led to a synergistic effect for the corrosion protection of the alloy. From the impedance data analysis, it was shown that 8-HQ acted mainly on the aluminium matrix with an additional action of the BTA on the intermetallic particles. Then, to analyse the role of the inhibitors on the galvanic coupling between the aluminium matrix and the particles, local electrochemical impedance measurements were performed on a model system (Al/Cu couple). It was shown that in the presence of 8-HQ or BTA alone, the galvanic coupling between copper and aluminium was little reduced while in the presence of both compounds together it was strongly limited. The local impedance results confirmed the specific inhibition of the 8-HQ and of the BTA on Al and Cu respectively

Etude de la corrosion caverneuse d'un acier inoxydable martensitique : utilisation d'une cellule à couche mince

Les aciers inoxydables martensitiques sont utilisés dans l'industrie aéronautique où de hautes propriétés mécaniques sont requises. Cependant, dû à leur faible teneur en chrome, ils sont relativement sensibles à la corrosion localisée et particulièrement à la corrosion caverneuse qui se développe en milieu confiné. Tout d'abord, le comportement électrochimique de l'acier inoxydable martensitique X12CrNiMoV12-3 a été étudié dans une solution neutre et chlorurée (NaCl 0,1 M + Na2SO4 0,04 M) en plein bain. Des mesures électrochimiques (courbes de polarisation et mesures d'impédance) couplées à des analyses de surface par XPS ont permis de caractériser les films passifs formés pour différentes conditions. Les résultats obtenus ont permis de montrer le rôle important joué par l'oxygène dissous sur la formation et/ou la modification du film passif pendant l'immersion dans l'électrolyte. Les diagrammes d'impédance obtenus au potentiel de corrosion et en milieu aéré sont caractérisés par deux constantes de temps qui ont été attribuées au film passif (hautes fréquences) et au transfert de charges (basses fréquences). L'analyse de la partie hautes fréquences des diagrammes d'impédance électrochimique à l'aide du modèle en loi de puissance a permis de montrer de faibles variations de l'épaisseur des films pendant l'immersion. Des mesures électrochimiques ont ensuite été réalisées à l'aide du montage de la cellule à couche mince qui permet de travailler avec des épaisseurs d'électrolyte rigoureusement contrôlées. Les essais réalisés ont montré l'aptitude à la repassivation de l'acier inoxydable martensitique dès qu'il est en contact avec l'oxygène dissous en particulier pour des faibles épaisseurs d'électrolyte (inférieur à 100 µm). Lorsque le milieu est confiné entre deux parois en acier afin de reproduire une situation de corrosion caverneuse, il a été montré la corrosion est fortement accélérée lorsque l'épaisseur d'électrolyte est faible (inférieur à 500 µm). ABSTRACT : Martensitic stainless steels are mainly used for applications where high mechanical performance is required. However, due to the low chromium content, they are relatively sensitive to localised corrosion, and particularly, to crevice corrosion encountered in confined environments. First, the electrochemical behavior of X12CrNiMoV12-3 martensitic stainless steel has been studied in a bulk neutral chloride solution (0.1 M NaCl + 0.04 M Na2SO4). Electrochemical measurements (polarisation curves and impedance measures) and XPS surface analysis were performed in order to characterise the passive films formed under different experimental conditions. The results showed the important role of dissolved oxygen to form and/or modify the passive film during immersion in electrolyte. The impedance diagrams are characterised by two time constants wich are attributed to passive film response (high frequency range) and to charge transfert resistance (low frequency range). The analyse of the high frequencies part of the diagrams by using the "power law model" showed low evolution of passive films thickness during immersion. Then, electrochemical measurements were perfomed in confined environments by using a thin layer cell where the electrolyte thickness were rigourosly adjusted. The measurements showed that the martensitic stainless steel is in passive state even for low electrolyte thickness (inferior in 100 µm). When the electrolyte is confined between two stainless electrodes in order to reproduce the same conditions find during crevice corrosion, the corrosion is sharply accelerated when the electrolyte thickness is above 500 µ

Etude de la corrosion caverneuse d'un acier inoxydable martensitique (utilisation d'une cellule à couche mince)

Les aciers inoxydables martensitiques sont utilisés dans l'industrie aéronautique où de hautes propriétés mécaniques sont requises. Cependant, dû à leur faible teneur en chrome, ils sont relativement sensibles à la corrosion localisée et particulièrement à la corrosion caverneuse qui se développe en milieu confiné. Tout d'abord, le comportement électrochimique de l'acier inoxydable martensitique X12CrNiMoV12-3 a été étudié dans une solution neutre et chlorurée (NaCl 0,1 M + Na2SO4 0,04 M) en plein bain. Des mesures électrochimiques (courbes de polarisation et mesures d'impédance) couplées à des analyses de surface par XPS ont permis de caractériser les films passifs formés pour différentes conditions. Les résultats obtenus ont permis de montrer le rôle important joué par l'oxygène dissous sur la formation et/ou la modification du film passif pendant l'immersion dans l'électrolyte. Les diagrammes d'impédance obtenus au potentiel de corrosion et en milieu aéré sont caractérisés par deux constantes de temps qui ont été attribuées au film passif (hautes fréquences) et au transfert de charges (basses fréquences). L'analyse de la partie hautes fréquences des diagrammes d'impédance électrochimique à l'aide du modèle en loi de puissance a permis de montrer de faibles variations de l'épaisseur des films pendant l'immersion. Des mesures électrochimiques ont ensuite été réalisées à l'aide du montage de la cellule à couche mince qui permet de travailler avec des épaisseurs d'électrolyte rigoureusement contrôlées. Les essais réalisés ont montré l'aptitude à la repassivation de l'acier inoxydable martensitique dès qu'il est en contact avec l'oxygène dissous en particulier pour des faibles épaisseurs d'électrolyte (inférieur à 100 m). Lorsque le milieu est confiné entre deux parois en acier afin de reproduire une situation de corrosion caverneuse, il a été montré la corrosion est fortement accélérée lorsque l'épaisseur d'électrolyte est faible (inférieur à 500 m).Martensitic stainless steels are mainly used for applications where high mechanical performance is required. However, due to the low chromium content, they are relatively sensitive to localised corrosion, and particularly, to crevice corrosion encountered in confined environments. First, the electrochemical behavior of X12CrNiMoV12-3 martensitic stainless steel has been studied in a bulk neutral chloride solution (0.1 M NaCl + 0.04 M Na2SO4). Electrochemical measurements (polarisation curves and impedance measures) and XPS surface analysis were performed in order to characterise the passive films formed under different experimental conditions. The results showed the important role of dissolved oxygen to form and/or modify the passive film during immersion in electrolyte. The impedance diagrams are characterised by two time constants wich are attributed to passive film response (high frequency range) and to charge transfert resistance (low frequency range). The analyse of the high frequencies part of the diagrams by using the "power law model" showed low evolution of passive films thickness during immersion. Then, electrochemical measurements were perfomed in confined environments by using a thin layer cell where the electrolyte thickness were rigourosly adjusted. The measurements showed that the martensitic stainless steel is in passive state even for low electrolyte thickness (inferior in 100 m). When the electrolyte is confined between two stainless electrodes in order to reproduce the same conditions find during crevice corrosion, the corrosion is sharply accelerated when the electrolyte thickness is above 500 mTOULOUSE-INP (315552154) / SudocSudocFranceF

Study of crevice corrosion of a martensitic stainless steel by using a thin layer cell

Les aciers inoxydables martensitiques sont utilisés dans l'industrie aéronautique où de hautes propriétés mécaniques sont requises. Cependant, dû à leur faible teneur en chrome, ils sont relativement sensibles à la corrosion localisée et particulièrement à la corrosion caverneuse qui se développe en milieu confiné. Tout d'abord, le comportement électrochimique de l'acier inoxydable martensitique X12CrNiMoV12-3 a été étudié dans une solution neutre et chlorurée (NaCl 0,1 M + Na2SO4 0,04 M) en plein bain. Des mesures électrochimiques (courbes de polarisation et mesures d'impédance) couplées à des analyses de surface par XPS ont permis de caractériser les films passifs formés pour différentes conditions. Les résultats obtenus ont permis de montrer le rôle important joué par l'oxygène dissous sur la formation et/ou la modification du film passif pendant l'immersion dans l'électrolyte. Les diagrammes d'impédance obtenus au potentiel de corrosion et en milieu aéré sont caractérisés par deux constantes de temps qui ont été attribuées au film passif (hautes fréquences) et au transfert de charges (basses fréquences). L'analyse de la partie hautes fréquences des diagrammes d'impédance électrochimique à l'aide du modèle en loi de puissance a permis de montrer de faibles variations de l'épaisseur des films pendant l'immersion. Des mesures électrochimiques ont ensuite été réalisées à l'aide du montage de la cellule à couche mince qui permet de travailler avec des épaisseurs d'électrolyte rigoureusement contrôlées. Les essais réalisés ont montré l'aptitude à la repassivation de l'acier inoxydable martensitique dès qu'il est en contact avec l'oxygène dissous en particulier pour des faibles épaisseurs d'électrolyte (inférieur à 100 µm). Lorsque le milieu est confiné entre deux parois en acier afin de reproduire une situation de corrosion caverneuse, il a été montré la corrosion est fortement accélérée lorsque l'épaisseur d'électrolyte est faible (inférieur à 500 µm).Martensitic stainless steels are mainly used for applications where high mechanical performance is required. However, due to the low chromium content, they are relatively sensitive to localised corrosion, and particularly, to crevice corrosion encountered in confined environments. First, the electrochemical behavior of X12CrNiMoV12-3 martensitic stainless steel has been studied in a bulk neutral chloride solution (0.1 M NaCl + 0.04 M Na2SO4). Electrochemical measurements (polarisation curves and impedance measures) and XPS surface analysis were performed in order to characterise the passive films formed under different experimental conditions. The results showed the important role of dissolved oxygen to form and/or modify the passive film during immersion in electrolyte. The impedance diagrams are characterised by two time constants wich are attributed to passive film response (high frequency range) and to charge transfert resistance (low frequency range). The analyse of the high frequencies part of the diagrams by using the "power law model" showed low evolution of passive films thickness during immersion. Then, electrochemical measurements were perfomed in confined environments by using a thin layer cell where the electrolyte thickness were rigourosly adjusted. The measurements showed that the martensitic stainless steel is in passive state even for low electrolyte thickness (inferior in 100 µm). When the electrolyte is confined between two stainless electrodes in order to reproduce the same conditions find during crevice corrosion, the corrosion is sharply accelerated when the electrolyte thickness is above 500 µ

In situ monitoring of thin alumina passive film growth by surface plasmon resonance (SPR) during an electrochemical process

International audienceAbstract This article presents a sensing technique to characterize the growth of an alumina passive film on an aluminum micro structured layer in situ. The technique uses surface plasmon resonance (SPR) on aluminum coated gratings with spectroscopic measurements during electrochemical polarization in 0.02M Na 2 SO 4 . The structure of the sensor was first simulated and then fabricated by photolithography. The grating was then replicated by nanoimprint (NIL) in Sol–Gel before pure aluminum layer was deposited by RF magnetron sputtering to produce the samples used in this study. Coupled plasmonic and electrochemical measurements confirmed the feasibility of in situ characterization (thickness) of alumina passive film on aluminum-based gratings in neutral aqueous media. Combining both measurements with an appropriated SPR spectrum fitting lead to alumina thickness monitoring within a few nanometers’ accuracy. The objectives and challenges of this study are to better characterize the alumina growth during electrochemical process combining in situ electrochemical process and SPR spectra in order to determine thin passive layer characteristics