Effect of alkaline treatment on mechanical properties of composites between vetiver fibers and epoxy resin

In this research, we were interested in studying whether vetiver fibers (VFs) treated with different concentrations of sodium hydroxide (NaOH) affect the mechanical properties of VF and epoxy resin (ER) composite material in a better way. As part of the experiment, VFs were treated with NaOH in various concentrations ranging from 0.5, 1, 1.5, 2, 2.5, and 3 mol/L. All of them were molded into composite material in the ratio of 10 wt% with ER. After that, they were tested for mechanical properties such as the tensile strength, impact strength, bending strength, and compressive strength to find the best mechanical properties. In addition, the surface was investigated with scanning electron microscopy (SEM) for adhesion of the VFs with ER. The results of the experiment were not as expected. We found that, increasing the concentration of vetiver treated with sodium hydroxide resulted in a decrease in the mechanical properties of the composite. The best values for impact, tensile, bending, and compressive strengths were 256.42 kJ/m2, 38.45 MPa, 43.70 MPa, and 110.27 MPa, respectively, and 0.5 mol/L is the best concentration of NaOH for mechanical strengths of the composites. Moreover, from SEM technique, it was found that the mechanical properties decreased at higher concentrations. This may be caused by damage to the VFs due to excessive NaOH corrosion and this point should be taken for further study

Mechanical, Physical, and Chemical Properties of Mycelium-Based Composites Produced from Various Lignocellulosic Residues and Fungal Species

Mycelium-based composites (MBCs) are characterized as biodegradable materials derived from fungal species. These composites can be employed across a range of industrial applications that involve the manufacturing of packaging materials as well as the manufacturing of buildings, furniture, and various other household items. However, different fungal species and substrates can directly affect the functional properties of MBCs, which ultimately vary their potential to be used in many applications. In this study, the mechanical, physical, and chemical properties of MBCs made from four different fungal species (Ganoderma fornicatum, Ganoderma williamsianum, Lentinus sajor-caju, and Schizophyllum commune) combined with three different types of lignocellulosic residues (sawdust, corn husk, and rice straw) were investigated. The results indicate that differences in both the type of lignocellulosic residues and the fungal species could affect the properties of the obtained MBCs. It was found that the MBCs obtained from sawdust had the highest degree of density. Moreover, MBCs obtained from S. commune with all three types of lignocellulosic residues exhibited the highest shrinkage value. The greatest degree of water absorption was observed in the MBCs obtained from rice straw, followed by those obtained from corn husk and sawdust. Additionally, the thermal degradation ability of the MBCs was observed to be within a range of 200 to 325 °C, which was in accordance with the thermal degradation ability of each type of lignocellulosic residue. The greatest degrees of compressive, flexural, impact, and tensile strength were observed in the MBCs of G. williamsianum and L. sajor-caju. The results indicate that the MBCs made from corn husk, combined with each fungal species, exhibited the highest values of flexural, impact, and tensile strength. Subsequently, an analysis of the chemical properties indicated that the pH value, nitrogen content, and organic matter content of the obtained MBCs were within the following ranges: 4.67–6.12, 1.05–1.37%, and 70.40–86.28%, respectively. The highest degree of electrical conductivity was observed in MBCs obtained from rice straw. Most of the physical and mechanical properties of the obtained MBCs were similar to those of polyimide and polystyrene foam. Therefore, these composites could be used to further develop relevant strategies that may allow manufacturers to effectively replace polyimide and polystyrene foams in the future

A Review Delving into the Factors Influencing Mycelium-Based Green Composites (MBCs) Production and Their Properties for Long-Term Sustainability Targets

Mycelium-based green composites (MBCs) represent an eco-friendly material innovation with vast potential across diverse applications. This paper provides a thorough review of the factors influencing the production and properties of MBCs, with a particular focus on interdisciplinary collaboration and long-term sustainability goals. It delves into critical aspects such as fungal species selection, substrate type selection, substrate preparation, optimal conditions, dehydrating methods, post-processing techniques, mold design, sterilization processes, cost comparison, key recommendations, and other necessary factors. Regarding fungal species selection, the paper highlights the significance of considering factors like mycelium species, decay type, hyphal network systems, growth rate, and bonding properties in ensuring the safety and suitability of MBCs fabrication. Substrate type selection is discussed, emphasizing the importance of chemical characteristics such as cellulose, hemicellulose, lignin content, pH, organic carbon, total nitrogen, and the C: N ratio in determining mycelium growth and MBC properties. Substrate preparation methods, optimal growth conditions, and post-processing techniques are thoroughly examined, along with their impacts on MBCs quality and performance. Moreover, the paper discusses the importance of designing molds and implementing effective sterilization processes to ensure clean environments for mycelium growth. It also evaluates the costs associated with MBCs production compared to traditional materials, highlighting potential cost savings and economic advantages. Additionally, the paper provides key recommendations and precautions for improving MBC properties, including addressing fungal strain degeneration, encouraging research collaboration, establishing biosecurity protocols, ensuring regulatory compliance, optimizing storage conditions, implementing waste management practices, conducting life cycle assessments, and suggesting parameters for desirable MBC properties. Overall, this review offers valuable insights into the complex interplay of factors influencing MBCs production and provides guidance for optimizing processes to achieve sustainable, high-quality composites for diverse applications

Sustainable Innovation: Fabrication and Characterization of Mycelium-Based Green Composites for Modern Interior Materials Using Agro-Industrial Wastes and Different Species of Fungi

Mycelium-based bio-composites (MBCs) represent a sustainable and innovative material with high potential for contemporary applications, particularly in the field of modern interior design. This research investigates the fabrication of MBCs for modern interior materials using agro-industrial wastes (bamboo sawdust and corn pericarp) and different fungal species. The study focuses on determining physical properties, including moisture content, shrinkage, density, water absorption, volumetric swelling, thermal degradation, and mechanical properties (bending, compression, impact, and tensile strength). The results indicate variations in moisture content and shrinkage based on fungal species and substrate types, with bamboo sawdust exhibiting lower shrinkage. The obtained density values range from 212.31 to 282.09 kg/m3, comparable to traditional materials, suggesting MBCs potential in diverse fields, especially as modern interior elements. Water absorption and volumetric swelling demonstrate the influence of substrate and fungal species, although they do not significantly impact the characteristics of interior decoration materials. Thermal degradation analysis aligns with established patterns, showcasing the suitability of MBCs for various applications. Scanning electron microscope observations reveal the morphological features of MBCs, emphasizing the role of fungal mycelia in binding substrate particles. Mechanical properties exhibit variations in bending, compression, impact, and tensile strength, with MBCs demonstrating compatibility with traditional materials used in interior elements. Those produced from L. sajor-caju and G. fornicatum show especially promising characteristics in this context. Particularly noteworthy are their superior compression and impact strength, surpassing values observed in certain synthetic foams multiple times. Moreover, this study reveals the biodegradability of MBCs, reaching standards for environmentally friendly materials. A comprehensive comparison with traditional materials further supports the potential of MBCs in sustainable material. Challenges in standardization, production scalability, and market adoption are identified, emphasizing the need for ongoing research, material engineering advancements, and biotechnological innovations. These efforts aim to enhance MBC properties, promoting sustainability in modern interior applications, while also facilitating their expansion into mass production within the innovative construction materials market